Preparation method of coated bismuth vanadate pigment
A bismuth vanadate and coating type technology is applied in the field of preparation of coating type bismuth vanadate pigments, which can solve the problems of weakened acid resistance of pigments, poor pigment performance, inability to improve the performance of bismuth vanadate, etc., so as to improve the acid resistance. , performance improvement, the effect of improving the coating effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] The preparation method of the coated bismuth vanadate pigment according to the present invention includes the steps of: providing a bismuth vanadate matrix with a prescribed particle size; preparing a bismuth vanadate matrix with a prescribed particle size and pure water to prepare a coated basic slurry; The coating base slurry is heated to carry out chemical reaction coating and pH adjustment. After the coating reaction is completed, it is filtered, washed, dried, calcined, wet milled, filtered, and washed to obtain coated bismuth vanadate; Bismuth vanadate and purified water to prepare coating basic slurry, repeat the previous step to a specified number of times to obtain the final coated bismuth vanadate pigment.
[0014] In the method for preparing the coated bismuth vanadate pigment according to the present invention, preferably, the specified number of repetitions is 1-3 times.
[0015] In the method for preparing the coated bismuth vanadate pigment according to the pr...
Example Embodiment
[0027] Example 1
[0028] Take 100g of bismuth vanadate substrate with an average particle size of 0.6μm, add 2L of purified water, stir to prepare a bismuth vanadate slurry, heat to 60℃, take 5.16g of ZnO and add HNO 3 After dissolving, add pure water to make the volume 43ml (to make Zn 2+ The concentration is 1.47mol / L), drip into the bismuth vanadate slurry, drip in 1.5h, and use 0.5mol / L Na 3 PO 4 ·12H 2 O maintains the pH value of 7.0. After the dripping is completed, continue to heat and stir for 1h, centrifuge precipitation filter, washing machine washing, drying, calcining in a muffle furnace at 400℃ for 2h, drum ball mill at 60RPM speed for wet ball milling for 1h, centrifuge Precipitation filtration, washing machine washing to obtain a layer of coated bismuth vanadate powder;
[0029] Prepare a slurry with pure water and a layer of coated bismuth vanadate powder at a mass ratio of 10:1, heat it to 65°C, and add 70ml1mol / L AlCl 3 Drop into the slurry, drop it within 30 minu...
Example Embodiment
[0032] Example 2
[0033] Take 100g of bismuth vanadate substrate with an average particle size of 0.6μm, add 2L of purified water, stir to prepare a bismuth vanadate slurry, heat to 30℃, take 3.39g of ZnO and add HNO 3 After dissolving, add pure water to make the volume 43ml (to make Zn 2+ The concentration is 0.97mol / L), drip into the bismuth vanadate slurry, drip in 1.5h, and use 0.5mol / L Na 3 PO 4 ·12H 2 O maintains the pH value of 7.0. After the addition is completed, continue to keep heat and stir for 1 hour, centrifuge precipitation filter, washing machine washing, drying, calcination in the muffle furnace at 200 ℃ for 2 hours, drum ball mill at 10RPM speed wet ball milling for 1 hour, centrifuge Precipitation filtration and washing machine washing to obtain a layer of coated bismuth vanadate powder;
[0034] Prepare a slurry with purified water and a layer of coated bismuth vanadate powder at a mass ratio of purified water of 10:1, heat it to 95°C, add 70mL1mol / L AlCl 3 Drop...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap