High temperature-resistance and high aluminum layer adhesion transfer coating material composition and applications thereof

A technology for transferring coatings and compositions, applied in the direction of coating, etc., can solve the problems of surface fogging, resin material bubbles and pores, poor temperature resistance, etc., and achieve the effect of good adhesion and good temperature resistance

Active Publication Date: 2016-01-27
上海睿途新材料科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN102585648A discloses a regenerated coating for laser anodized aluminum film and its preparation method, using ethyl acetate and butyl acetate mixture (1:1) as solvent, and copolymer of acrylic monomer as matrix resin to overcome poor temperature resistance Defects
[0006] However, in the actual production and application process, the applicant also found that due to the aluminum plating transfer coating in the coating process, during the solvent volatilization process, especially in the case of high air humidity, fogging occurs on the surface, and even, Bubbles and pores in the resin material can easily be caused by heating the coating process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature-resistance and high aluminum layer adhesion transfer coating material composition and applications thereof
  • High temperature-resistance and high aluminum layer adhesion transfer coating material composition and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Matrix resin 1) (Matrix1): methyl methacrylate homopolymer

[0050] Number average molecular weight 40000, ester 0.8mgKOH / g, softening point (ring and ball method) 200°C, Tg (DSC) 110°C, density (20°C) 1.18kg / L, viscosity (25°C, 25wt% butanone solution, Brookfield Viscometer) 30mPa·S

[0051] Matrix resin 2) (Matrix2): cellulose acetate-butyrate

[0052] Acetyl 29.5wt%, butyryl 17.5wt%, melting temperature 230-240°C, Tg151°C, viscosity 1.1-1.2 poise

[0053] Mix the components according to the ratio in Table 1.

Embodiment 2

[0055] Matrix resin 1): Methyl methacrylate homopolymer

[0056] Number average molecular weight 50000, ester 1mgKOH / g, softening point (ring and ball method) 220°C, Tg (DSC) 130°C, density (20°C) 1.15kg / L, viscosity (25°C, 25wt% methyl ethyl ketone solution, Brookfield viscosity meter) 25mPa·S

[0057] Matrix resin 2): cellulose acetate-butyrate

[0058] Acetyl 28.1wt%, butyryl 18.6wt%, melting temperature 250°C, Tg160°C, viscosity 1.15-1.22 poise

[0059] Mix the components according to the ratio in Table 1.

Embodiment 3

[0061] Matrix resin 1): Methyl methacrylate homopolymer

[0062] Number average molecular weight 40000, ester 0.8mgKOH / g, softening point (ring and ball method) 200°C, Tg (DSC) 110°C, density (20°C) 1.18kg / L, viscosity (25°C, 25wt% butanone solution, Brookfield Viscometer) 30mPa·S

[0063] Matrix resin 2): cellulose acetate

[0064] Acetyl 30.7wt%, melting temperature 225°C, Tg143°C, viscosity 1.12-1.2 poise

[0065] Mix the components according to the ratio in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
melting pointaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The present invention provides a high temperature-resistance and high aluminum layer adhesion transfer coating material composition and applications thereof. The composition comprises, by weight, 5-30% of a matrix resin material and a solvent, wherein the matrix resin is a composition of 1) a methyl methacrylate homopolymer and 2) cellulose and / or cellulose derivative, the solvent is a mixed solvent, and during the coating process, the mixed solvent is gradually volatilized, such that the coating needle eye bubbles and other apparent defects produced through the instant solvent volatilizing are avoided, the volatilization of the trace water in the coating material before the complete coating drying can be ensured, and the apparent fog generation phenomenon can be avoided, wherein the apparent fog generation phenomenon easily occurs when the relative air humidity is high.

Description

technical field [0001] The invention relates to a coating for printing, in particular to a transfer coating with high temperature resistance and high aluminum layer adhesion. Background technique [0002] Transfer aluminum-coated paper does not contain polymer materials such as PET and PP that are difficult to decompose, and has degradable and recyclable environmental protection properties. It is an environmentally friendly packaging material. Holographic technology can copy characters, patterns, etc. onto the surface of aluminum sprayed paper, so as to achieve good anti-counterfeiting effect. At the same time, transfer aluminum coated paper has the advantages of economy and beauty, and is currently widely used. [0003] Since the transfer coating needs to go through molding and hot stamping processes in the printing process, both of which are carried out at relatively high temperatures, therefore, the temperature resistance of the coating is very important. [0004] CN1025...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D101/14C09D133/12C09D101/12C09D101/26
Inventor 吴军华张绳凯
Owner 上海睿途新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com