Friction-resistant plastic and preparation method thereof

A friction-resistant and plastic technology, applied in the field of plastic products, can solve the problems of poor friction resistance, restricting the development of plastics, and short service life, etc., and achieve the effects of high production efficiency, enhanced chemical stability, and convenient operation

Inactive Publication Date: 2015-07-22
SUZHOU JIN YUAN OIL MACHINERY
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because plastic has the advantages of light weight, no rust, good insulation, and low cost, plastic products are used in many links in various fields, but plastic itself also has some disadvantages: such as poor friction resistance, low strength, Factors such as short service life restrict the development of plastics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A friction-resistant plastic provided in this embodiment, the composition of the friction-resistant plastic is as follows: polyvinyl chloride resin: 90 parts, silicon carbide: 6 parts, talcum powder: 1 part, graphite powder: 5 parts, double Phenol A epoxy resin: 50 parts, sodium tripolyphosphate: 5 parts, mineral oil: 3 parts, polyvinylidene chloride: 7 parts, sodium tripolyphosphate: 7 parts, hydroxypropyl methacrylate: 6 parts, titanium White powder: 1 part, iron powder: 5 parts, deionized water: 30 parts, silane coupling agent KH560: 3 parts, auxiliary agent: 2 parts;

[0024] The components of the additives are calculated in parts by weight: mica powder: 3 parts, kaolinite: 1 part, deionized water: 50 parts, glycerin: 5 parts, calcium oxide: 1 part, magnesium hydroxide: 4 parts, Paraffin: 1 part, polyvinyl chloride resin: 12 parts;

[0025] The preparation method of the auxiliary agent is: mix and pulverize mica powder, kaolinite, glycerin, and calcium oxide, pass ...

Embodiment 2

[0031] A friction-resistant plastic provided in this embodiment, the components of the friction-resistant plastic are: polyvinyl chloride resin: 92 parts, silicon carbide: 8 parts, talcum powder: 3 parts, graphite powder: 7 parts, double Phenol A epoxy resin: 55 parts, sodium tripolyphosphate: 10 parts, mineral oil: 5 parts, polyvinylidene chloride: 9 parts, sodium tripolyphosphate: 9 parts, hydroxypropyl methacrylate: 8 parts, titanium White powder: 3 parts, iron powder: 7 parts, deionized water: 40 parts, silane coupling agent KH560: 5 parts, additives: 4 parts;

[0032]The components of the auxiliary agent are calculated in parts by weight: mica powder: 5 parts, kaolinite: 3 parts, deionized water: 60 parts, glycerin: 7 parts, calcium oxide: 3 parts, magnesium hydroxide: 6 parts, Paraffin: 3 parts, polyvinyl chloride resin: 14 parts;

[0033] The preparation method of the auxiliary agent is: mix and pulverize mica powder, kaolinite, glycerin, and calcium oxide, pass throug...

Embodiment 3

[0039] A friction-resistant plastic provided in this embodiment, the components of the friction-resistant plastic are: polyvinyl chloride resin: 91 parts, silicon carbide: 7 parts, talcum powder: 2 parts, graphite powder: 6 parts, double Phenol A epoxy resin: 54 parts, sodium tripolyphosphate: 8 parts, mineral oil: 4 parts, polyvinylidene chloride: 8 parts, sodium tripolyphosphate: 8 parts, hydroxypropyl methacrylate: 7 parts, titanium White powder: 2 parts, iron powder: 6 parts, deionized water: 35 parts, silane coupling agent KH560: 4 parts, additives: 3 parts;

[0040] The components of the auxiliary agent are calculated in parts by weight: mica powder: 4 parts, kaolinite: 2 parts, deionized water: 56 parts, glycerin: 6 parts, calcium oxide: 2 parts, magnesium hydroxide: 5 parts, Paraffin: 2 parts, polyvinyl chloride resin: 13 parts;

[0041] The preparation method of the auxiliary agent is: mix and pulverize mica powder, kaolinite, glycerin, and calcium oxide, pass throug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a friction-resistant plastic and a preparation method thereof. The friction-resistant plastic comprises the following components in parts by mass: 90-92 parts of polyvinyl chloride resin, 6-8 parts of silicon carbide, 1-3 parts of talcum powder, 5-7 parts of graphite powder, 50-55 parts of bisphenol A epoxy resin, 5-10 parts of sodium tripolyphosphate, 3-5 parts of mineral oil, 7-9 parts of polyvinylidene chloride, 7-9 parts of sodium tripolyphosphate, 6-8 parts of hydroxypropyl methacrylate, 1-3 parts of titanium dioxide, 5-7 parts of iron powder, 30-40 parts of deionized water, 3-5 parts of a silane coupling agent KH560 and 2-4 parts of auxiliaries.

Description

technical field [0001] The invention belongs to plastic products, and relates to a friction-resistant plastic and a preparation method thereof. Background technique [0002] With the development and progress of society and the improvement of material living standards, people's requirements for living and working environments are getting higher and higher. Because plastic has the advantages of light weight, no rust, good insulation, and low cost, plastic products are used in many links in various fields, but plastic itself also has some disadvantages: such as poor friction resistance, low strength, Factors such as short service life restrict the development of plastics. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the shortcomings of the prior art and provide a friction-resistant plastic and its preparation method. The plastic has high strength, good toughness, vibration resistance, heat resistance, corrosion...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L63/00C08L27/08C08K13/02C08K3/04C08K3/34C08K3/32C08K5/01C08K3/08C08F291/10C08F220/28
CPCC08L27/06C08K2201/014C08L2201/08C08L2205/02C08L2205/025C08L2205/035C08L63/00C08L27/08C08L91/06C08L91/00C08K13/02C08K3/34C08K5/053C08K2003/2224C08K2003/324C08K2003/2241C08K3/04C08K2003/0856
Inventor 袁增泉李国庆
Owner SUZHOU JIN YUAN OIL MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap