Alcohol acid ripple finish and preparation method thereof

A wrinkle and alkyd technology, applied in polyester coatings, coatings, etc., can solve problems such as large safety hazards, complicated processes, and high risks, and achieve the effects of reducing hazards, simple production processes, and high cost performance

Active Publication Date: 2013-12-25
天津灯塔涂料工业发展有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the paint film of this wrinkle paint has good water resistance, high gloss and hardness, pure benzene is used as a diluent in the synthesis process of the phenolic wrinkle resin, which has certain toxicity; Refining is generally heated by open fire, which poses a great safety hazard, and the resin is composed of multiple hard resins that need to be refined by open fire at high temperature (290°C). The process is complex, costly, energy-consuming, and dangerous. According to national regulations, Tianjin Safety Supervision Bureau requires chemical companies within the outer ring road to prohibit the use of open flame heating to produce various resins, and the process must be changed, otherwise the production and sales of such products will be stopped
Therefore, it is of great practical significance to seek a wrinkle paint with good water resistance and high gloss to overcome the safety hazards existing in the production process of the existing wrinkle paint.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alcohol acid ripple finish and preparation method thereof
  • Alcohol acid ripple finish and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of alkyd wrinkle resin (60% by weight solid) (the weight solid refers to the weight of its solid share of the coating formula by weight), composed of soybean oil, glycerin, lead monoxide, phthalic anhydride, reflux xylene, tung oil, 200 # Composed of solvent oil and toluene, including 27kg of soybean oil, 6kg of glycerin, 0.02kg of lead monoxide, 21kg of phthalic anhydride, 4kg of refluxing xylene, 13kg of tung oil, 16kg of 200# solvent oil, and 25kg of toluene.

[0036] The preparation method of the above-mentioned alkyd wrinkle resin (weight solid 60%), the specific preparation steps are as follows:

[0037] (1) Weigh 27kg of soybean oil, 6kg of glycerin, 0.02kg of lead monoxide, 21kg of phthalic anhydride, 4kg of refluxing xylene, 13kg of tung oil, 16kg of 200# solvent oil, and 25kg of toluene, and set aside;

[0038] (2) Add the soybean oil with formula quantity and 80% glycerin with formula quantity into the reaction kettle, stir and heat up;

[0039] (3) R...

Embodiment 2

[0046]A kind of alkyd wrinkle resin (weight solid 62.5%) (the weight solid refers to the weight of its solids in the coating formula by weight), consisting of soybean oil, glycerin, lead monoxide, phthalic anhydride, reflux xylene, tung oil, 200 # Composed of solvent oil and toluene, including 30kg of soybean oil, 5kg of glycerin, 0.01kg of lead monoxide, 25kg of phthalic anhydride, 5kg of refluxing xylene, 10kg of tung oil, 20kg of 200# solvent oil, and 30kg of toluene.

[0047] The preparation method of the above-mentioned alkyd wrinkle resin (weight solid 62.5%), the specific preparation steps are as follows:

[0048] (1) Weigh 30kg of soybean oil, 5kg of glycerin, 0.01kg of lead monoxide, 25kg of phthalic anhydride, 5kg of refluxing xylene, 10kg of tung oil, 20kg of 200# solvent oil, and 30kg of toluene, and set aside;

[0049] (2) Add the soybean oil with formula quantity and 80% glycerin with formula quantity into the reaction kettle, stir and heat up;

[0050] (3) Rais...

Embodiment 3

[0057] A kind of alkyd wrinkle resin (weight solid 60.8%) (the weight solid refers to the weight of its solids in the coating formula by weight), consisting of soybean oil, glycerin, lead monoxide, phthalic anhydride, reflux xylene, tung oil, 200 # Composed of solvent oil and toluene, including 20kg of soybean oil, 10kg of glycerin, 0.03kg of lead monoxide, 15kg of phthalic anhydride, 2kg of refluxing xylene, 20kg of tung oil, 15kg of 200# solvent oil, and 25kg of toluene.

[0058] The preparation method of the above-mentioned alkyd wrinkle resin (weight solid 60.8%), the specific preparation steps are as follows:

[0059] (1) Weigh 20kg of soybean oil, 10kg of glycerin, 0.03kg of lead monoxide, 15kg of phthalic anhydride, 2kg of refluxing xylene, 20kg of tung oil, 15kg of 200# solvent oil, and 25kg of toluene, and set aside;

[0060] (2) Add the soybean oil with formula quantity and 80% glycerin with formula quantity into the reaction kettle, stir and heat up;

[0061] (3) R...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides alcohol acid ripple finish and a preparation method thereof. The alcohol acid ripple finish comprises, by weight, 50-60 parts of alcohol acid ripple resin (having solid content of 60+/-3wt%), 5-10 parts of polymerized oil pattern-adjustment resin, 2-3 parts of carbon black, 20-35 parts of light calcium, 0.5-1.5 parts of bentonite HFGEL-40A, 1-2.5 parts of lead naphthenate having the content of 10%, 2-3.5% of cobalt naphthenate having the content of 4%, 0.1-0.3 parts of an anti-skinning agent and 5-10 parts of toluene. The anti-skinning agent is methyl ethyl ketoxime, butyraldehyde oxime or cyclohexanone-oxime and is obtained by mixing. The film of the alcohol acid ripple finish has excellent characters, realizes a flexible change of ripple patterns according to user demands and can be prepared by a simple method.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to an alkyd wrinkle paint and a preparation method thereof. Background technique [0002] Most of the wrinkle paints currently used in the market are phenolic wrinkle paints based on phenolic wrinkle resin. The surface of the wrinkle paint looks like the hammer pattern left by hammering iron plates. It is used as a decorative coating on the surface of various metal products such as various medical devices, instruments, and instruments. However, although the paint film of this wrinkle paint has good water resistance, high gloss and hardness, pure benzene is used as a diluent in the synthesis process of the phenolic wrinkle resin, which has certain toxicity; Refining is generally heated by open fire, which poses a great safety hazard, and the resin is composed of multiple hard resins that need to be refined by open fire at high temperature (290°C). The process is complex,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D5/28C09D7/12
Inventor 黄继伟牛顺李月曹振亚王志敏张玉彬刘建颖
Owner 天津灯塔涂料工业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap