Anti-scratch and weather-resistant polyurethane pu glossy black finish

A polyurethane and black topcoat technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems such as loss of gloss, poor hardness, and discoloration, and achieve the effects of overcoming poor hardness, high flexibility, and high scratch resistance

Active Publication Date: 2016-05-25
SHANGHAI BADES CHEM NEW MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current polyurethane bright black topcoat usually uses short-oil alkyd resin, ordinary carbon black and other materials, and the main agent is prepared by high-speed dispersion method. Under the baking environment, the paint film is formed by cross-linking. Because of the poor hardness of materials such as short-oil alkyd resin, ordinary carbon black, and ordinary TDI-TMP adducts, the furniture is easy to be scratched due to scratches during use. There are traces on the surface of the film. At the same time, due to the poor weather resistance of the materials used, it is easy to cause loss of light, discoloration, and darkening, which reduces the beautification and decoration effect of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Component A

[0043] .

[0044] The preparation process of the A component is as follows: in a clean and standard container, add 20kg of 10% 6# carbon black batter, 55kg of acrylic resin, 15kg of 60% aldehyde and ketone resin solution, and 2kg of xylene, start the disperser, Disperse uniformly under medium-speed stirring at 800~1000r / min, add defoamer BYK-1410.3kg, leveling agent EFKA-37770.3kg, leveling agent BYK-3330.1kg, propylene glycol methyl ether acetate 4kg, n-butyl acetate 3.3kg, stir and disperse at a medium speed of 800~1000r / min for 10~15min, and the viscosity is 3500mpa.s / 25℃.

[0045] component B

[0046] .

[0047] The preparation process of the B component is as follows: in a clean container, add 26 kg of dehydrated n-butyl acetate and 5 kg of dehydrated xylene in turn, start the disperser, stir evenly at a medium speed of 500 to 800 r / min, and add TDI Adduct curing agent DesmodurL-7544kg, TDI trimer curing agent DesmodurIL145125kg, stir at a med...

Embodiment 2

[0053] Prepare the raw materials as listed in Table 1, and prepare the three components A, B and C respectively by the same preparation method as in Example 1.

[0054] How to use: When using, mix the three components A, B, and C evenly at a weight ratio of 1:1:0.8, and carry out construction by spraying, brushing, and curtain coating. The C component does not participate in the chemical reaction, only Play the role of thinning construction.

[0055] Table 1:

[0056] .

Embodiment 3

[0058] Prepare the raw materials as listed in Table 2, and prepare the three components A, B and C respectively by the same preparation method as in Example 1.

[0059] How to use: When using, mix the three components A, B, and C evenly in a weight ratio of 1:0.8:0.8, and use spraying, brushing, and curtain coating for construction. The C component does not participate in chemical reactions, only Play the role of thinning construction.

[0060] Table 2:

[0061] .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to a scratch-resistant and weather-resistant polyurethane (PU) bright black finishing coat, which is mainly prepared from three components A, B and C according to the weight ratio 1:(0.8-1):(0.6-0.8) in a mixing manner. Aiming at the technical defects that the product in the prior art is poor in hardness, poor in scratch resistance and poor in weather fastness in the application process, the materials with excellent weatherability, such as acrylic resin and 6# carbon material are adopted to react with a toluene diisocyanate (TDI) trimer curing agent with high hardness, high flexibility and high scratch resistance, so that the product has the characteristics of being high in weatherability, high in hardness, high in flexibility, high in scratch resistance and the like. Thus, the defects of poor hardness and poor scratch resistance easily generated in the product, and fading, discoloring, shading and the like of a film along with time lapse are overcome.

Description

technical field [0001] The invention relates to a polyurethane PU bright black topcoat with scratch resistance and weather resistance, belonging to the woodware coating industry. Background technique [0002] In the decoration and protection of materials, the polyurethane bright black topcoat presents a mirror-like decorative effect with a full paint film and a smooth surface. It is widely used in the coating of high-end furniture and is deeply loved by people. The decorative protection effect of polyurethane bright black topcoat mainly depends on the hiding power, fullness, gloss and hardness of its product film, and also needs to take into account adhesion, flexibility, weather resistance, wear resistance, chemical resistance, protection. Consideration of comprehensive properties such as light color retention. [0003] The current polyurethane bright black topcoat usually uses materials such as short oil alkyd resin and ordinary carbon black. Crosslinking to form a paint...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D7/12
Inventor 方学平赖晓宗刘欢
Owner SHANGHAI BADES CHEM NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com