Toughening agent with chain extension function and application of toughening agent in engineering plastic processing

A toughening agent and functional technology, applied in the field of toughening agent, can solve problems such as poor mechanical properties and difficult processing of recycled PET

Active Publication Date: 2014-05-28
HEFEI UNIV OF TECH
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the above-mentioned prior art, the present invention provides a toughening agent with chain extension function, which can effectively increase the chain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] In a nitrogen environment, 0.6 parts of glycidyl methacrylate, 70 parts of methyl methacrylate, 30 parts of n-butyl acrylate and 0.6 parts of initiator dibenzoyl peroxide are mixed and dissolved in 50 parts of toluene organic solvent. Add dropwise to an organic solution containing 0.6 parts of chain transfer agent n-dodecyl mercaptan and 50 parts of toluene, the dropping time is 2h, the temperature is 60°C, and the speed is 3000rdm. After the dripping is completed, adjust the temperature to 70℃, continue the reaction for 2h, adjust the speed to 5000rdm, the resulting product is washed, filtered and dried in sequence. It is a chain-extended toughening agent with an epoxy value of 4.2×10 -3 mol / 100g.

[0020] 100 parts of rPET (intrinsic viscosity of 0.60dl / g), 50 parts of the above-mentioned chain extension type toughener (epoxy value 4.2×10 -3 mol / 100g), 0.1 part of antioxidant 1024, 0.2 part of antioxidant 168, blended for 5 minutes, and then added to the...

Example Embodiment

[0021] Example 2

[0022] In a nitrogen environment, 1.0 part of glycidyl acrylate, 80 parts of styrene, 20 parts of n-butyl acrylate and 0.3 parts of initiator azobisisobutyronitrile are mixed and dissolved in 50 parts of toluene organic solvent, and added dropwise containing 0.5 In an organic solution of 1 part chain transfer agent n-dodecyl mercaptan and 50 parts toluene, the dropping time is 2.5h, the temperature is 70℃, and the rotation speed is 3000rdm. After the addition is complete, continue the reaction for 2.5 hours, adjust the temperature to 80°C, and adjust the speed to 5000 rdm. The resulting product is washed, filtered and dried in sequence. It is a chain-extended toughening agent with an epoxy value of 7.04×10 -3 mol / 100g.

[0023] 100 parts of rPET (intrinsic viscosity of 0.60dl / g), 40 parts of the above-mentioned chain extension type toughener (epoxy value 7.04×10 -3 mol / 100g), 0.2 part of antioxidant 1024, 0.2 part of antioxidant 168, after blending for 5 minutes...

Example Embodiment

[0024] Example 3

[0025] In a nitrogen environment, 1.5 parts of glycidyl acrylate, 60 parts of styrene, 40 parts of ethyl acrylate and 0.3 parts of initiator azobisisobutyronitrile are mixed and dissolved in 50 parts of toluene organic solvent, and 0.5 parts are added dropwise. The chain transfer agent n-butyl mercaptan, 50 parts of toluene in an organic solution, the dripping time is 2h, the temperature is 70℃, and the rotation speed is 3000rdm. After the addition is complete, continue the reaction for 2 hours, adjust the temperature to 80°C, and adjust the speed to 5000 rdm. The resulting product is washed, filtered and dried in sequence. It is a chain-extending toughening agent with an epoxy value of 1.05×10 -2 mol / 100g.

[0026] 100 parts of rPET (intrinsic viscosity of 0.60dl / g), 15 parts of the above-mentioned chain-extended toughener (epoxy value 1.05×10 -2 mol / 100g), 0.4 parts of antioxidant 1024, 0.4 parts of antioxidant 168, blended for 5 minutes, and then added to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a toughening agent with a chain extension function. Under a nitrogen environment, a total monomer and an initiator are jointly and dropwise added into a chain transfer agent contained organic solvent with the temperature of 50 DEG C-70 DEG C, and the dropwise adding time is 2-3 hours; after dropwise adding is ended, the reaction continues for 2-6 hours, and a product is sequentially washed, filtered and dried; and the toughening agent is prepared through a polymerization reaction of a solvent, and the epoxy value is about 4*10<-3> mol/100g to 5*10 <-2> mol/100g. A preparation process of the toughening agent is simple, the reaction conditions are mild, the activity is moderate, and a good chain extension function is realized; and a final product has good toughness and excellent tensile property. The toughening agent can be used for recovering and processing hydroxyl-terminated and carboxyl-terminated polycondensate such as PET (polyethylene terephthalate), PBT (polybutylene terephthalate) and the like, and chain extension and toughening of a PET recovery material are realized; and at the same time, the production technology process is simplified, and the operation is easy.

Description

technical field [0001] The invention relates to a toughening agent with chain extending function and the application of the toughening agent with chain extending function in recycling and processing of hydroxyl-terminated and carboxyl-terminated condensation polymers of engineering plastics such as PET and PBT. Background technique [0002] Polymethyl terephthalate (PET), polybutylene terephthalate (PBT) and other hydroxyl-terminated carboxyl-terminated condensation polymers are important engineering plastics. Their common feature is that they generally have good mechanical strength, weather resistance and chemical resistance, and are widely used in film materials, outer packaging materials, bottles, castings and other fields. However, this also causes white pollution. In order to protect the environment and save resources, the recycling technology of engineering plastics has received strong attention in the industry, and outstanding progress has been made in this regard. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/14C08F212/08C08F218/08C08F220/18C08F220/32C08F2/38C08L33/12C08L25/14C08L31/04C08L67/02B29B9/06
Inventor 徐卫兵曹渊周正发马海红任凤梅
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap