High-performance polyvinyl chloride composite material for wires and cables and preparation method thereof

A polyvinyl chloride, wire and cable technology, which is applied in the field of high-performance polyvinyl chloride composite materials and its preparation, can solve the problem that the performance defects of polyvinyl chloride materials cannot be well improved, restrict the application of wire and cable insulation sheaths, Improve the processing cost and processing control difficulty to achieve the effect of promoting technological innovation and industry development, improving the small scope of use, and enhancing the bonding force

Inactive Publication Date: 2014-06-11
深圳市领亚电子有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Most manufacturers at home and abroad have improved their equipment and added a mandatory feeding device during the feeding process to improve the uneven dispersion of antimony trioxide flame retardants due to their high specific gravity. Increased processing cost and processing control difficulty
Especially in terms of high environmental protection and flame retardant performance requirements for smoke suppression, the flammability of plasticizers in polyvinyl chloride and the poor mechanical and mechanical properties of inorganic magnesium-aluminum flame retardants restrict the use of polyvinyl chloride materials in high-end products or Application of wire and cable insulation layer sheath in special environment
The wire and cable industry is an industry with a high degree of industrial correlation, and the demand for flame-retardant materials will maintain a high growth rate in the last ten years, but due to the performance defects of PVC materials, it is not well understood. Improvement, the industrialization development at home and abroad is bound to be restricted in the short term

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance polyvinyl chloride composite material for wires and cables and preparation method thereof
  • High-performance polyvinyl chloride composite material for wires and cables and preparation method thereof
  • High-performance polyvinyl chloride composite material for wires and cables and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] see figure 1 , the invention provides a high-performance polyvinyl chloride composite material for wire and cable, which is made of the following raw materials in parts by weight:

[0055]

[0056] The antimony-free environment-friendly flame retardant system is made of the following raw materials in parts by weight:

[0057]

[0058] The polyvinyl chloride resin has a molecular weight of 750-1400, a K value of 55-75, and a degree of polymerization of 750-1400.

[0059] The mineral filler is one of magnesium hydroxide and aluminum hydroxide or a combination thereof; the antioxidant is 2.4 di-tert-butylphenyl-phosphite triester, thiodipropylene One of dilauryl thiolate, distearyl thiodipropionate and a combination thereof.

[0060] The slip agent is a butyl fat slip agent; the plasticizer is one of trioctyl trimellitate, epoxidized soybean oil or a combination thereof.

[0061] The heat stabilizer, which is a polyvinyl chloride composite heat stabilizer, is one ...

Embodiment 2

[0094] The high-performance polyvinyl chloride composite material for wire and cable provided in this embodiment and the preparation method thereof, its steps are basically the same as in Example 1, except that:

[0095] A high-performance polyvinyl chloride composite material for wire and cable, which is made of the following raw materials in parts by weight:

[0096]

[0097] The antimony-free environment-friendly flame retardant system is made of the following raw materials in parts by weight:

[0098]

[0099] The polyvinyl chloride resin has a molecular weight of 1200, a K value of 55, and a degree of polymerization of 1400.

[0100] The mineral filler, which is magnesium hydroxide;

[0101] Described antioxidant, it is 2.4 di-tert-butylphenyl-phosphite triesters.

[0102] Described plasticizer, it is trioctyl trimellitate.

[0103] Described thermal stabilizer, it is tribasic lead sulfate.

[0104] A preparation method for the above-mentioned high-performance p...

Embodiment 3

[0132] The high-performance polyvinyl chloride composite material and preparation method thereof for electric wires and cables provided by this embodiment, its steps are basically the same as those in Examples 1 and 2, except that:

[0133] A high-performance polyvinyl chloride composite material for wire and cable, which is made of the following raw materials in parts by weight:

[0134]

[0135]

[0136] The antimony-free environment-friendly flame retardant system is made of the following raw materials in parts by weight:

[0137]

[0138] The polyvinyl chloride resin has a molecular weight of 1400, a K value of 65, and a degree of polymerization of 1200.

[0139] The mineral filler is aluminum hydroxide;

[0140] Described antioxidant, it is dilauryl thiodipropionate.

[0141] Described plasticizer, it is epoxy soybean oil.

[0142] The heat stabilizer is dibasic lead phosphite.

[0143] A preparation method for the above-mentioned high-performance polyvinyl c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-performance polyvinyl chloride composite material for wires and cables. The high-performance polyvinyl chloride composite material is characterized in that the high-performance polyvinyl chloride composite material is prepared from the following raw materials in parts by weight: 85-93 parts of polyvinyl chloride resin, 35-45 parts of mineral filler, 1.5-2 parts of antioxidant, 2.6-3 parts of lubricant, 25-35 parts of plasticizer and 8-13 parts of heat stabilizer and 6-10 parts of antimony-free environment-friendly fire retardant system, wherein the antimony-free environment-friendly fire retardant system is prepared from the following raw materials in parts by weight: 15-20 parts of phosphate environment-friendly fire retardant material, 25-30 parts of organosilicone fire retardant material, 40-45 parts of magnesium-aluminum inorganic flame retardant materials and 5-10 parts of titanate coupling agent. The invention also provides a preparation method of the high-performance polyvinyl chloride composite material for wires and cables.

Description

technical field [0001] The invention belongs to the technical field of material modification, and in particular relates to a high-performance polyvinyl chloride composite material for electric wires and cables and a preparation method thereof. Background technique [0002] In line with the requirements of global green and environmental protection economic development, actively developing high-performance environmentally friendly flame retardants is an important means for manufacturers around the world to compete for more market share in the future. With the increasingly stringent fire safety standards at home and abroad and the development of my country's economy, the amount of plastic and rubber is increasing rapidly, and various flame-retardant materials are showing a geometric growth trend. It is understood that the total consumption of flame retardants in the world in 2012 has exceeded 1.8 million tons per year, of which 85% are additive flame retardants and 15% are reac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/04C08K3/22C08K3/32C08K5/54C08K3/04B29B7/00B29B9/06
Inventor 白建文
Owner 深圳市领亚电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap