A kind of resistance spot welding method of aluminum matrix composite material

An aluminum-based composite material, resistance spot welding technology, applied in resistance welding equipment, welding/cutting medium/material, welding medium, etc., can solve the problem of small tensile shear force, low joint strength, and small nugget diameter of spot welded joints. and other problems, to achieve the effect of simple and convenient welding process, reducing equipment damage and improving tensile and shear force.

Inactive Publication Date: 2016-09-07
ZHENGZHOU UNIV +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The technical problem to be solved by the present invention is: aiming at defects such as small nugget diameter, small tensile shear force and adhesion of the spot welded joint existing in the existing aluminum matrix composite material resistance spot welding method, the present invention provides a method that can improve At present, the method of resistance spot welding joint performance of aluminum matrix composite material, that is, the present invention provides a new resistance spot welding method of aluminum matrix composite material
The technical solution of the invention is to add a pure aluminum foil between the aluminum matrix composite materials for resistance spot welding connection, thereby effectively improving the performance of the current resistance spot welding joints of aluminum matrix composite materials, that is, thereby solving the problem of resistance spot welding of aluminum matrix composite materials Defects such as small nugget diameter, low joint strength and adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of resistance spot welding method of aluminum matrix composite material
  • A kind of resistance spot welding method of aluminum matrix composite material
  • A kind of resistance spot welding method of aluminum matrix composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The matrix of the aluminum-based composite material used in the present invention is 2A12 (LY12), and the reinforcing phase is silicon carbide particles; the aluminum-based composite material is used as a plate with equal thickness on both sides, and is processed into a workpiece with a specification of 45×25×1.5mm. The lap length of the aluminum matrix composite material sample is 15mm when welding; the surface and back of the aluminum matrix composite material are sanded with sandpaper before resistance spot welding, the surface oxide film is removed, and then cleaned with acetone and air-dried; the pure aluminum foil used Smooth and flat, and cleaned with acetone and allowed to air dry before resistance spot welding.

[0057] When resistance spot welding is performed on an aluminum matrix composite material whose matrix is ​​2A12 (LY12) and the reinforcing phase is silicon carbide particles, a pure aluminum foil with a thickness of 6 μm is added between the processed ...

Embodiment 2

[0059] Embodiment 2: basically the same as Embodiment 1, the difference is:

[0060] When resistance spot welding is performed on an aluminum matrix composite material with a matrix of 2A12 (LY12) and a reinforcing phase of silicon carbide particles, a pure aluminum foil with a thickness of 5 μm is added between the processed samples of the aluminum matrix composite material. When a pure aluminum foil is added between the materials for spot welding connection, the preload time is 1.5 seconds, the holding time is 1.8 seconds, the electrode pressure is 3200 Newton, the welding time is 0.5 seconds, and the welding current is 19.0 kA.

[0061] The shape of the electrode tip of the spot welder used in the above embodiments is a flat electrode.

Embodiment 3

[0062] Embodiment 3: basically the same as Embodiment 1, the difference is:

[0063] When resistance spot welding is performed on an aluminum matrix composite material with a matrix of 2A12 (LY12) and a reinforcing phase of silicon carbide particles, a pure aluminum foil with a thickness of 7 μm is added between the processed samples of the aluminum matrix composite material. When a pure aluminum foil is added between the materials for spot welding connection, the preload time is 1.0 seconds, the holding time is 1.2 seconds, the electrode pressure is 2800 Newton, the welding time is 0.4 seconds, and the welding current is 17.5 kA.

[0064] The electrode tip shape of the spot welder used in the above embodiments is a dome surface electrode.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a resistance spot welding method of an aluminum-based composite material. When performing resistance spot welding connection of aluminum matrix composite materials, a pure aluminum foil with a thickness of 2-10 μm is added between the aluminum matrix composite materials, and a pure aluminum foil is added between the aluminum matrix composite materials for spot welding connection. The preloading time is 0.8-1.8 seconds, the holding time is 1.0-2.2 seconds, the electrode pressure is 2500-3500 Newtons, the welding time is 0.3-0.5 seconds, and the welding current is 16.5-19.5 kA. In the invention, a pure aluminum foil is added between the aluminum matrix composite materials for resistance spot welding connection, thereby effectively improving defects such as small nugget diameter, low joint strength and adhesion of the current aluminum matrix composite material resistance spot welding. The aluminum-based composite material is spot-welded by the present invention, the average diameter of the nugget is 7.2mm, and the average shear resistance of the joint is 2043.9N.

Description

technical field [0001] The invention relates to a process method for improving the performance of resistance spot welding joints of aluminum-based composite materials, in particular to a method for improving the joint performance by adding pure aluminum foil between two aluminum-based composite materials on the basis of conventional aluminum-based composite material resistance spot welding. Process methods for joint performance. That is, the present invention specifically relates to a method for resistance spot welding of aluminum matrix composite materials. Background technique [0002] Aluminum matrix composites are currently the most widely used and fastest-growing metal matrix composites. They have the advantages of high specific strength, high specific modulus, good wear resistance and low thermal expansion coefficient. Combination design is carried out, so it has a great application prospect. However, the thermophysical properties such as melting point, thermal condu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K11/11
CPCB23K11/115B23K11/185B23K11/34B23K35/002B23K35/0261B23K35/0288B23K35/302B23K2103/10
Inventor 李杏瑞牛济泰史新伟
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com