Black infrared reflection type photovoltaic EVA (Ethylene Vinyl Acetate) adhesive film

An infrared reflection and photovoltaic technology, which is used in photovoltaic power generation, adhesives, film/sheet adhesives, etc., can solve the problems of low power, high power consumption, and low infrared reflectivity of components, and reduce temperature rise and power. effect of loss

Active Publication Date: 2014-06-25
CSI SOLAR POWER GROUP CO LTD +2
View PDF4 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Black components have a strong absorption of infrared light, resulting in a large temperature rise of the components, which is 2-8°C higher than that of white or colorless components, and the power of the components is 1.5%-5% lower than that of ordinary components.
When the photovoltaic EVA film of the prior art encapsulates blac

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black infrared reflection type photovoltaic EVA (Ethylene Vinyl Acetate) adhesive film
  • Black infrared reflection type photovoltaic EVA (Ethylene Vinyl Acetate) adhesive film
  • Black infrared reflection type photovoltaic EVA (Ethylene Vinyl Acetate) adhesive film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: The photovoltaic EVA adhesive film of this example comprises EVA resin, and the raw material components described below in terms of the mass of EVA resin:

[0020]

[0021] In this example, the cross-linking agent is tert-butyl peroxycarbonate-2-ethylhexyl; the auxiliary cross-linking agent is triallyl isocyanurate and trihydroxyl in a mass ratio of 1:0 to 1:1 Methylpropane trimethacrylate; infrared-reflecting pigments such as BASF's Black; UV light absorber is 2-hydroxy-4-n-octyloxybenzophenone; UV light stabilizer is bis(2,2,6,6 tetramethyl-4 piperidine) sebacic acid ester; auxiliary Antioxidant is tris(4-nonylphenol) phosphite and tris(2,4-di-tert-butylphenyl) phosphite in mass ratio of 1:0~1:1; tackifier is γ-methyl phosphite Acryloyloxypropyltrimethoxysilane; flame retardant is trioctyl phosphate; antacid is calcium stearate.

Embodiment 2

[0022] Embodiment 2: The photovoltaic EVA adhesive film of this example comprises EVA resin, and the raw material components described below in terms of the mass of EVA resin:

[0023]

[0024]

[0025] The specific types of each raw material component in this example are the same as those in Example 1.

Embodiment 3

[0026] Embodiment 3: The photovoltaic EVA adhesive film of this example comprises EVA resin, and the raw material components described below in terms of the mass of EVA resin:

[0027]

[0028] The specific types of each raw material component in this example are the same as those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Volume resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a black infrared reflection type photovoltaic EVA (Ethylene Vinyl Acetate) adhesive film. The photovoltaic EVA adhesive film comprises EVA resin as well as the following raw materials counted by the mass of the EVA resin: 0.1-2% of a cross-linking agent, 0.1-2% of an assistant crosslinker and 0.05-0.5% of an infrared reflection pigment. According to the photovoltaic EVA adhesive film, the infrared reflection pigment is added in the EVA resin, is black and has high infrared reflectivity, so that the prepared EVA adhesive film has good infrared reflection performance; by packaging a photovoltaic assembly by virtue of the photovoltaic EVA adhesive film, the power loss and temperature rise of the packaging assembly can be effectively reduced.

Description

technical field [0001] The invention relates to the technical field of photovoltaic EVA adhesive films, in particular to a black infrared reflective photovoltaic EVA adhesive film. Background technique [0002] Photovoltaic industry is an industry with rapid technological update and development. At present, the photovoltaic industry is developing towards diversification. The research and development of various functional components with high reliability, high power, low energy consumption and low cost has become a direction of photovoltaic module development. On the basis of the production of traditional components in ordinary EVA packaging, various photovoltaic manufacturers are also developing new functional components, such as double-sided glass components, anti-glare components, heat dissipation components, and black components. [0003] Photovoltaic EVA film is usually colorless, transparent or white material. White EVA film is usually used on the lower layer of the mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J7/00C09J123/08C09J11/00C09J11/06H01L31/048H01L31/054
CPCY02E10/52
Inventor 唐景傅冬华彭丽霞唐应堂
Owner CSI SOLAR POWER GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap