Cold mix epoxy resin material for quickly repairing epoxy asphalt pavement pits as well as preparation method and application thereof

A cold-mix epoxy resin and epoxy asphalt technology, which is applied to the coagulation pavement, buildings, roads and other directions of on-site paving, can solve the problem of developing into pits, affecting the normal use of bridges, and epoxy asphalt pavement. The lack of maintenance materials and other problems can achieve the effect of good waterproof performance, short open traffic time and good toughness

Inactive Publication Date: 2014-01-08
NANJING UNIV
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the widespread use of high-performance epoxy asphalt materials on steel bridge decks and the increase in the number of years of traffic, the pavement of epoxy asphalt steel bridge decks will also have various diseases, such as cracking, slurrying, bulging, potholes, and network cracks. , cracks, etc. Among them, cracks and bulges are the most common diseases. If the bulges are not treated in time, they will develop into potholes and affect the normal use of the bridge.
Since the research on epoxy asphalt steel bridge deck pavement started late in our country, most of the epoxy asphalt materials used were imported from abroad. There is even a lack of materials for repairing potholes in epoxy asphalt pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold mix epoxy resin material for quickly repairing epoxy asphalt pavement pits as well as preparation method and application thereof
  • Cold mix epoxy resin material for quickly repairing epoxy asphalt pavement pits as well as preparation method and application thereof
  • Cold mix epoxy resin material for quickly repairing epoxy asphalt pavement pits as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Example 1: Weigh 100 parts (parts by mass, the same below) bisphenol A glycidyl ether epoxy resin (E51) (provided by Wuxi Bluestar Petrochemical Co., Ltd.), add 10 parts of allyl glycidyl ether (Wuxi Bluestar Petrochemical Co., Ltd.), 5 parts of glycerol triglycidyl ether (provided by Wuxi Bluestar Petrochemical Co., Ltd.), 0.2 parts of γ-(2,3-epoxypropoxy)propyltrimethoxysilane ( KH-560) (provided by Nanjing Yudeheng Fine Chemical Co., Ltd.), 1 part of oil-soluble fumed silica (provided by Degussa, Germany), 0.1 part of carbon black (N660) (provided by Cabot Corporation of the United States), heating to 60°C, stirred for 1 hour, and cooled to room temperature to obtain component A of the cold-mix epoxy resin material for rapid repair of potholes in epoxy asphalt pavement layers.

Embodiment 2

[0050] Example 2: Weigh 100 parts of bisphenol A glycidyl ether epoxy resin (E51), add 10 parts of allyl glycidyl ether, 10 parts of glycerol triglycidyl ether, 0.2 parts of γ-(3,4 Epoxycyclohexane) ethyltrimethoxysilane (KH-530) (provided by Nanjing Wanda Silicon Industry Co., Ltd.), 1 part of oil-soluble fumed silica, 0.2 part of carbon black (N660), heated to 60 ° C, stirred After cooling to room temperature for 1 hour, component A of the cold-mix epoxy resin material for rapid repair of potholes in epoxy asphalt pavement was obtained.

Embodiment 3

[0051] Example 3: Weigh 100 parts of bisphenol A glycidyl ether epoxy resin (E51), add 5 parts of allyl glycidyl ether, 10 parts of glycerol triglycidyl ether, 0.5 parts of γ-(2,3 Glycidyloxy) propyltrimethoxysilane (KH-560), 2 parts of organically modified attapulgite (provided by Jiangsu Dianjinshi Attapulgite Research and Development Co., Ltd.), 0.3 parts of carbon black (N660), heated to 60 ℃, stirred for 1 hour, and cooled to room temperature to obtain component A of the cold-mix epoxy resin material for rapid repair of epoxy asphalt pavement potholes.

[0052] The preparation method of component B of cold mix epoxy resin material is as follows:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cold mix epoxy resin material for quickly repairing epoxy asphalt pavement pits. The cold mix epoxy resin material comprises a component A and a component B, wherein the component A mainly comprises epoxy resin, an active diluent, a coupling agent, a thixotropic agent and a reinforcing agent, and the component B mainly comprises a curing agent, an accelerant, a thixotropic agent, a defoaming agent and a toughening agent. The mass ratio of the component A to the component B is 100: (200 to 100): 260, a mixture of components A and B is mixed with aggregate to obtain a cold mix epoxy resin mixture, and the mass ratio of the sum of the A component and the B component to the aggregate is 16:84 to 19:81. The cold mix epoxy resin material for quickly repairing epoxy asphalt pavement pits disclosed by the invention has the advantages of high bonding strength, good toughness, good waterproofness, normal temperature mixing, simple construction process, short open traffic time, energy conservation, environmental protection, etc. The cold mix epoxy resin material disclosed by the invention is mainly suitable for quickly repairing epoxy asphalt pavement pits and suitable for quickly repairing such pavements as high grade highways, tunnels, airport runways, cement concrete bridge decks, etc. The invention discloses a preparation method of the cold mix epoxy resin material.

Description

technical field [0001] The invention relates to a cold-mixed epoxy resin material for rapid repair of potholes in epoxy asphalt paving layers, a preparation method and an application method thereof. Background technique [0002] High-performance epoxy asphalt material is a kind of polymer modified asphalt material, which uses high-performance epoxy resin and its curing agent as asphalt modifier. When the epoxy resin in the asphalt reacts with the curing agent, an irreversible three-dimensional network cross-linked structure will be formed. At this time, the asphalt is firmly bound in the cross-linked network formed by the epoxy resin, so that the asphalt cannot flow, and the crack resistance of asphalt is also greatly improved at low temperature, which fundamentally changes the thermoplastic behavior of asphalt and endows asphalt with excellent performance. Therefore, high-performance epoxy asphalt materials have the characteristics of high strength, good toughness, excelle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/02C08G59/38C08G59/36C08G59/50C08K13/06C08K9/04C08K3/34C08K3/36C08K3/04C04B26/14E01C7/30
Inventor 谢鸿峰张育歌孙一帆王睿王治流程镕时
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap