Special paint for wear-resistant skid-resistant sport field

A technology for sports venues and coatings, applied in the field of coatings, to achieve the effects of good antibacterial properties, improved wear resistance and anti-skid performance, and excellent mechanical properties

Inactive Publication Date: 2013-11-13
WUJIANG WUHUA HARDWARE PROD
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Acrylic coatings are widely used in sports field coatings. With the development of acrylic coatings and the continuous increase in usage, the performance requirements are getting higher and higher. Although the existing acrylic coatings can meet the basic requirements of sports venues for coatings, but There is still a lot of room for further modification of acrylic coatings to improve their deficiencies in abrasion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Wear-resistant and non-slip special coating for sports venues, including the following raw materials in parts by mass: 180 parts of acrylic emulsion, 100 parts of nano rubber powder, 20 parts of ethylene glycol, 1.6 parts of hydroxyethyl cellulose, 10 parts of silicon micropowder, nano-oxidized 10 parts of zinc, 5 parts of zinc green, 1 part of water-based bentonite, 1.5 parts of TRITON X-405, 2.2 parts of simethicone.

[0014] The preparation method of the present invention: according to the above-mentioned proportion, according to the mass proportion, add hydroxyethyl cellulose to ethylene glycol for pre-mixing, and then add dimethyl silicone oil, TRITON X-405, water-based bentonite, silicon micropowder, and nano rubber powder and nano zinc oxide, stir and mix evenly, then add acrylic acid emulsion and zinc green, stir for 8 minutes, and filter to obtain the finished product of the present invention.

Embodiment 2

[0016] Wear-resistant and non-slip special coating for sports venues, including the following raw materials in parts by mass: 200 parts of acrylic emulsion, 150 parts of nano rubber powder, 25 parts of ethylene glycol, 2 parts of hydroxyethyl cellulose, 15 parts of silicon micropowder, nano-oxidized 20 parts of zinc, 10 parts of zinc green, 2 parts of water-based bentonite, 2 parts of TRITON X-405, 2.8 parts of simethicone.

[0017] The preparation method of the present invention: the same as in Example 1, the mass proportion is as above, and the finished product of the present invention can be obtained.

Embodiment 3

[0019] Wear-resistant and non-slip special coating for sports venues, including the following raw materials in parts by mass: 190 parts of acrylic emulsion, 130 parts of nano rubber powder, 22 parts of ethylene glycol, 1.8 parts of hydroxyethyl cellulose, 13 parts of silicon micropowder, nano-oxidized 16 parts of zinc, 8 parts of zinc green, 1.6 parts of water-based bentonite, 1.8 parts of TRITON X-405, 2.6 parts of simethicone.

[0020] The preparation method of the present invention: the same as in Example 1, the mass proportion is as above, and the finished product of the present invention can be obtained.

[0021] The performance test of the coating obtained in the present invention: the anti-slip performance is good, and the friction coefficient can reach 5; the elasticity is good, it is not easy to crack, and there is a comfortable sense of movement; the heat-resistant temperature is high, up to 300 ° C; 6% sodium chloride solution), salt spray resistance and alkali resi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Heat resistance temperatureaaaaaaaaaa
Login to View More

Abstract

A special paint for a wear-resistant skid-resistant sport field consists of the following raw materials in parts by mass: 180-200 parts of an acrylic acid emulsion, 100-150 parts of a nanometer rubber powder, 20-25 parts of glycol, 1.6-2 parts of hydroxyethyl cellulose, 10-15 parts of silicon powder, 10-20 parts of nanometer zinc oxide, 5-10 parts of zinc green, 1-2 parts of water-based bentonite, 1.5-2 parts of a wetting agent, 2.2-2.8 parts of dimethicone, wherein the special paint wetting agent for the wear-resistant skid-resistant sport field is a wetting agent Dow TRITONX-405. The paint has good wear resistance, skid resistance and toughness, better flame resistance, excellent weatherability, excellent mechanical properties and good antibacterial property; and the paint is difficult in infection of dust, simple in daily nursing and effectively reduced in cost, and is widely applicable to sport fields such as tennis courts, basketball courts, badminton courts and the like.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a special coating for wear-resistant and anti-slip sports grounds. Background technique [0002] Acrylic coatings are widely used in sports field coatings. With the development of acrylic coatings and the continuous increase in usage, the performance requirements are getting higher and higher. Although the existing acrylic coatings can meet the basic requirements of sports venues for coatings, but There is still a lot of room for further modification of acrylic coatings to improve their deficiencies in abrasion resistance. [0003] To sum up, how to overcome the deficiencies of the prior art has become an urgent problem to be solved in the field of coatings. Contents of the invention [0004] The purpose of the present invention is to overcome the deficiencies of the prior art and propose a special coating for wear-resistant and anti-slip sports fields. The coating of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D121/00C09D7/12
Inventor 庄亚东
Owner WUJIANG WUHUA HARDWARE PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com