A production method and zipper technology, which is applied in the field of zippers, can solve problems such as short dipping time, affecting production efficiency, and difficulty in accurately controlling dipping time, and achieve the effects of ensuring stable production and reducing the color difference of chain teeth

Inactive Publication Date: 2013-10-09
王萍煌
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In production, as the concentration of the electroless tin plating solution changes, the immersion time is affected by the concentration of the electroless tin plating solution. If the concentration is high, the immersion time required is short, and if the concentration is low, the immersion time required is long. The required immersion time Difficult to control accurately
In actual production, the zipper color difference often occurs (the zipper is white or yellowish), which causes the zipper to be reworked and affects the production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The H65 brass zipper was selected for the experiment, and it was processed according to the following steps:

[0019] (a) Ultrasonic degreasing of the zipper: The parameters of the ultrasonic degreasing liquid are: sodium hydroxide 0.5% (mass fraction, the same below), sodium carbonate 3%, sodium phosphate 0.8%, OP emulsifier 0.8%, temperature 60 ℃. For example, GDS-1036 ultrasonic degreasing machine is used, the ultrasonic power is 2160W, the ultrasonic frequency is 28KHZ, and the size of the inner tank is 650mm (length) × 500mm (width) × 430mm (height). Clean the zipper with clean water after ultrasonic degreasing for 10 minutes.

[0020] (b) Polish the zipper: first immerse the zipper in the polishing solution for 4 minutes to form a layer of purple-red film on the surface of the zipper. The composition of the polishing solution is: 30wt% hydrogen peroxide 600ml / L, 98wt% sulfuric acid 6ml / L, and the balance is water; then place the zipper in a 98wt% sulfuric acid ...

Embodiment 2

[0025] The H65 brass zipper was selected for the experiment, and it was processed according to the following steps:

[0026] (a) Ultrasonic degreasing of the zipper: The parameters of the ultrasonic degreasing liquid are: sodium hydroxide 0.5% (mass fraction, the same below), sodium carbonate 3%, sodium phosphate 0.8%, OP emulsifier 0.8%, temperature 60 ℃. For example, GDS-1036 ultrasonic degreasing machine is used, the ultrasonic power is 2160W, the ultrasonic frequency is 28KHZ, and the size of the inner tank is 650mm (length) × 500mm (width) × 430mm (height). Clean the zipper with clean water after ultrasonic degreasing for 10 minutes.

[0027] (b) Polish the zipper: first immerse the zipper in the polishing solution for 10 minutes to form a layer of purple-red film on the surface of the zipper. The composition of the polishing solution is: 30wt% hydrogen peroxide 400ml / L, 98wt% sulfuric acid 4ml / L, and the balance is water; then place the zipper in a 98wt% sulfuric acid...

Embodiment 3

[0032] The H65 brass zipper was selected for the experiment, and it was processed according to the following steps:

[0033] (a) Ultrasonic degreasing of the zipper: The parameters of the ultrasonic degreasing liquid are: sodium hydroxide 0.5% (mass fraction, the same below), sodium carbonate 3%, sodium phosphate 0.8%, OP emulsifier 0.8%, temperature 60 ℃. For example, GDS-1036 ultrasonic degreasing machine is used, the ultrasonic power is 2160W, the ultrasonic frequency is 28KHZ, and the size of the inner tank is 650mm (length) × 500mm (width) × 430mm (height). Clean the zipper with clean water after ultrasonic degreasing for 10 minutes.

[0034] (b) Polish the zipper: first immerse the zipper in the polishing solution for 10 minutes to form a layer of purple-red film on the surface of the zipper. The composition of the polishing solution is: 30wt% hydrogen peroxide 500ml / L, 98wt% sulfuric acid 5ml / L, and the balance is water; then place the zipper in a 98wt% sulfuric acid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method of light-golden zippers, and belongs to the field of zippers. The manufacturing method of the light-golden zippers includes the steps that after the zippers are processed in an oil-removing mode, the zippers are processed in a chemical polishing mode, after the chemical polishing, silver is displaced chemically to form a silver layer, then the zippers are dried in a water-throwing mode, the zippers are baked for 20-30 minutes at the temperature of 120-130 DEG C, and finally, varnish coating and stoving curing are performed. Traditionally, by relying on manual experience, the light-golden zippers are formed in a chemical tinning mode, but according to the manufacturing method, yellowing processing is performed after the sliver is displaced chemically, through accurate control of the baking temperature and the baking time, color difference of the zippers is reduced, reworking is reduced, and the zippers are steadily produced.

Description

technical field [0001] The invention relates to the field of zippers, in particular to a method for making a light gold zipper. Background technique [0002] At present, the zippers on the market are mainly divided into three categories: nylon zippers, plastic steel zippers, and metal zippers. Common metal zippers are generally made of brass substrates, which are mainly oxidized and colored to enrich the color of the zipper and improve the corrosion resistance of the zipper. Among them, the light gold zipper is generally made in this way: after the brass zipper is degreased, the zipper is chemically polished. After polishing, the surface of the zipper is smooth and golden yellow; then the zipper is dipped in chemical tin plating solution. A thin layer of silver-white tin layer is formed on the zipper, and the zipper is quickly taken out for cleaning, so that the golden-yellow zipper is silver-white and becomes light gold. Using this method requires good manual operation ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A44B19/42C23F3/06C23C18/42
Inventor 王萍煌
Owner 王萍煌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com