Sand texture type polyester/epoxy powder coating and preparation method thereof

A technology of epoxy powder and polyester, applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of lack of three-dimensional effect, flat surface, poor hand feeling, etc., to improve wettability and affinity, The sand texture is fine and clear, and the effect is evenly distributed

Inactive Publication Date: 2013-06-19
ANHUI HUAHUI SUYE TECH SHARE CO LTD
View PDF8 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface of the powder coating commonly used at present is flat, dull, poor in hand feeling and lacks three-dimensional effect after curing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] A kind of sand grain type polyester / epoxy powder coating, it is made from the raw material of following weight part:

[0045] Polyester resin (P5040) 390 parts

[0046] Epoxy resin (E-12) 260 parts

[0047] Dull barium sulfate 120 parts

[0048] 50 parts of quasi-spherical silica powder

[0049] Modified polyethylene wax powder 10 parts

[0050] 10 parts of organic coated titanium dioxide

[0051] Sand texture agent (SWMBX-30) 10 parts

[0052] Benzoin 5 parts

[0053] 2-phenylimidazoline 6 parts

[0054] 2-methylimidazole 6 parts

[0055] Iron yellow 10 parts

[0056] iron red 10 parts

[0057] Carbon black 10 parts.

[0058] Wherein, the particle size of the quasi-spherical silica powder is 500 mesh.

[0059] The modified polyethylene wax micropowder is prepared by the following method: (1) Add polytetrafluoroethylene micropowder, organic bentonite and tree ash in a high-speed mixer at a mass ratio of 4:1.5:0.6 and mix for 25 minutes, then add 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a sand texture type polyester/epoxy powder coating and a preparation method thereof. The sand texture type polyester/epoxy powder coating comprises the following raw materials, by weight, 350-400 parts of polyester resin (P5040), 240-280 parts of epoxy resin (E-12), 100-150 parts of extinction barium sulfate, 40-60 parts of spherical silica powder, 8-12 parts of modified polyethylene wax powder, 10-15 parts of organic coated titanium dioxide, 5-10 parts of sand texture agent (SWMBX-30), 4-6 parts of benzoin, 5-8 parts of 2-phenyl imidazoline, 4-6 parts of 2-methylimidazole, 5-10 parts of ferrite yellow, 5-10 parts of iron oxide red and 10-15 parts of carbon black. The prepared powder coating has the advantages of being high in hardness, high in intensity, high in abrasion resistance, good in heat resistance, good in ageing resistance, short in solidifying time, environment-friendly, free of pollution and the like. The solidified coating produces a texture effect of the sand texture, the sand texture is meticulous and clear, distribution is even, visual comfort is provided for people, and combination properties of the coating are good.

Description

technical field [0001] The invention relates to a powder coating, in particular to a sand grain type polyester / epoxy powder coating and a preparation method thereof. Background technique [0002] As an environmentally friendly coating, powder coating has the advantages of no solvent, low pollution, simple coating process and high coating efficiency. The surface of the powder coating commonly used at present is flat, dull, poor in hand feeling and lacks three-dimensional effect after curing. With the rapid development of the powder coating industry, people are no longer satisfied with the monotonous gloss or color-changing decoration of various home appliances and equipment to be coated. The art-type powder coating has a beautiful and clear appearance on the surface of the coating film. Patterns, to give the coated device a beautiful and colorful appearance, or to cover up the defects on the surface of the coated object by its texture effect, so as to improve the decorativen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D163/00C09D123/06C09D7/12C09D5/03C09D5/28
Inventor 刘荣兴费邦忠
Owner ANHUI HUAHUI SUYE TECH SHARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap