Semi-worsted bamboo charcoal polyester fiber blended health care yarn

A bamboo charcoal polyester fiber, semi-worsted spinning technology, applied in the direction of yarn, textiles and papermaking, etc., can solve the problems of lack of health care function, and achieve the effect of good fullness, good moisture absorption and heat dissipation, and good comfort

Inactive Publication Date: 2016-08-31
ZHONGYUAN ENGINEERING COLLEGE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Wool fiber fineness, good elasticity, good fullness, good warmth retention, fine and smooth handle, soft luster, good fluffy, good moisture absorption, good comfort, but no health care function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Taking the 45-count blended yarn as an example, the weight percentage of bamboo charcoal polyester fiber, nylon fiber, long-staple cotton fiber and wool fiber blended is 40:20:20:20.

[0033] Its preparation method is as follows:

[0034] (1) Raw materials and wool oiling process: raw materials are generally dyed with loose fibers separately. The dyes used must ensure green environmental protection, uniform dyeing, high dyeing rate, not easy to fade, and good dyeing fastness. During the dyeing process, the temperature is strictly controlled to make The fibers are less damaged, and some leveling agents are properly added to avoid unfavorable phenomena such as color flower and floating color; according to the characteristics of raw materials, in order to reduce unfavorable phenomena such as static electricity, a certain amount of antistatic agent 1.5% is properly added; the weight ratio of raw materials is general Weighing method is adopted, and the raw material and wool ar...

Embodiment 2

[0044] Taking the 45-count blended yarn as an example, the weight percentage of bamboo charcoal polyester fiber, nylon fiber, long-staple cotton fiber and wool fiber blended is 45:15:25:15.

[0045] Its preparation method is as follows:

[0046] (1) Raw materials and wool oiling process: raw materials are generally dyed with loose fibers separately. The dyes used must ensure green environmental protection, uniform dyeing, high dyeing rate, not easy to fade, and good dyeing fastness. During the dyeing process, the temperature is strictly controlled to make The fibers are less damaged, and some leveling agents are properly added to avoid unfavorable phenomena such as color flower and floating color; according to the characteristics of raw materials, in order to reduce unfavorable phenomena such as static electricity, a certain amount of antistatic agent 1.5% is properly added; the weight ratio of raw materials is general Weighing method is adopted, and the raw material and wool ...

Embodiment 3

[0056] Taking the 45-count blended yarn as an example, the weight percentage of bamboo charcoal polyester fiber, nylon fiber, long-staple cotton fiber and wool fiber blended is 50:15:15:20.

[0057] Its preparation method is as follows:

[0058] (1) Raw materials and wool oiling process: raw materials are generally dyed with loose fibers separately. The dyes used must ensure green environmental protection, uniform dyeing, high dyeing rate, not easy to fade, and good dyeing fastness. During the dyeing process, the temperature is strictly controlled to make The fibers are less damaged, and some leveling agents are properly added to avoid unfavorable phenomena such as color flower and floating color; according to the characteristics of raw materials, in order to reduce unfavorable phenomena such as static electricity, a certain amount of antistatic agent 1.5% is properly added; the weight ratio of raw materials is general Weighing method is adopted, and the raw material and wool ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a semi-worsted bamboo charcoal polyester fiber blending health-care yarn and a production method thereof. In the blending yarn, the weight content of a bamboo charcoal polyester fiber accounts for 30-50%; the weight content of a polyamide fiber accounts for 15-40%; the weight content of a long stapled cotton fiber accounts for 15-40%; the weight content of a wool fiber accounts for 15-35%; and performance indexes of the blending yarn are that the single yarn breaking strength is 11.8-21.6cN / tex, a Cv (coefficient of variation) value of the single yarn breaking strength is 10.4-18.1%, and a Cv value of the yarn evenness is 13.7-20.4%. The blending health-care yarn and manufactured fabric have health-care functions of antibiosis, deodorization, bacteriostasis, inflammation diminishing, odor removal, skin protection, fitness, beauty, skin moistening and the like; the fabric is good in skin friendliness, good in comfortability, good in moisture absorption and breathability, good in chromaticity and soft in hand feel; an appearance of a product is noble, elegant and unique; the color is bright and rich in gloss; ultraviolet resistance is good; an application of the product is wide; and top-grade, high-quality and health-care textile can be produced in the field of knitting or weaving.

Description

technical field [0001] The invention relates to spinning and its application, in particular to a semi-worsted bamboo charcoal polyester fiber, nylon fiber, long-staple cotton fiber and wool fiber blended health care yarn, production method and application thereof. Background technique [0002] Bamboo charcoal polyester fiber is a functional fiber with far-infrared rays and negative ion effects. It continuously generates negative ions and releases far-infrared rays under natural conditions. The health care function of human immunity. Compared with other fibers, it has high functionality, good air permeability, unique resilience, greater strength and luster. However, the fabric made of pure bamboo charcoal polyester fiber has poor hygroscopicity, poor bulkiness and not soft feel. [0003] Nylon fiber has good strength, high toughness, good wear resistance, high elongation at break, and good mildew and moth resistance. However, nylon fiber is not light-resistant, has low mod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D02G3/44
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com