High-strength colorfast faux-wooden plate material
A high-strength, imitation wood technology, applied in the field of imitation wood panels, can solve the problems of high maintenance cost, simulation degree, poor weather resistance during service life, and unsustainable effect, so as to save costs, broaden the scope of use, and overcome the problems of wood The effect of short service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0041] A high-strength non-fading wood-like board of the present invention comprises a surface coloring layer and a structural filling layer, the surface coloring layer adopts cement-based polymer modified color paste, and the structural filling layer adopts high-performance filling concrete;
[0042] The cement-based polymer modified color paste is prepared from the following components:
[0043] 45 parts by weight of cement,
[0044] 20 parts by weight of hard calcium,
[0045] Iron oxide pigment 5 parts by weight,
[0046] 12 parts by weight of acrylic emulsion,
[0047] 18 parts by weight of water;
[0048] The high-performance filled concrete is made from the following components:
[0049] 25 parts by weight of cement,
[0050] 25 parts by weight of river sand,
[0051] Crushed stone 40 parts by weight,
[0052] 1 part by weight of superplasticizer,
[0053] 1 part by weight of cellulose,
[0054] Iron oxide pigment 8 parts by weight.
[0055] The size of the gr...
Embodiment 2
[0057] A high-strength non-fading wood-like board of the present invention comprises a surface coloring layer and a structural filling layer, the surface coloring layer adopts cement-based polymer modified color paste, and the structural filling layer adopts high-performance filling concrete;
[0058] The cement-based polymer modified color paste is prepared from the following components:
[0059]50 parts by weight of cement,
[0060] 15 parts by weight of hard calcium,
[0061] Iron oxide pigment 8 parts by weight,
[0062] 13 parts by weight of acrylic emulsion,
[0063] 14 parts by weight of water;
[0064] The high-performance filled concrete is made from the following components:
[0065] 24 parts by weight of cement,
[0066] 24 parts by weight of river sand,
[0067] Crushed stone 45 parts by weight,
[0068] 0.8 parts by weight of superplasticizer,
[0069] 0.8 parts by weight of cellulose,
[0070] Iron oxide pigment 6.4 parts by weight.
[0071] The size of...
PUM
Property | Measurement | Unit |
---|---|---|
size | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com