Preparation method of high-strength non-fading imitation wood plank

A high-strength, imitation wood technology, applied in the field of preparation of building decoration materials, can solve the problems of physical strength, simulated life cycle, poor weather resistance, unsustainable impact effect, high material bonding strength, etc., to broaden the scope of use , long service life, high material bonding strength

Active Publication Date: 2014-03-26
广东崀玉新材料科技股份有限公司
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this invention is to solve the problem of poor physical strength, simulation degree, service life and weather resistance of "wood effect" products currently on the market. Insufficient of high cost, a preparation method of high-strength and non-fading wood-like board is provided. In the preparation method of wood-like board, the structural layer of the wood-like board is made of high-performance filled concrete, the finished product has high structural strength, and the surface layer is made of cement-based polymer. The modified color paste has a high degree of simulation, and the finished product is made through an integrated forming method. The material bonding strength is high, the finished product will not be delaminated, peeled off, and has good weather resistance. The obtained decorative material has excellent comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-strength non-fading imitation wood plank
  • Preparation method of high-strength non-fading imitation wood plank
  • Preparation method of high-strength non-fading imitation wood plank

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The production process of a high-strength non-fading imitation wood board of the present invention includes a mold preparation stage, a base material production stage, and an integrated forming stage;

[0035] The mold preparation stage adopts the following process steps:

[0036] a. Select silicone rubber with strong replication ability, good alkali resistance and high tensile strength as the molding material. The performance parameters of the silicone rubber are selected with a viscosity of 39000mPa·s, a hardness of Shore 33, and an elongation of 450%. ;

[0037] b. Select the wood with the required texture as the matrix of the mould, and the wood requires no repeated texture within 3 square meters;

[0038] c. Using the above-mentioned silicone rubber as a raw material, cooperate with the above-mentioned wood as the mold matrix to make a mold.

[0039] In particular, the silicone rubber stirring, pouring and forming maintenance in the above step c requires a space ...

Embodiment 2

[0056] The production process of a high-strength non-fading imitation wood board of the present invention includes a mold preparation stage, a base material production stage, and an integrated forming stage;

[0057] The mold preparation stage adopts the following process steps:

[0058] a. Select silicone rubber with strong replication ability, good alkali resistance and high tensile strength as the molding material. The performance parameters of the silicone rubber are selected with a viscosity of 40000mPa·s, a hardness of Shore 30, and an elongation of 400%. ;

[0059] B, select the wood of required texture as the parent body of mould, described wood does not appear repeated texture within 5 square meters;

[0060] c. Using the above-mentioned silicone rubber as a raw material, cooperate with the above-mentioned wood as the mold matrix to make a mold.

[0061] In particular, the stirring, pouring, and forming maintenance of the silicone rubber in the above step c requires...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a high-strength non-fading imitation wood plank. The preparation method comprises a mold preparation stage, a substrate manufacturing stage and an integrally forming stage, wherein the substrate manufacturing stage comprises the steps as follows: manufacturing of a surface coloring layer substrate: cement used for manufacturing the surface coloring layer substrate is taken as a cementing material, an iron oxide pigment, an acrylic emulsion and hard calcium are combined, cement-based polymer modified color paste is prepared, and all component materials are required to be mixed and stirred uniformly into dilute paste; and manufacturing of a structure packing layer substrate: the structure packing layer takes cement as a cementing material, river sand, macadam, a superplasticizer, cellulose, an iron oxide pigment, an acrylic emulsion and hard calcium are combined, all component materials of the structure packing layer substrate are required to be mixed and stirred uniformly, and high-performance filling concrete is prepared. An imitation wood plank finished product prepared with the preparation method of the imitation wood plank is high in strength and imitation degree and good in weather resistance, the finished product cannot layer or strip, and the performance of an obtained material is excellent.

Description

Technical field [0001] The present invention involves a preparation method for building decorative materials, especially a preparation method for high -intensity and non -fading imitation wood plate. Background technique [0002] As a natural architectural decorative material, wood is almost synchronized with the development of human civilization. From the traditional building of houses, making wooden products and furniture, to various kinds of wooden products, and wooden crafts, etc., the use method is used.The fineness of use and the scope of use have been made in endless breakthroughs. [0003] In today's era, with the rapid development of technology and economy, the use of wood is increasing. Due to the continuous mining and the growth cycle required by the wood itself, the world forest resources are trending in a shortage. In additionThe indiscriminate and waste of the wood resources have become the shortage of wood resources. At the same time, forest resources are human wea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B13/00
Inventor 王忠平
Owner 广东崀玉新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com