Silk/ES semi-perforated structure non-woven material and method for preparing same

A non-woven material, semi-opening technology, applied in the direction of non-woven fabrics, textiles, papermaking, degumming, etc., can solve the problems of not highlighting the advantages of fibers, and achieve the effect of saving silk consumption, low reverse osmosis, and feeling fluffy

Active Publication Date: 2014-01-15
SHANDONG DERUN NEW MATERIAL TECH
View PDF9 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the past, the idea of ​​compounding was to mix two kinds of fibers together, and make the fibers into non-wov...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silk/ES semi-perforated structure non-woven material and method for preparing same
  • Silk/ES semi-perforated structure non-woven material and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] (1) Prepare the bottom air-through non-woven fabric, using 100% ES (PE / PET) fibers with a fiber length of 38mm and a fineness of 1.5D, and the obtained bottom air-through non-woven fabric has a grammage of 18g / m 2 . Send the fiber raw materials into the cotton storage box, lay them in piles, grab them vertically and send them to the BG038 opening equipment for loosening and dissociation until they are mixed and opened until they are evenly opened. The resulting opening rate is 95%, and then pass through the BG218 carding machine The bottom fiber web is obtained by carding and cross-lapping machine, and the specific process parameters are: carding machine feeding speed 0.35m / min, cylinder speed 200m / min, web laying speed 46m / min, hot air flat net output speed 20m / min, The hot-air bonding temperature is 156°C, the wind pressure is 50Mpa, and the unevenness of the output fiber web is 2.0%, so as to obtain a hot-air nonwoven fabric.

[0048] (2) Prepare the upper layer sil...

Embodiment 2

[0054] (1) Prepare the bottom air-through fiber web, using 100% ES (PE / PET) fibers with a fiber length of 36mm and a fineness of 2D, and the obtained bottom air-through non-woven fabric has a grammage of 18g / m 2 , send the fiber raw materials into the cotton storage box, lay them in piles, grab them vertically and send them to the BG038 type opening equipment for loosening, dissociation, mixing and opening until uniform, the resulting opening rate is 95%, and then through BG218 type carding Machine carding and cross-lapping machine laying the net to obtain the bottom fiber web, specific process parameters: carding machine feeding speed 0.35m / min, cylinder speed 250m / min, web laying speed 50m / min, hot air flat net output speed 30m / min , the hot air bonding temperature is 156°C, the wind pressure is 50Mpa, and the unevenness of the output fiber web is 2.0%, and the hot air nonwoven fabric is obtained.

[0055] (2) Prepare the upper layer silk fiber web, using 100% silk fiber, fi...

Embodiment 3

[0061] (1) The hot air non-woven fabric directly purchased from the bottom air net, with a weight of 18g / m 2 , thickness 0.52mm.

[0062] (2) Prepare the upper layer of silk fiber web, using 100% silk fiber, the fiber length is 25mm-50mm, the fineness is 1D, and the weight of the upper layer of fiber web is 20g / m 2 , send the fiber raw materials into the cotton storage box, lay them in piles, grab them vertically and send them to the BG038 type opening equipment for loosening, dissociation, mixing and opening until uniform, the resulting opening rate is 95%, and then through BG218 type carding The upper fiber web is obtained by machine carding and cross-lapper machine laying. Specific process parameters: carding machine feeding speed 0.4m / min, cylinder speed 700m / min, web laying speed 50.0m / min, output fiber web speed 48m / min , the unevenness of the output fiber web is 3.0%

[0063] (3) Spread the silk fiber net on the upper layer of the hot-air non-woven fabric, and enter t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a silk/ES semi-perforated structure non-woven material and a method for preparing the silk/ES semi-perforated structure non-woven material. The non-woven material is formed by compositing two fiber net layers. The two fiber net layers are combined through spunlace in a tangling mode. The surface-layer fibers are provided with holes, the bottom-layer fibers are not provided with holes, and accordingly a semi-perforated structure is formed. The preparing method includes the steps that silk fibers are fed into a cotton storage box, debonding and dissociation are carried out to make the silk fibers evenly mixed and opened, and then carding and net laying are carried out to acquire the surface-layer silk fiber net; opening, carding, net laying and hot air bonding and strengthening are carried out on ES fibers to acquire the bottom-layer fiber net; the surface-layer silk fiber net is laid on the bottom-layer fiber net, the surface-layer silk fiber net and the bottom-layer fiber net are put into a spunlace unit together, and after spunlace forming is finished, dewatering, hydrophilic treatment, drying, winding and cutting are carried out to acquire the silk/ES semi-perforated structure non-woven material. The non-woven material prepared according to the method is provided with the semi-perforated structure, silk utilization ratio is high, water permeation time is short, and reverse osmosis amount is small.

Description

technical field [0001] The invention belongs to the field of nonwoven materials and their preparation, in particular to a silk / ES nonwoven material with a semi-open pore structure and a preparation method thereof. Background technique [0002] Silkworms cannot be exposed to any pesticides or harmful chemicals during the entire growth process. Silk fibers are thin and soft. The ingredient silk peptide contains 18 kinds of amino acids that are beneficial to the human body. It has strong compatibility with human skin and less irritation (stimulation to the skin) Coefficient of only 7.4%, while polyester is 25.5%), known as the "fiber queen", so silk is often regarded as the most "green" environmental protection fiber. In recent years, the pure natural products developed by some companies - silk needle-punched non-woven fabrics and silk spunlace non-woven fabrics are particularly eye-catching. This product has changed the single purpose of silk as clothing, and it can also be wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/4382D04H1/492D01C3/02
Inventor 靳向煜王娅吴海波殷保璞王洪黄晨黄健华陈晶晶
Owner SHANDONG DERUN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap