Modified butyl rubber

A butyl rubber and modification technology, applied in the field of high-performance materials, can solve the problems of poor compatibility of polar polymers and weak polarity of chlorinated butyl rubber, and achieve the effect of improving stickiness and good peel strength

Inactive Publication Date: 2013-09-11
GERON RUBBER HAIMEN
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, since the polarity of chlorobutyl rubber is still weak, it has poor compatibility with polar polymers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A modified butyl rubber, the composition of the modified butyl rubber:

[0023] Butyl rubber 15㎏;

[0024] Maleic anhydride 8㎏;

[0025] Sulfonyl chloride 5㎏;

[0026] Plasticizer 7㎏;

[0027] Vulcanizing agent 0.5㎏;

[0028] Antioxidant 0.5㎏;

[0029] Inorganic filler 20㎏.

[0030] Butyl rubber is a rubber copolymer of isobutylene and isoprene, the plasticizer is petrolatum, the vulcanizing agent is sulfur, the inorganic filler is clay, and the antioxidant is vulcanized alkylphenol.

Embodiment 2

[0032] A modified butyl rubber, the composition of the modified butyl rubber:

[0033] Butyl rubber 25㎏;

[0034] Maleic anhydride 12㎏;

[0035] Sulfonyl chloride 7㎏;

[0036] Plasticizer 8㎏;

[0037] Vulcanizing agent 1㎏;

[0038] Antioxidant 0.8㎏;

[0039] Inorganic filler 25㎏.

[0040] Butyl rubber is a rubber copolymer of isobutylene and isoprene, the plasticizer is a phthalate compound, the vulcanizing agent is zinc oxide, the inorganic filler is talc, and the antioxidant is vulcanized alkylphenol.

Embodiment 3

[0042] A modified butyl rubber, the composition of the modified butyl rubber:

[0043] Butyl rubber 40㎏;

[0044] Maleic anhydride 15㎏;

[0045] Sulfonyl chloride 10㎏;

[0046] Plasticizer 10㎏;

[0047] Vulcanizing agent 2㎏;

[0048] Antioxidant 1㎏;

[0049] Inorganic filler 30㎏.

[0050] Butyl rubber is a rubber copolymer of isobutylene and isoprene, the plasticizer is isoprene rubber, the vulcanizing agent is sulfur, the inorganic filler is calcium carbonate, and the antioxidant is vulcanized alkylphenol.

[0051] The plasticizer mentioned above can also be a combination of petrolatum, phthalate compounds, and isoprene rubber. The inorganic filler can be silica, or clay, talc, calcium carbonate, and dioxide. A combination of several in silicon.

[0052] The plasticizer is added in the present invention to reduce the viscosity of the system. At room temperature, it has the high elasticity and high strength of ordinary vulcanized rubber. The addition of vulcanizing agent makes it produced ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified butyl rubber. The modified butyl rubber comprises the following components in parts by weight: 15-40 parts of butyl rubber, 8-15 parts of maleic anhydride, 5-10 parts of sulfonyl chloride, 7-10 parts of plasticizer, 0.5-2 parts of vulcanizing agent, 0.5-1 part of antioxidant, and 20-30 parts of inorganic filler. The modified butyl rubber disclosed by the invention is added with the plasticizer, so that the guarant viscosity is lowered; at the room temperature, the modified butyl rubber has high elasticity and high strength of the common vulcanized rubber; the added vulcanizing agent is produced in a vulcanizing manner, so that the holding power of a product is improved, and the peel strength is better.

Description

Technical field [0001] The invention relates to a modified butyl rubber, which belongs to the field of high-performance materials. Background technique [0002] Halogenation modification of butyl rubber has become a more mature butyl rubber modification technology. Its main products are chlorinated butyl rubber and bromobutyl rubber. Chlorinated butyl rubber retains the low air permeability, shock absorption, ozone resistance and chemical resistance of ordinary butyl rubber, but also adds the characteristics that ordinary butyl rubber does not have, such as fast vulcanization speed and good heat resistance. [0003] However, the polarity of chlorinated butyl rubber is still weak, resulting in poor compatibility with polar polymers. Therefore, it is necessary to provide a new technical solution to solve the above-mentioned problems. Summary of the invention [0004] The purpose of the present invention is to provide a modified butyl rubber with excellent performance. [0005] In or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F255/10C08K3/06C08K3/22C08K3/34C08K3/26C08K3/36
Inventor 严火标
Owner GERON RUBBER HAIMEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap