Preparation method of cork and solid wood cabinet boards

A cabinet and cork technology, applied in the field of preparation of building decoration materials, can solve the problems of not being able to achieve the aesthetic effect of decoration materials, destroying the natural pattern of oak bark, etc., and achieve the effect of natural and elegant colors

Inactive Publication Date: 2014-02-12
何永明
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing processing method destroys the natural pattern of the oak bark, and cannot achieve the aesthetic appearance of the decorative material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation method of the cork plus solid wood cabinet board of the present invention firstly prepares the surface layer granular fabric of the cork plus solid wood cabinet board, the surface layer pattern fabric of the cork plus solid wood cabinet board, and then composites the surface layer particle fabric and the surface pattern fabric with polyurethane glue On the solid wood board, pressurize, dry, paint, sand and trim, the specific steps are as follows:

[0034] Preparation of cork plus solid wood cabinet top layer particle fabric:

[0035] 1. Dry the oak bark and put it into a pulverizer for crushing, then carry out cone milling, put the oak bark particles after cone milling into a vibrating screen for screening, and then carry out steel milling to obtain a diameter of 0.05-0.2mm and a bulk density of 55- 65g / dm 3 of cork particles;

[0036] 2. Put the cork particles into the mixer, add polyurethane glue according to the ratio of 180kg cork particles to 21.6...

Embodiment 2

[0046] Preparation of cork plus solid wood cabinet top layer particle fabric:

[0047] 1. Dry the oak bark and put it into a pulverizer for crushing, then carry out cone milling, put the oak bark particles after cone milling into a vibrating screen for screening, and then carry out steel milling to obtain a diameter of 0.05-0.2mm and a bulk density of 55- 65g / dm 3 of cork particles;

[0048]2. Put the cork particles into the mixer, add polyurethane glue according to the ratio of 180kg cork particles to 21.6kg polyurethane glue, mix and stir for 30 minutes, then take it out and put it into a round mold with a diameter of 1m and a height of 1.3m , use a 200-250 ton press to press the blank to get the blank;

[0049] 3. The billet is heated by electric heating, and kept at a high temperature of 80-120°C for 4 hours, then released from the furnace and cooled naturally for 3 hours, then removed from the mold, and then cut out a cork coil with a width of 1.3m and a thickness of 2m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of cork and solid wood cabinet boards. The preparation method comprises the steps as follows: firstly, a cork and solid wood cabinet board surface layer particle fabric and a cork and solid wood cabinet board surface layer pattern fabric are prepared, and then the surface layer particle fabric and the surface layer pattern fabric are composited on the cabinet boards for pressurization, drying and trimming; or firstly, the surface layer particle fabric is prepared, then two surfaces of the surface layer particle fabric are composited on the cabinet boards by polyurethane glue, and the cork and solid wood cabinet boards with various patterns are printed by a printing machine. With the adoption of the preparation method, the cork and solid wood cabinet boards with different colors and various patterns can be prepared.

Description

technical field [0001] The invention relates to a method for preparing a building decoration material, in particular to a method for preparing a cork plus solid wood cabinet board. Background technique [0002] Cork is processed from oak bark. The section of oak bark is composed of cork parenchyma cells arranged in a hexagonal honeycomb shape. The cells are filled with air. The main component of the cell wall is suberin, which is a kind of hydroxy acid. Polyester with phenolic acid, chemically stable. Because of this special cell structure and chemical composition, cork products have unique properties, such as sound absorption, moisture resistance, pollution prevention, insect resistance, antistatic, heat insulation, insulation and other characteristics. As a pure natural decorative material, it is more beneficial to human health and also meets the needs of human environmental protection. Moreover, the cork decorative board has a unique natural pattern, which can be used f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/08
Inventor 何永明
Owner 何永明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap