Method for manufacturing recombined bamboo decorative veneers
A manufacturing method and a technology of recombining bamboo, which are applied in the jointing of wooden veneers, manufacturing tools, and monocarboxylate copolymer adhesives, etc., can solve the problems of difficult planing, low moisture content, and high density of bamboo. question
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] Embodiment 1: get the bamboo bunch 12Kg that length is 60cm, through degreening and yellowing and loosening treatment, moderate carbonization, moisture content is dried to 12%, put into the plastic tank that adhesive is housed and impregnate. The formula of the adhesive is: urea-formaldehyde resin 30Kg, modified starch emulsion 20Kg, polyvinyl acetate emulsion 20Kg, organic acid solution 1.5Kg, isocyanate prepolymer 2.5Kg;
[0021] After soaking for 15 minutes, take out the bamboo bundles for a simple pressing process, squeeze out the excess adhesive, and then put them into an iron mold, apply high pressure to make it a bamboo square with a cross-sectional size of 15cm×15cm, and do a reinforcement treatment to make it bulky. In the same state, place it at room temperature for 6 days, let the adhesive fully cure, remove the formwork and get the recombined bamboo square. The thus obtained recombined bamboo square is planed and dried to obtain the required recombined bambo...
Embodiment 2
[0022] Embodiment 2: the adhesive formulation in embodiment 1 is changed as follows:
[0023] Urea-formaldehyde resin 30Kg, modified starch emulsion 10Kg, polyvinyl acetate emulsion 30Kg, organic acid solution 1.5Kg, isocyanate prepolymer 3.0Kg. The rest remain unchanged, that is, the recombined bamboo decorative veneer is obtained.
Embodiment 3
[0024] Embodiment 3: the adhesive formulation in embodiment 1 is changed as follows:
[0025] Urea-formaldehyde resin 30Kg, modified starch emulsion 30Kg, polyvinyl acetate emulsion 30Kg, organic acid solution 1.5Kg, isocyanate prepolymer 4.0Kg. The rest remain unchanged, that is, the recombined bamboo decorative veneer is obtained.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com