Asphalt phenolic waterproof material

A waterproof material and phenolic technology, used in building thermal insulation materials, building components, buildings, etc., can solve the problems of poor anti-corrosion performance and long drying time, and achieve the effects of good weather resistance, good waterproof performance, and good crack resistance.

Inactive Publication Date: 2014-05-14
NANTONG SOUTHEAST HIGHWAY ENG
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] This application aims at the technical problems of existing asphalt phenolic waterproof materials such as

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1:

[0013] A kind of asphalt phenolic waterproof material, the composition of which is expressed in parts by mass: 100 parts of petroleum pitch; 10 parts of pine tar; 15 parts of glycerin rosin ester; 1 part of calcium chloride; 12 parts of rosin modified phenolic resin; iron oxide 20 parts of yellow; 40 parts of solvent gasoline; 10 parts of aluminum-silver paste; 30 parts of benzene; 6 parts of silica; 8 parts of xylene; 1 part of butanol; 2 parts of ethylene diamine. Put the pitch into a reaction kettle and heat to 150 degrees Celsius to dissolve, add the remaining components at 160 degrees Celsius, and stir for 1 hour to obtain the product.

[0014] Product surface dry for 3.2h, hard-dry for 22h; resistant to low temperature of -50℃, no foaming and no flow at 100℃ for 4h; water impermeability 0.1MPa.

Example Embodiment

[0015] Example 2:

[0016] A kind of asphalt phenolic waterproof material, its composition is expressed in parts by mass: 100 parts of petroleum pitch; 25 parts of pine tar; 20 parts of glycerin rosin ester; 2 parts of calcium chloride; 18 parts of rosin modified phenolic resin; iron oxide 30 parts of yellow; 60 parts of solvent gasoline; 18 parts of aluminum silver paste; 40 parts of benzene; 8 parts of silica; 10 parts of xylene; 2 parts of butanol; 3 parts of ethylene diamine. Put the pitch into a reaction kettle and heat to 150 degrees Celsius to dissolve, add the remaining components at 160 degrees Celsius, and stir for 1 hour to obtain the product.

[0017] Product surface dry for 2.5h, hard-dry for 21h; resistance to low temperature of -50℃, no foaming or flow at 110℃ for 4h; impermeability of 0.15MPa.

Example Embodiment

[0018] Example 3:

[0019] A kind of asphalt phenolic waterproof material, its composition is expressed in parts by mass: 100 parts of petroleum pitch; 15 parts of pine tar; 17 parts of glycerin rosin ester; 1.5 parts of calcium chloride; 15 parts of rosin modified phenolic resin; iron oxide 25 parts of yellow; 50 parts of solvent gasoline; 14 parts of aluminum silver paste; 35 parts of benzene; 7 parts of silica; 9 parts of xylene; 1.5 parts of butanol; 2.5 parts of ethylenediamine. Put the pitch into a reaction kettle and heat to 150 degrees Celsius to dissolve, add the remaining components at 160 degrees Celsius, and stir for 1 hour to obtain the product.

[0020] The product is surface-dried for 2.2h, hard-drying for 20h; resistant to low temperature of -50℃, no foaming and no flow at 120℃ for 4h; water impermeability 0.2MPa.

[0021] All the components in the above examples are commercially available.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an asphalt phenolic waterproof material. The asphalt phenolic waterproof material comprises the following components in parts by mass: 100 parts of petroleum asphalt, 10-25 parts of pine tar, 15-20 parts of ester gum, 1-2 parts of calcium chloride, 12-18 parts of rosin modified phenolic resin, 20-30 parts of pigment, 40-60 parts of solvent gasoline, 10-18 parts of aluminium paste, 30-40 parts of benzene, 6-8 parts of silicon dioxide, 8-10 parts of dimethylbenzene, 1-2 parts of butanol and 2-3 parts of ethanediamine; the product is excellent in corrosion resistance and has resistance to microbial corrosion; the time for surface drying is 2.2-3.2 hours; the time for hard dry is 20-22 hours; the asphalt phenolic waterproof material is high-temperature resistant and cold-resistant, has resistance to low temperature of 50 DEG C below zero and is incapable of defoaming and flowing within 4 hours at the temperature of 100-120 DEG C; the asphalt phenolic waterproof material is excellent in waterproof property, impermeable under 0.1-0.2MPa and excellent in anti-cracking property; and the product is high in bending resistance, excellent in weather resistance, high in compressive strength, applicable to extensive production and capable of continuously replacing the current material.

Description

technical field [0001] The application belongs to the field of asphalt waterproof materials, in particular to an asphalt phenolic waterproof material. Background technique [0002] Bitumen is a product of crude oil processing. It is a black or dark brown viscous liquid or solid at room temperature. It mainly contains soluble trichlorethylene hydrocarbon derivatives. Its properties and composition vary with sources and production methods. Variety. Like petroleum, asphalt is a complex organic mixture without fixed chemical composition and physical constants, and many oil minerals form a continuous series in transitional form. This brings many difficulties to classification and identification. Asphalt is a product of crude oil processing. It is a black or dark brown viscous liquid or solid at room temperature. It is a brown-black organic gelatinous substance, including natural asphalt, petroleum asphalt, shale asphalt and coal. Tar pitch and other four. The main components ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L93/04C08L61/14C08K13/02C08K3/16C08K3/36C08K5/17C08K5/05C08K5/01C08K3/08
Inventor 吴志仁蔡永华何平徐宏庆于艳
Owner NANTONG SOUTHEAST HIGHWAY ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap