Method for forming metal gate

A metal gate, aluminum metal technology, applied in electrical components, semiconductor/solid-state device manufacturing, semiconductor devices, etc., can solve the problems of easy leakage current, affecting transistor stability, low interaction rate and efficiency between aluminum and polysilicon, etc. Achieving the effect of increased diffusion, increased speed and efficiency

Active Publication Date: 2017-07-14
SEMICON MFG INT (SHANGHAI) CORP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, as the size of the device continues to decrease, the impedance of the metal gate formed by the above method will increase, and leakage current will easily occur, and gaps will easily occur when filling the metal layer, which will affect the stability of the transistor. In order to solve the above problems, the application number The US patent of US6080646A proposes a method for forming a metal gate, comprising: providing a semiconductor substrate on which a dummy gate is formed; forming a dielectric layer on the semiconductor substrate, and the surface of the dielectric layer is in contact with The surface of the dummy gate is flush; an aluminum metal layer is formed on the surface of the dummy gate and the dielectric layer; annealing is performed, and the polysilicon in the dummy gate is exchanged with the aluminum in the aluminum metal layer to form a metal gate; the interactive polysilicon and some unreacted aluminum layer
[0009] However, in the above-mentioned method of forming an aluminum metal gate, the interaction rate and efficiency of aluminum and polysilicon are low, and the annealing temperature is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for forming metal gate
  • Method for forming metal gate
  • Method for forming metal gate

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0046] refer to Figure 4 , Figure 4 It is a schematic flow chart of the method for forming a metal gate according to the first embodiment of the present invention, including steps:

[0047] Step S21, providing a semiconductor substrate, forming a dummy gate on the semiconductor substrate, a gate dielectric layer is formed between the semiconductor substrate and the dummy gate, and the gate dielectric layer is a stack of an interface layer and a high-K dielectric layer structure;

[0048] Step S22, forming a dielectric layer on the surface of the semiconductor substrate, the surface of the dielectric layer being flush with the surface of the dummy gate;

[0049] Step S23, removing the dummy gate, forming a groove, and forming a functional layer on the bottom and sidewall of the groove;

[0050] Step S24, forming a silicon material layer on the surface of the functional layer in the groove, and the surface of the silicon material layer is flush with the surface of the diele...

no. 2 example

[0086] refer to Figure 13 , Figure 13 It is a schematic flow chart of the method for forming a metal gate according to the second embodiment of the present invention, including steps:

[0087] In step S31, a semiconductor substrate is provided, the semiconductor substrate includes a first region and a second region, a first dummy gate is formed on the first region of the semiconductor substrate, and a first dummy gate is formed on the second region of the semiconductor substrate. There is a second dummy gate;

[0088] Step S32, forming a dielectric layer on the surface of the semiconductor substrate, the surface of the dielectric layer being flush with the surfaces of the first dummy gate and the second dummy gate;

[0089] Step S33, removing the first dummy gate, forming a first groove, and forming a first functional layer on the bottom and side walls of the first groove;

[0090] Step S34, forming a first silicon material layer on the surface of the first functional lay...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

A formation method of a metal gate includes: providing a semiconductor substrate and forming pseudo gates on the semiconductor substrate; forming a dielectric layer on the surface of the semiconductor substrate; flushing the surface of the dielectric layer and the surfaces of the pseudo gate; removing the pseudo gates to form grooves, and forming functional layers at the bottoms and the side walls of the grooves; forming silicon layers on the surfaces of the functional layers in the grooves, wherein the surfaces of the silicon layers are flush with the surfaces of the dielectric layer; forming an aluminum metal layer on the surface of the dielectric layer and the surfaces of the silicon layers; annealing the semiconductor substrate in an atmosphere containing fluorine, wherein aluminum in the aluminum metal layer and silicon in the silicon layers are exchanged to form the metal gate, and the silicon and fluorine are reacted at the same time to form a fluorine silicon compound. Since annealing is performed in the atmosphere containing the fluorine, the exchanged silicon stored in the aluminum metal layer is consumed by the fluorine, speed and efficiency of silicon exchange in the aluminum and silicon layers in the aluminum metal layer are accordingly increased.

Description

technical field [0001] The invention relates to the field of semiconductor manufacturing, in particular to a method for forming an aluminum metal gate. Background technique [0002] With the continuous development of integrated circuit manufacturing technology, the feature size of MOS transistors is getting smaller and smaller. In order to reduce the parasitic capacitance of the gate of MOS transistors and improve the device speed, the gate stack of high K gate dielectric layer and metal gate structure is introduced into MOS transistors. In order to avoid the influence of the metal material of the metal gate on other structures of the transistor, the gate stack structure of the metal gate and the high-K gate dielectric layer is usually fabricated by a “gate last” process. [0003] Figure 1 ~ Figure 3 It is a schematic diagram of a cross-sectional structure of a metal gate fabricated by an existing "gate last" process. [0004] refer to figure 1 , provide a semiconductor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01L21/28
CPCH01L21/28158H01L21/823857
Inventor 洪中山
Owner SEMICON MFG INT (SHANGHAI) CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products