A technology of high-temperature leveling agent and polyester polyether, which is applied in dyeing, textiles and papermaking, can solve the problems of complex production process, high cost, and lack of finishing effect, and achieve uniform color of fabrics, cost of raw materials and manufacturing The effect of low cost, good antistatic properties and hydrophilic properties

Active Publication Date: 2013-09-25
DUPLUS CHEM OF ZHANGJIAGANG CITY
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing leveling agent only has a leveling effect and does not have other finishing effects
For polyester fibers or their fabrics, it is necessary to carr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature leveling agent, and preparation method and application thereof
  • High-temperature leveling agent, and preparation method and application thereof
  • High-temperature leveling agent, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of high temperature leveling agent, it is prepared by following steps:

[0025] (1) Weigh 800 grams of polyethylene glycol (PEG4000), 150 grams of ethylene glycol, 125 grams of dihydroxypolyether, 140 grams of dimethyl terephthalate, and 150 grams of amino-terminated double-header silicone, 50g of 3-piperazinepropylmethyldimethoxysilane, 10g of magnesium acetate;

[0026] (2) Put the above materials into the reaction kettle, raise the temperature to 140°C and keep it for 180 minutes, then continue to raise the temperature to 220°C and keep it for 60 minutes. Then carry out polymerization at a vacuum degree of -0.08MPa and a temperature of 240°C to generate a polyester polyether silicone oil block copolymer, which is cooled to 190°C and discharged to obtain a polyester polyether silicone oil block copolymer;

[0027] (3) Mix the polyester polyether silicone oil block copolymer obtained in step (2), polyethylene glycol (200) monostearate and water in a weight rati...

Embodiment 2

[0029] A kind of high temperature leveling agent, it is prepared by following steps:

[0030] (1) Weigh 900 grams of polyethylene glycol (PEG2000), 140 grams of ethylene glycol, 140 grams of dihydroxypolyether, 165 grams of dimethyl terephthalate, and 180 grams of amino-terminated double-header silicone, 3-piperazinepropylmethyldimethoxysilane 60g, zinc acetate 6g;

[0031] (2) Put the above materials into the reaction kettle, raise the temperature to 150°C and keep it for 180 minutes, then continue to raise the temperature to 230°C and keep it for 60 minutes. Then carry out polymerization, carry out polymerization at a vacuum degree of -0.08MPa, and a temperature of 260°C to generate a polyester polyether silicone oil block copolymer, and discharge it after cooling down to 200°C to obtain a polyester polyether silicone oil block copolymer;

[0032] (3) Mix the polyester polyether silicone oil block copolymer obtained in step (2), polyethylene glycol (200) monostearate and wa...

Embodiment 3

[0034] A kind of high temperature leveling agent, it is prepared by following steps:

[0035] (1) Weigh 700 grams of polyethylene glycol (PEG2000), 125 grams of ethylene glycol, 125 grams of dihydroxypolyether, 130 grams of dimethyl terephthalate, and 150 grams of amino-terminated double-header silicone, 50 grams of 3-piperazinepropylmethyldimethoxysilane, 10 grams of calcium acetate;

[0036] (2) Put the above materials into the reaction kettle, raise the temperature to 170°C and keep it for 180 minutes, continue to raise the temperature to 220°C and keep it for 60 minutes, then carry out polymerization at a vacuum degree of -0.09MPa and a temperature of 250°C to form The polyester polyether silicone oil block copolymer is discharged after cooling down to 200°C to obtain the polyester polyether silicone oil block copolymer;

[0037] (3) Mix the polyester polyether silicone oil block copolymer obtained in step (2), polyethylene glycol (600) monostearate and water in a weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-temperature leveling agent, and a preparation method and an application thereof. The high-temperature leveling agent is prepared from 0.1-1% of a polyester-polyether-silicon oil block copolymer, 9-10% of polyethylene glycol monostearate, and balance of water. The polyester-polyether-silicon oil block copolymer is prepared from the raw materials of, by weight: 120-160 parts of polyethylene glycol, 18-30 parts of glycol, 15-25 parts of dihydroxy polyether, 20-28 parts of dimethyl terephthalate, 10-30 parts of an amino-terminated double-head sealant organosilicon, 5-10 parts of 3-piperazine propyl dimethoxysilane, and 0.2-2 parts of metal acetate. With the high-temperature leveling agent provided by the invention, dyeing quality of polyester fiber or fabric thereof can be improved, and the dyed polyester fiber or fabric thereof is provided with excellent fluffy and soft property, good antistatic performance, and good hydrophilic property. The dyed polyester or fiber thereof can be provided with excellent comfortableness with no other finishing.

Description

technical field [0001] The invention relates to the technical field of fabric finishing agents, in particular to a high-temperature leveling agent and a preparation method thereof. Background technique [0002] As we all know, polyester fiber has poor fluffy softness, moisture absorption and perspiration, antistatic performance and easy decontamination performance. Therefore, the textiles processed with polyester fibers have poor wearability, are easy to stick to dirt, and are prone to static electricity. This will undoubtedly cause certain harm to human health. In order to overcome the shortcomings of polyester fiber and to meet the increasingly high requirements of the market for textiles, polyester fiber must be finished in order to improve its performance. [0003] It is also known that in the dyeing process of fiber yarns, threads or fabrics, it is often necessary to add a leveling agent in order to promote uniform dyeing and avoid defects such as color stripes and st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P1/52D06P1/60D06P1/613C08G63/695C08G63/672
Inventor 陈金辉吴玉春方玉琦王宇飞吴宇文
Owner DUPLUS CHEM OF ZHANGJIAGANG CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap