Waterproof ceramic tile adhesive material

A tile adhesive and permeable material technology, applied in the field of waterproof tile adhesive materials, can solve the problems of weakening the bonding performance of walls and tiles, failing to play the waterproof function of buildings, affecting building and personal safety, etc., and achieving improved compactness and waterproof and anti-seepage performance, improve compactness and waterproof and anti-seepage performance, and reduce porosity

Active Publication Date: 2014-03-05
广东龙马新材料科技有限公司
View PDF2 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this method, the waterproof paint is painted on the ordinary plastering mortar layer and then the tiles are pasted. Often there will be swelling and separation between the coating and the wall mortar layer, causing the decorative tiles to fall off. To the role of waterproof, while seriously affecting the safety of buildings and personal
[0007] To sum up, at present, the disadvantages of ordinary rigid tile adhesive bonding materials in the field of architectural decoration and building adhesive materials are: ① only used as an adhesive material between tiles and wall plastering layers, with only bonding performance and single function; ②The tile bonding material does not have the function of waterproof and impermeability. After being soaked by rain or humid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof ceramic tile adhesive material
  • Waterproof ceramic tile adhesive material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Example 1 - in parts by weight, 40 parts of cement, 40 parts of graded aggregate, 1 part of mineral filling permeable material, 0.5 part of water retention agent, 0.1 part of defoaming agent, 0.1 part of anti-sag agent, water repellent 0.1 part of superplasticizer, 0.5 part of superplasticizer, 2 parts of dispersible polymer powder, 0.1 part of anti-cracking fiber, 0.1 part of anti-pan-alkali agent, 0.1 part of thixotropic lubricant, 3 parts of swelling agent, 0.1 part of early strength agent 0.01 part of coagulant is mixed evenly, the mass ratio of the above mixture and water is 1:0.2, and then the above materials and water are stirred, and the stirring is uniform without caking. The prepared slurry is placed for about 5 minutes, and then mixed with a mixer. Evenly can be constructed.

Embodiment 2

[0042] Example 2——In parts by weight, 60 parts of cement, 50 parts of graded aggregate, 10 parts of mineral filling permeable material, 3 parts of water retention agent, 1 part of defoaming agent, 0.5 part of anti-sag agent, water repellent 1 part of superplasticizer, 2 parts of superplasticizer, 5 parts of redispersible latex powder, 1 part of anti-cracking fiber, 2 parts of anti-pan-alkali agent, 0.5 part of thixotropic lubricant, 5 parts of swelling agent, 0.3 part of early strength agent 0.05 part of the coagulant is mixed evenly, the mass ratio of the above mixture and water is 1:0.3, and then the above materials and water are stirred, and the stirring is uniform without agglomeration. Evenly can be constructed.

Embodiment 3

[0043] Example 3—in parts by weight, 50 parts of cement, 45 parts of graded aggregate, 3 parts of mineral filling permeable material, 1 part of water retention agent, 0.5 part of defoaming agent, 0.2 part of anti-sag agent, water repellent 0.5 parts of superplasticizer, 1.5 parts of superplasticizer, 3.5 parts of dispersible polymer powder, 0.6 parts of anti-cracking fiber, 1 part of anti-pan-alkali agent, 0.2 part of thixotropic lubricant, 3.5 parts of swelling agent, 0.2 part of early strength agent 0.04 part of the coagulant is mixed evenly, the mass ratio of the above mixture to water is 1:0.2.5 for configuration, then the above materials and water are stirred, stirred evenly without caking, the prepared slurry is placed for about 5 minutes, and then stirred Mix well to construct.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a waterproof ceramic tile adhesive material which is prepared from the following components in parts by weight: 40-60 parts of cement, 40-50 parts of grading aggregate, 1-10 parts of mineral filling permeable material, 0.5-3 parts of water retaining agent, 0.1-1 part of antifoaming agent, 0.1-0.5 part of anti-sagging agent, 0.1-1 part of water repellent, 0.5-2 parts of superplasticizer, 2-5 parts of re-dispersible latex powder, 0.1-1 part of anti-cracking fiber, 0.1-2 parts of anti-saltpetering agent, 0.1-0.5 part of thixotropic lubricant, 3-5 parts of expanding agent, 0.1-0.3 part of early strength agent and 0.01-0.05 part of retarder. The waterproof ceramic tile adhesive material disclosed by the invention can be used for pasting ceramic tiles, realizes a waterproof anti-permeation function with low shrinkage and high compaction, has the characteristics of high bonding strength and strong environmental adaptability, and provides a guarantee to the building and personal safety.

Description

technical field [0001] The invention relates to the field of building materials, in particular to the design of a waterproof tile adhesive material. Background technique [0002] At present, the tile bonding materials used for bonding tiles in the home decoration and building interior and exterior decoration markets are mainly cement-based materials, which are in the form of powder. When using on-site, the tile adhesive powder is mixed with water and directly smeared on the back of the tile, and then the tile is pressed and kneaded on the wall plastering mortar layer. This material is only used as an adhesive material between the tile and the plastering layer of the wall, but cannot protect the waterproof function of the base wall. [0003] In order to avoid the erosion of water on the wall, there are usually two methods: [0004] The first is to bond the tiles on the ordinary plastering layer of the wall, and use cement or special caulking material for the joints of the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B22/06C04B22/08C04B24/26C04B111/27
Inventor 辉宝琨卢文书
Owner 广东龙马新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.