Thermoplastic acrylic resin plastic paint

A technology of thermoplastic acrylic and plastic paint, which is applied in the field of plastic paint of thermoplastic acrylic resin, which can solve the problems of inconvenient construction and rapid gelling, and achieve good adhesion and good thermoplastic performance

Inactive Publication Date: 2014-05-07
NANJING HENGAN RESIN CHEM
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Unsaturated polyester paint is a commonly used paint. Its main disadvantage is that the two components will gel quickly after being mixed. big inconvenience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1 : A kind of plastic paint of thermoplastic acrylic resin, its raw material contains the component of following parts by weight: thermoplastic acrylic resin: 100 parts; Titanium dioxide: 5 parts; Light calcium carbonate: 50 parts; Polyfluorinated polyolefin: 1- 3 parts; dispersant: 1-3 parts; IPDI curing agent: 1.5 parts;

[0019] Wherein, the parts by weight of the thermoplastic acrylic resin component are: a mixture of methyl methacrylate and cyclohexyl methacrylate at a ratio of 1:3: 100 parts; methacrylic acid: 15-25 parts; styrene: 25-30 parts; dibenzoyl peroxide: 25-30 parts; dibenzoyl peroxide, azobisisobutylcyanide or tert-butyl peroxybenzoate: 3-5 parts; triphenylphosphine: 0.5 -1.5 parts; solvent mixed with polyvinyl alcohol and water in a ratio of 1:35-50: 35-50 parts.

[0020] The preparation method of the plastic paint of above-mentioned thermoplastic acrylic resin, carries out as follows:

[0021] (1) Prepare thermoplastic acrylic resin in part...

Embodiment 2

[0024] Example 2 : a plastic paint of thermoplastic acrylic resin, its raw material contains the following components in parts by weight: thermoplastic acrylic resin: 100 parts; iron oxide red: 6 parts; talcum powder: 55 parts; polyfluorinated polyolefins: 1-3 parts; dispersant: 1-3 parts; IPDI curing agent: 1.5 parts;

[0025] Wherein, the parts by weight of the thermoplastic acrylic resin component are: a mixture of methyl methacrylate and cyclohexyl methacrylate at a ratio of 1:3: 100 parts; methacrylic acid: 15-25 parts; styrene: 25-30 parts; dibenzoyl peroxide: 25-30 parts; dibenzoyl peroxide, azobisisobutylcyanide or tert-butyl peroxybenzoate: 3-5 parts; triphenylphosphine: 0.5 -1.5 parts; solvent mixed with polyvinyl alcohol and water in a ratio of 1:35-50: 35-50 parts.

[0026] A kind of preparation method of the plastic paint of thermoplastic acrylic resin, carries out as follows:

[0027] (1) Prepare thermoplastic acrylic resin in parts by weight of the following...

Embodiment 3

[0030] Example 3 : A plastic paint of thermoplastic acrylic resin, its raw material contains the following components in parts by weight: thermoplastic acrylic resin: 100 parts; carbon black: 6.5 parts; mica powder: 62 parts; polyfluorinated polyolefins: 1-3 parts ; Dispersant: 1-3 parts; IPDI curing agent: 1.5 parts;

[0031] Wherein, the parts by weight of the thermoplastic acrylic resin component are: a mixture of methyl methacrylate and cyclohexyl methacrylate at a ratio of 1:3: 100 parts; methacrylic acid: 15-25 parts; styrene: 25-30 parts; dibenzoyl peroxide: 25-30 parts; dibenzoyl peroxide, azobisisobutylcyanide or tert-butyl peroxybenzoate: 3-5 parts; triphenylphosphine: 0.5 -1.5 parts; solvent mixed with polyvinyl alcohol and water in a ratio of 1:35-50: 35-50 parts.

[0032] A kind of preparation method of the plastic paint of thermoplastic acrylic resin, carries out as follows:

[0033] (1) Prepare thermoplastic acrylic resin in parts by weight of the following ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a thermoplastic acrylic resin plastic paint. Raw materials of the thermoplastic acrylic resin plastic paint comprise, by weight, 100 parts of a thermoplastic acrylic resin, 5-8 parts of a pigment, 50-70 parts of a filler, 1-3 parts of a flatting agent, 1-3 parts of a dispersant and 1.5 parts of a curing agent, wherein the thermoplastic acrylic resin comprises, by weight, 100 parts of a mixture obtained by mixing methyl methacrylate and cyclohexyl methacrylate according to a ratio of 1:3, 15-25 parts of methacrylic acid, 25-30 parts of styrene, 25-30 parts of dibenzoyl peroxide, 3-5 parts of dibenzoyl peroxide, azobisisbutyronitrile or tert-butyl peroxybenzoate, 0.5-1.5 parts of triphenylphosphine and 35-50 parts of a mixed solvent obtained by mixing polyvinyl alcohol and water according to a ratio of 1:35-50. A coating prepared by using the thermoplastic acrylic resin plastic paint can be applied by diluting with an organic solvent, can also be applied by hot melting, and has good adhesive force to surfaces of cement, asphalt and plastics.

Description

technical field [0001] The invention relates to a plastic paint of acrylic resin, in particular to a plastic paint of thermoplastic acrylic resin. Background technique [0002] Unsaturated polyester paint is a commonly used paint. Its main disadvantage is that the two components will gel quickly after being mixed. Big inconvenience. Contents of the invention [0003] Purpose of the invention: in order to overcome the deficiencies in the prior art, the purpose of the present invention is to provide a thermoplastic acrylic resin plastic paint with strong adhesion, wear resistance and flexibility. [0004] Technical solution: In order to solve the above object, the technical solution adopted in the present invention is: a plastic paint of thermoplastic acrylic resin, the raw material of which contains the following components in parts by weight: [0005] Thermoplastic acrylic resin: 100 parts; [0006] Pigment: 5-8 parts; [0007] Filler: 50-70 parts; [0008] Leveling a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/10C08F220/18C08F220/14C08F220/06C08F212/08
Inventor 马步强
Owner NANJING HENGAN RESIN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com