Cellulose triacetate membrane

A technology of cellulose triacetate and ester film, applied in the field of cellulose triacetate film, can solve the problems of quality defects, affecting the appearance of the film, precipitation of plasticizers, etc. Effect

Inactive Publication Date: 2013-12-25
CHINA LUCKY FILM CORP
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to replace phthalate plasticizers, relevant literature discloses that triphenyl phosphate esters and biphenyl diphenyl phosphate can be used in combination to improve the physical and mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cellulose triacetate membrane
  • Cellulose triacetate membrane
  • Cellulose triacetate membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025]

[0026] Add 1.2 parts of triphenyl phosphate and 0.3 parts of bisphenol A bis(diphenyl phosphate) into a mixed solvent of 70 parts of methylene chloride and 6 parts of methanol, stir and dissolve, and then add 14 parts of cellulose triacetate, Filtration after dissolving, casting, stripping, drying and winding to obtain the cellulose triacetate film of the present invention. Measure its performance.

Embodiment 2

[0028]

[0029] Add 1.0 parts of triphenyl phosphate and 0.2 parts of bisphenol S bis(diphenyl phosphate) into a mixed solvent of 72 parts of dichloromethane and 8 parts of methanol, stir and dissolve, then add 14 parts of cellulose triacetate to dissolve After filtering, casting, stripping, drying and winding, the cellulose triacetate film of the present invention is obtained. Measure its performance.

Embodiment 3

[0031]

[0032] Add 0.3 parts of triphenyl phosphate and 0.2 parts of resorcinol tetraphenyl diphosphate into a mixed solvent of 76 parts of dichloromethane and 4 parts of methanol, stir and dissolve, then add 14 parts of cellulose triacetate, and dissolve Filtration, casting, stripping, drying and winding to obtain the cellulose triacetate film of the present invention. Measure its performance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cellulose triacetate membrane which is prepared from a solution containing cellulose triacetate, a solvent and a plasticizer by using a solution curtain-casting method. The cellulose triacetate membrane is characterized in that the dosage of the plasticizer is 3-15% of weight of the cellulose triacetate; the plasticizer is prepared from a triphenyl phosphate primary plasticizer and an aryl diphosphate coplasticizer; the weight ratio of aryl diphosphate to triphenyl phosphate is 1/6 to 4/5. By adopting the cellulose triacetate membrane, precipitation of the plasticizer caused by fluctuation of a production process condition in a membrane production process is solved; apparent defects of the membrane caused by precipitation of the plasticizer are avoided; the apparent mass, the optical property and the physical and mechanical properties of the membrane are ensured; meanwhile, the cellulose triacetate membrane accords with the environment-friendly emission requirements.

Description

technical field [0001] The invention relates to a cellulose triacetate film. Background technique [0002] Cellulose acetate with an average degree of esterification of 57.5~62.5% is generally called triacetate cellulose, and the triacetate cellulose film (TAC film) made of it is suitable for polarizing because of its excellent optical isotropy. In-chip protective film or color filter for liquid crystal display, anti-glare film, anti-reflection film, phase difference film and other functional film layers, and its market is expanding rapidly. [0003] TAC film is generally prepared by solution casting method, that is, cellulose triacetate, plasticizer, various additives, etc. are dissolved in a solvent to form a viscous high-concentration cotton glue solution, and then the high-concentration cotton glue solution is cast on On the strip or drum-shaped endless support, a film is formed through a series of processes such as drying and winding. Compared with other methods such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L1/12C08K5/523
Inventor 滕领贞孙志英成志秀千昌富
Owner CHINA LUCKY FILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap