Electronic grade glass fiber cloth surface treating agent and method for producing glass fiber cloth

A technology of glass fiber cloth and surface treatment agent, which is applied in the field of electronic grade glass fiber cloth surface treatment agent and its production of glass fiber cloth, can solve the problem of increasing cost, affecting the close combination of glass cloth and resin, and affecting the reliability of circuit board substrates. and other problems, to achieve the effect of good bonding, fast impregnation and strong water resistance

Inactive Publication Date: 2013-12-04
TAIJIA GLASS FIBER
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] If the treatment agent is not evenly coated on the surface of the glass fiber cloth or the treatment agent cannot penetrate between each monofilament of the glass fiber cloth, it will directly affect the close combination of the glass cloth and the resin, so that the reliability of the formed circuit board substrate sex is severely affected
After the plate is made, its heat resistance and water resistance must be continuously improved, which increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An electronic-grade glass fiber cloth surface treatment agent, comprising the following components in mass percentage: 0.3% of silane coupling agent, 0.3% of acid regulator, 0.1% of surfactant, and the rest is deionized water;

[0031] The general formula of the silane coupling agent is (Y(CH 2 ) n SiX 3 ), n=0-3;

[0032] The structural formula is

[0033]

[0034] Among them, R 1、 R 2 is a hydrocarbon group;

[0035] X represents a hydrolyzable group, methoxy, ethoxy, acetoxy or halogen;

[0036] Y represents an organic functional group, such as vinyl, amino, methacryloyloxy and the like.

[0037] In the above technical solution, the acid regulator is acetic acid, the surfactant is an organosilicon nonionic surfactant, and the pH of the surface treatment agent is 2-7 through detection.

[0038] A method for producing glass fiber cloth with an electronic-grade glass fiber cloth surface treatment agent, using the electronic-grade glass fiber cloth surface trea...

Embodiment 2

[0044] The rest are the same as the above examples, except that an electronic-grade glass fiber cloth surface treatment agent includes the following components in mass percentage: 0.9% of silane coupling agent, 0.8% of acid regulator, 0.5% of surfactant, and the rest for deionized water.

Embodiment 3

[0046] The rest are the same as the above examples, except that the following components are included in mass percentage: 0.5% of silane coupling agent, 0.4% of acid regulator, 0.2% of surfactant, and the rest is deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an electronic grade glass fiber cloth surface treating agent. The surface treating agent comprises the following ingredients, by weight, 0.3%-0.9% of silane coupling agents, 0.3%-0.8% of acidity regulators, and 0.1%-0.5% of surfactants, the balance being deionized water. The glass fiber cloth after treated by the electronic grade glass fiber cloth surface treating agent has good heat resistant performance, good water resistant performance and good wetting property, and has good combination with resins.

Description

technical field [0001] The invention relates to a surface treatment agent, in particular to an electronic-grade glass fiber cloth surface treatment agent applied to printed circuit board insulation reinforcement materials and a method for producing the glass fiber cloth. Background technique [0002] Electronic-grade glass fiber cloth is an inorganic non-metallic material, and the resin is an organic structure. When used as a printed circuit board substrate, the two cannot directly undergo a chemical reaction. In order to effectively combine the two, it is usually necessary to coat the surface of the glass fiber cloth with a Layer treatment agent, the two ends of the treatment agent molecule are inorganic functional groups and organic functional groups, the inorganic functional groups are closely combined with the surface of the glass fiber cloth, and the organic functional groups are reacted and combined with the resin, so that the surface properties of the glass fiber can b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/647C08J5/08
Inventor 林嘉佑
Owner TAIJIA GLASS FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap