Ultraviolet light polymerization water-based paint universal for metal and non-metal and preparation method thereof

A water-based coating, non-metallic technology, applied in the direction of polyester coating, polyurea/polyurethane coating, coating, etc., can solve the problems of poor stability, long curing time, etc. Short, well-stabilized effects

Inactive Publication Date: 2014-04-30
SUZHOU CITY BANGCHENG ELECTRICITY TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] UV-curable coatings have attracted more and more attention because of their good environmental protection, but traditional photo-curable coatings generally cannot avoid the use of organic volatiles that are irritating to the human body, so the existing UV-curable coatings have used water To replace irritating organic diluents, UV-curable water-based coatings have attracted the attention of researchers, but the existing UV-curable coatings still have the disadvantages of long curing time and poor stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Metal and non-metal universal UV-curable water-based coatings, including the following raw materials in parts by mass: 60 parts of vinyl ester resin, 38 parts of polyurethane acrylate, 1 part of 2-hydroxy-2-methyl-1-phenylacetone, 0.5 part of isooctyl dithioglycolate, 0.5 part of di-n-octyltin, 35 parts of ethanol, and 150 parts of water.

[0014] The preparation method of this example: according to the mass ratio, mix and stir vinyl ester resin and polyurethane acrylate evenly, add 2-hydroxy-2-methyl-1-phenylacetone and isooctyl di-n-octyltin dimercaptoacetate to mix Evenly, add the mixed solution of ethanol and water dropwise, the dropping speed is controlled at 2mL / min, and stir evenly after the dropping, to obtain a general-purpose UV-curable water-based paint for metals and non-metals.

[0015] The finished product was tested for performance, and the test results are shown in Table 1.

Embodiment 2

[0017] Metal and non-metal universal UV-curable water-based coatings, including the following raw materials in parts by mass: 70 parts of vinyl ester resin, 46 parts of polyurethane acrylate, 2 parts of 2-hydroxy-2-methyl-1-phenylacetone, 1 part of isooctyl dithioglycolate, 1 part of di-n-octyltin, 40 parts of ethanol, and 180 parts of water.

[0018] The preparation method of this embodiment is the same as that of Example 1, and the performance of the finished product is tested, and the test results are shown in Table 1.

Embodiment 3

[0020] Metal and non-metal universal UV-curable water-based coatings, including the following raw materials in parts by mass: 65 parts of vinyl ester resin, 40 parts of polyurethane acrylate, 1.5 parts of 2-hydroxy-2-methyl-1-phenylacetone, 0.7 parts of isooctyl di-n-octyltin dimercaptoacetate, 37 parts of ethanol, and 160 parts of water.

[0021] The preparation method of this embodiment is the same as that of Example 1, and the performance of the finished product is tested, and the test results are shown in Table 1.

[0022] The finished product prepared by embodiment 1-3 is carried out performance test, and the results are shown in Table 1:

[0023] Table 1 Performance test data

[0024] performance Example 1 Example 2 Example 3 Curing time, min 3 2 3 Adhesion (circle method), grade 1 1 1

[0025] It can be seen from the above table that the coating of the present invention has good adhesion and short curing time.

[0026] The finished...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses ultraviolet light polymerization water-based paint universal for metal and non-metal and a preparation method of the paint. The ultraviolet light polymerization water-based paint universal for metal and non-metal comprises the following raw materials in parts by mass: 60-70 parts of vinyl ester resin, 38-46 parts of urethane acrylate, 1-2 parts of 2-hydroxy-2-methyl-1-phenylacetone, 0.5-1 part of bimercaptoacetic acid isooctyl di-n-octyltin, 35-40 parts of ethanol and 150-180 parts of water. The paint is short in curing time, that is, the curing time is 3 minutes and the adhesion capability to a substrate is of 1 grade, is good in stability and free of layering after being preserved for 6 months. The paint is simple in preparation method and applicable to popularization and application in a wide range.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a metal and non-metal universal UV-curable water-based coating and a preparation method thereof. Background technique [0002] UV-curable coatings have attracted more and more attention because of their good environmental protection, but traditional photo-curable coatings generally cannot avoid the use of organic volatiles that are irritating to the human body, so the existing UV-curable coatings have used water To replace irritating organic diluents, UV-curable water-based coatings have attracted the attention of researchers, but the existing UV-curable coatings still have the disadvantages of long curing time and poor stability. [0003] To sum up, how to overcome the deficiencies of the prior art has become an urgent problem to be solved in the field of coatings. Contents of the invention [0004] The purpose of the present invention is to overcome the deficiencies of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D175/14C09D7/12
Inventor 陈汉刚
Owner SUZHOU CITY BANGCHENG ELECTRICITY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com