Release agent for coating release paper, preparation method of release agent and release paper prepared by utilizing release agent

A technology of release paper and release agent, applied in special paper, paper, papermaking and other directions, can solve the problems of affecting product performance and service life, large shrinkage, high equipment requirements, etc., to achieve simple formula and preparation method, production cost Low, good release effect

Inactive Publication Date: 2013-11-20
浙江池河科技有限公司
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Radical radiation curing system has been widely used in the release paper industry, but it is generally necessary to isolate oxygen during the processing to prevent incomplete surface curing due to the inhibition of oxygen molecules, so the equipment requirements are relatively high; on the other hand, The shrinkage of the system after curing is large, which affects the performance and service life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Add 350g of amino silicone oil (purchased from Shandong Dayi Chemical Co., Ltd., model DY-N322, the same model of amino silicone oil unless otherwise specified in the following examples), 650g of epoxy diluent 622 into a 1000mL four-necked flask and stir to mix evenly , heated to 60°C to 65°C, kept warm for 4h, then cooled to room temperature and discharged to prepare a release agent for coated release paper for artificial leather production.

Embodiment 2

[0044] Add 400g of amino silicone oil and 600g of epoxy diluent 622 into a 1000mL four-necked flask, stir and mix evenly, heat to 60°C-65°C, keep warm for 6h, then cool to room temperature and discharge to prepare a coated anti-corrosion material for artificial leather production. Release agent for sticky paper.

Embodiment 3

[0046] Add 450g of amino silicone oil and 550g of epoxy diluent 622 into a 1000mL four-neck flask, stir and mix evenly, heat to 60°C-65°C, keep warm for 6h, then cool to room temperature and discharge to prepare a coated anti-corrosion material for artificial leather production. Release agent for sticky paper.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a release agent for coating release paper, a preparation method of the release agent and release paper prepared by utilizing the release agent. The release agent comprises the following raw materials by weight percent: 30-60% of amino silicon oil and 40-70% of epoxy diluent. The preparation method comprises the following steps of: uniformly mixing the amino silicon oil with the epoxy diluents in proportion, heating the mixture to 50 to 80 DEG C, reacting for 1-6 hours, and cooling to the room temperature, so as to obtain the release agent for coating the release paper. The release paper sequentially comprises raw paper, a bottom coating and a release coating, wherein the bottom coating and the release coating are sequentially adhered to one side of the surface of the raw paper, and the release coating is formed after the release agent for coating the release paper is coated and thermally cured. By combining a formula disclosed by the invention with the preparation method disclosed by the invention, the release effect of the prepared release agent is good, the formula and the preparation method are relatively simple and suitable for large-scale industrial production, and the production cost is low.

Description

technical field [0001] The invention relates to the field of artificial leather processing and manufacturing, in particular to a release agent for coating release paper, a preparation method thereof, and a release paper prepared by using the release agent. Background technique [0002] Coated release paper for artificial leather production belongs to a special type of release paper, which is the carrier and temporary template for the manufacture of polyurethane artificial leather (PU leather) and polyvinyl chloride artificial leather (PVC leather). Coated release papers for artificial leather production usually have a two-layer structure: the first layer is base paper as a substrate, and the second layer is a release coating. The general manufacturing method is to apply a layer of primer on the base paper to prevent the penetration of the release agent, and then coat the coating containing the release agent, emboss and cure, and form a release coating on the primer. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H19/24D21H19/10D21H27/00
Inventor 陈冬平
Owner 浙江池河科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap