Color masterbatch with pearly luster color capable of changing along with angle

A technology of pearlescent color masterbatch and angle follower, which is applied in the field of color masterbatch, which can solve the problem that the color masterbatch cannot change color, etc., and achieve the effects of improving weather resistance, bright color, and impact resistance

Inactive Publication Date: 2014-08-27
CHUZHOU HONGYUAN SPRAYING
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the color masterbatch in the prior art cannot achieve color change with the angle, therefore, there is an urgent need for a new technical solution that can solve the above technical problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Example 1 : A kind of angle-changing pearlescent color masterbatch, said angle-changing pearlescent color masterbatch is composed of the following components and mass percentage: carrier 30-80%, additive 5-7%, dispersant 6-9%, pearl powder 3 —6%, pigment 2-5%, organic acid calcium 1-2%, organic acid zinc 1-2%.

[0014] The carrier is one of polyvinyl chloride, polyethylene, polypropylene and polystyrene. The additive is one or a mixture of flame retardants, brighteners, antibacterial agents, antistatic agents and antioxidants. The dispersant is one of polyethylene low molecular weight wax, stearate or a mixture of both.

Embodiment 2

[0015] Example 2 : A preparation method of angular-variable pearlescent masterbatch, said method comprising the following steps: 1) according to mass percentage, add 5-7% of additive, 6-9% of dispersant, 3-6% of pearl powder, 2% of pigment -5% mixing; 2) Add 1-2% calcium organic acid and 1-2% zinc organic acid; 3) Co-extrude the mixture obtained in step 2 with 30-80% carrier; 4) Cool the obtained mixture with water can be made. The carrier is one of polyvinyl chloride, polyethylene, polypropylene and polystyrene. The additive is one or a mixture of flame retardants, brighteners, antibacterial agents, antistatic agents and antioxidants. The dispersant is one of polyethylene low molecular weight wax, stearate or a mixture of both.

[0016]

Embodiment 3

[0017] Example 3 : A preparation method of angular-variable pearlescent masterbatch, said method comprising the following steps: 1) according to mass percentage, add 6-7% of additive, 7-8% of dispersant, 4-5% of pearl powder, 3% of pigment -4% mixing; 2) Add 1-1.5% calcium organic acid and 1-1.5% zinc organic acid; 3) Co-extrude the mixture obtained in step 2 with 40-75% carrier; 4) Cool the obtained mixture with water can be made. The carrier is one of polyvinyl chloride, polyethylene, polypropylene and polystyrene. The additive is one or a mixture of flame retardants, brighteners, antibacterial agents, antistatic agents and antioxidants. The dispersant is one of polyethylene low molecular weight wax, stearate or a mixture of both.

[0018]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to color masterbatch with pearly luster color capable of changing along with the angle. The color masterbatch with the pearly luster color capable of changing along with the angle is characterized by comprising, by weight percentage, 30-80% of carriers, 5-7% of additives, 6-9% of dispersants, 3-6% of pearl powder, 2-5% of paints, 1-2% of organic acid calcium and 1-2% of organic acid zinc. The color of the masterbatch can change continuously along with the angle, the masterbatch is indispensable additives for colorization of plastic products, and for PVC products formed in an extrusion mode, the color masterbatch with the pearly luster color capable of changing along with the angle is rich in type and color, good in lustrousness and high in controllability.

Description

Technical field [0001] The present invention involves a kind of female material, which is particularly involved in a color -changing pearl -colored parent material. Background technique [0002] The color mother material, that is, the color concentrate, is a mixture of high concentration colors prepared by resin and large pigments or dyes.The color mother, also known as color species, is a cluster that is made of ultra -constant pigments or dyes in the resin.During processing, a colorful resin or product can be achieved with a small amount of female material and unsolved resin to achieve the design pigment concentration.Color maternal materials are widely used in resin, which are widely used in polyethylene, polypropylene, polystyrene, ABS, nylon, PC, PMMA, PET and other resin.Electrical appliances, agricultural film, automobile accessories, health equipment and other products.However, the color female material in the existing technology cannot be discolored with the angle. There...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/06C08L23/12C08L25/06C08K5/098
Inventor 王新志
Owner CHUZHOU HONGYUAN SPRAYING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com