Composite metal wire and manufacturing method

A metal composite, wire technology, applied in the direction of metal/alloy conductors, cable/conductor manufacturing, conductors, etc., can solve the problems of hard material, high elasticity, high processing cost, and achieve the effect of low loss

Inactive Publication Date: 2014-07-23
黄忠波
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the low-carbon steel required by copper-clad steel needs to be highly purified, so the processing cost is high. Its material is hard and has high elasticity and is not easy to b...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A metal composite wire, which is composed of a core body and a cladding layer, wherein the cladding layer is copper, especially copper with a weight purity of 99.90-99.98%; the core body is made of 35% copper by weight, 55% iron by weight and aluminum 10% iron alloy by weight; the thickness of the cladding layer is 1 / 4-1 / 2 of the wire radius.

[0018] The wire blank is drawn by a wire drawing machine through a multi-pass drawing die, so that the interface of copper and iron alloy is metallurgically combined to form a wire with a required wire diameter.

[0019] Its preparation method comprises the following steps:

[0020] Remove the grease and oxidation passivation layer on the surface of copper strip and ferroalloy wire;

[0021] Copper is coated on the iron alloy wire with a diameter of 10mm-12mm to make a composite billet;

[0022] Draw the composite blank to a diameter of 3-5mm at a speed of 120m / min-150m / min and a diameter reduction rate of 13-18%;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite metal wire and a manufacturing method. The composite metal wire is formed by compositing a core body and a coating layer, and the coating layer is made of copper and particularly the copper with the weight purity ranging from 99.90% to 99.98%; the core body is an iron alloy comprising, by weight, 35% of copper, 55% of iron and 10% of aluminum; the thickness of the coating layer is from one fourth to one second the radius of the wire. The direct-current resistivity of the composite wire made of the copper-coated iron alloy is lower than that of a copper-coated steel wire, signal transmission is ensured, the requirement for the carrying capacity when the composite metal wire is applied to the electron industry is met, and the loss of the composite metal wire is smaller than that of the copper-coated steel wire.

Description

technical field [0001] The invention belongs to the field of metal wires, in particular to a copper-clad iron composite wire and a preparation method thereof. Background technique [0002] From the point of view of the social benefits of resource use and the saving of copper resources, it is also of great practical significance to use bimetallic materials as ground conductors for communication and power transmission. [0003] However, the low-carbon steel required by copper-clad steel needs to be highly purified, so the processing cost is high. Its material is hard and has high elasticity and is not easy to bend. It is only suitable for the communication cable industry. It is not suitable to use this composite material instead of copper in the electronics industry. line, so there are certain limitations. Contents of the invention [0004] The purpose of the present invention is to solve the deficiencies of existing composite wires in certain application fields by providin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01B1/02H01B5/00H01B13/00
Inventor 黄忠波
Owner 黄忠波
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap