Abrasion-resistant anti-impact multi-hole cable protective pipe and preparing method thereof
A technology for protecting pipes and cables, which is applied in the field of wear-resistant and impact-resistant porous cable protection pipes and their preparation. It can solve the problems of limiting the use efficiency of cable pipes, PVC pipes are easy to freeze and crack, and lag behind, so as to improve the function and use Efficiency, high impact strength, and improved service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0018] Example 1
[0019] Take 100 parts of polyvinyl chloride resin; 5 parts of composite impact modifier; 3 parts of 30 micron molybdenum disulfide powder; 10 parts of 100 nanometer alumina powder; 0.2 part of aminosilane; 0.5 part of antioxidant 1010; 0.5 part of didecyl adipate; 0.5 part of zinc stearate; 2 parts of color masterbatch according to the proportion of parts by weight. Put the raw materials into the high-speed mixer in turn for blending, the speed is 500 rpm, the stirring temperature is 50 ℃, stir and mix for 5 minutes, then form by twin screw extruder.
[0020] The composite impact modifier is a mixture of polyethylene and ethylene-octene copolymer with a molecular weight of 2-8 million and a diameter of 1-10 microns in a weight ratio of 1:1, and then smashed after mixing at 150°C for 5 minutes Become.
[0021] The temperature of the extruder barrel is 170°C in the first zone; 175°C in the second zone; 180°C in the third zone; 185°C in the fourth zone; the die temp...
Example Embodiment
[0022] Example 2
[0023] Take 100 parts of polyvinyl chloride resin; 3 parts of composite impact modifier; 2 parts of 20-micron graphite powder; 10 parts of 100-nanometer boron nitride powder; 0.3 part of octylsilane; 0.5 part of antioxidant 1010; 0.5 part of didecyl adipate; 0.5 part of zinc stearate; 3 parts of color masterbatch according to the proportion of parts by weight. Put the raw materials into a high-speed mixer for blending at a speed of 500 rpm and a stirring temperature of 50 ℃, stir and mix for 5 minutes, then form by twin screw extruder.
[0024] The composite impact modifier is a mixture of acrylonitrile-butadiene-styrene copolymer and ethylene-vinyl acetate copolymer at a weight ratio of 1:1, banburying at 150°C for 5 minutes and then crushing. The technical parameters of the ethylene-vinyl acetate copolymer are melt index ≤ 5 g / 10min, ASTM D-1238, 100℃, 1.2kg; VA content 50 wt%, Mooney viscosity ML1+4, 27 at 100℃ ±4, density 1.00 g / cm 3 .
[0025] The temperatu...
PUM
Property | Measurement | Unit |
---|---|---|
Melt index | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap