A technology of red bed mudstone and main raw materials, which is applied in the field of inorganic non-metallic materials (ceramics), can solve the problems such as no research reports on ceramic materials, and achieve the effects of high yield, pure color and low cost

Inactive Publication Date: 2015-04-08
JINGDEZHEN CERAMIC INSTITUTE
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many studies involving red bed mudstone in rock mechanics, engineering mechanics, highways, hydropower and other engineering, but there is no research report on its use as a ceramic material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic ferrosilicon red material prepared with red-bed mudstones as main raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Formula: 96.2% red bed mudstone, 3.8% iron oxide, plus 3% borax as a mineralizer

[0019] (1) Coarsely crush the red bed mudstone and pass through a 180-mesh sieve;

[0020] (2) Weigh the ingredients according to the formula, mix them evenly by dry method, and pass through a 180-mesh sieve;

[0021] (3) The ball is a zirconia ball with a diameter of 5 mm, the mass ratio of the ball to material is 20:1, the speed of the ball mill is 300 rpm, and the ball is dry-milled with a high-energy ball mill for 10 hours;

[0022] (4) Take out the powder obtained in (3), put it into a corundum crucible, and put it into an electric furnace for roasting. The initial temperature is room temperature, and the temperature is raised to 1150°C in 6 hours, kept for 2 hours, and cooled naturally to obtain a powdered color product.

Embodiment 2

[0024] Formula: 96.2% red bed mudstone, 3.8% iron oxide, plus 3% boric acid as a mineralizer

[0025] (1) Coarsely crush the red bed mudstone and pass through a 180-mesh sieve;

[0026] (2) Weigh the ingredients according to the formula, mix them evenly by dry method, and pass through a 180-mesh sieve;

[0027] (3) The ball is a zirconia ball with a diameter of 3 mm, the mass ratio of the ball to material is 30:1, the speed of the ball mill is 400 rpm, and the ball is dry-milled with a high-energy ball mill for 20 hours;

[0028] (4) Take out the powder obtained in (3), put it into a corundum crucible, and put it into an electric furnace for roasting. The initial temperature is room temperature, and the temperature is raised to 1150°C in 6 hours, kept for 2 hours, and cooled naturally to obtain a powdered color product.

Embodiment 3

[0030] Formula: 96.2% red bed mudstone, 3.8% iron oxide, plus 3% NaF as mineralizer

[0031] (1) Coarsely crush the red bed mudstone and pass through a 180-mesh sieve;

[0032] (2) Weigh the ingredients according to the formula, mix them evenly by dry method, and pass through a 180-mesh sieve;

[0033] (3) The ball is a zirconia ball with a diameter of 1 mm, the mass ratio of the ball to material is 40:1, the speed of the ball mill is 450 rpm, and the ball is dry-milled with a high-energy ball mill for 30 hours;

[0034] (4) Take out the powder obtained in (3), put it into a corundum crucible, and put it into an electric furnace for roasting. The initial temperature is room temperature, and the temperature is raised to 1150°C in 6 hours, kept for 2 hours, and naturally cooled to obtain a powdered color product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a ceramic ferrosilicon red material prepared with red-bed mudstones as a main raw material. The ceramic ferrosilicon red material is prepared by the following steps: with red-bed mudstones and ferric oxide as raw materials, adding a mineralizer, and carrying out coarse crushing, burdening, mixing, sieving, mechanochemistry ball milling and roasting to obtain a product. By adopting the preparation method of the ceramic ferrosilicon red material, with cheap red-bed mudstones as the main raw material, only a small quantity of Fe2O3 chemical material needs to be added, and the ceramic ferrosilicon red material with good color generation is prepared by combining a mechanochemistry method; and compared with the traditional preparation method of a ferrosilicon red material, the preparation method of the ceramic ferrosilicon red material has the advantages of simpleness in process, no pollution to the environment, high yield, little energy consumption, lower cost, pure color development and the like and has a wide market prospect.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a ceramic ferrosilicon red material prepared from red bed mudstone as a main raw material. Background technique [0002] Ferrosilicon red material is a ceramic-wrapped color material that can present a bright desert red tone in the green body and is resistant to high temperatures. Its main chemical composition is SiO 2 It acts as a carrier in the color material, similar to ZrSiO in zirconium iron red material 4 The role of crystals. It is SiO 2 As the wrapping phase, SiO is used 2 Microcrystalline phase and SiO 2 Glass relative colorant Fe 2 o 3 Wrapped so as to play a role in high temperature stability. while Fe 2 o 3 As a colorant, it is the main component of the coloring of the pigment. The main components of natural ferrosilicon red material are silicon and iron, and also contain a small amount of aluminum. Its coloring mechani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/85
Inventor 卢希龙曹春娥
Owner JINGDEZHEN CERAMIC INSTITUTE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap