Wood plastic composite material cladding plywood formwork and manufacturing method thereof

A wood-plastic composite and plywood technology, which is applied in the direction of wood layered products, formwork/formwork components, chemical instruments and methods, etc., can solve the problems of low strength and poor durability, and achieve strong acid resistance, heat deformation, and smooth surface smooth effect

Active Publication Date: 2014-04-30
NORTHEAST FORESTRY UNIVERSITY
View PDF6 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problems of low strength and poor durability of the wooden plywood formwork prepared in the prior art, and provides a wood-plastic composite clad plywood formwork and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wood plastic composite material cladding plywood formwork and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0032] Embodiment 1: In this embodiment, a wood-plastic composite cladding plywood template is prepared from wood-plastic thin boards, modified non-woven fabrics and core plywood.

[0033] The surface of the wood-plastic composite clad plywood template prepared in this embodiment is flat and smooth, inert, easy and quick to demould, and has a small error in the flatness of the board surface. It has good water resistance, no delamination after long-term immersion in water, and good dimensional stability of the board. With the protection of wood-plastic veneer, the core plywood is not easy to absorb moisture and deform or swell. It solves the bonding problem between the large-format polar wood surface and the non-polar plastic surface. There is no water vapor generated during hot pressing, and hot pressing defects such as delamination and bubbling will not be caused; the wood is grafted by coupling agent The bonding strength of plywood and polyolefin is greatly improved; it can...

specific Embodiment approach 2

[0036] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the wood-plastic thin board is prepared according to the following steps:

[0037] 1. Raw material preparation: Weigh 30-100 parts of thermoplastic, 20-200 parts of plant fiber powder, 20-100 parts of inorganic filler, 3-10 parts of coupling agent, 1-4 parts of lubricant, 1 ~4 parts of masterbatch and 3~10 parts of other fillers;

[0038] 2. Blending and granulation: Put the thermoplastics, plant fiber powder, inorganic fillers, coupling agents, lubricants, masterbatches and other fillers weighed in step 1 into a high-speed mixer, and control the temperature at 25 ° C ~ Mix at 150°C for 5min to 20min, then cool to room temperature to obtain a premix, then put the premix into a twin-screw granulator, control the temperature to 145°C to 235°C, and the speed to 30r / min to 100r / min , carry out granulation to obtain wood-plastic granules, and perform molding processing on the wood-plastic granules...

specific Embodiment approach 3

[0046] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that the modified non-woven fabric is prepared by adding grafting monomers and initiators into an organic solvent to prepare a mixed solution, and then the mixed solution Spray evenly on the non-woven fabric, and then place it in an oven at a temperature of 50°C to 100°C to dry for 10 minutes to 30 minutes to obtain a modified nonwoven fabric;

[0047] The non-woven fabric is one of polypropylene, polyethylene, polyvinyl chloride and polystyrene or a mixture of several of them, and when it is a mixture, it is mixed in any ratio;

[0048] Described grafting monomer is maleic acid, maleic anhydride, methyl methacrylate, acrylic acid, glycidyl methacrylate, ethyl acrylate or styrene monomers;

[0049] Described initiator is dicumyl peroxide, benzoyl peroxide, tert-butyl benzoyl peroxide or di-tert-butane peroxide;

[0050] Described organic solvent is toluene, xylene, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a plywood formwork and a manufacturing method of the plywood formwork, in particular to a wood plastic composite material cladding plywood formwork and a manufacturing method of the wood plastic composite material cladding plywood formwork. The wood plastic composite material cladding plywood formwork aims to solves the problems that a wood plywood formwork manufactured in the prior art is low in intensity and poor in durability. The wood plastic composite material cladding plywood formwork is formed by a wood plastic sheet, an improved non-woven fabric and core-layer plywood in a manufactured mode. The manufacturing method comprises the steps that the wood plastic sheet is manufactured; the non-woven fabric is improved; the core-layer plywood is manufactured; pavement is carried out; the formwork is formed. The wood plastic composite material cladding plywood formwork is low in manufacturing cost, high in intensity, good in toughness, long in service life, resistant to moisture and corrosion, stainless, bright, clean and flat in surface, light in weight, and convenient to transport and construct, a die does not swell easily, and the die is released easily. The wood plastic composite material cladding plywood formwork is used as a building formwork.

Description

technical field [0001] The invention relates to a plywood template and a preparation method thereof. Background technique [0002] Building formwork is an indispensable tool in concrete pouring projects. In current concrete pouring projects, formwork engineering generally accounts for 20% to 30% of the cost of concrete structure projects, 30% to 40% of engineering labor, and 50% of the construction period. %, formwork technology directly affects the quality, cost and benefit of the project. It is an important aspect to promote the progress of construction technology in our country. [0003] At present, there are two main types of concrete formwork in the domestic market, steel formwork and plywood formwork. The steel formwork is heavy, inconvenient to use, easy to rust, and easy to bond with concrete, which brings inconvenience to construction and affects project quality. . There are two main types of plywood formwork: bamboo plywood formwork and wood plywood formwork. B...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04G9/05B32B27/18B32B27/12B32B21/10C08L97/02C08L23/06C08L23/12C08L27/06C08L25/06C08L77/00D06M14/10
Inventor 王伟宏黄浪郭丽敏王海刚王清文
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap