Environment-friendly latex paint

A technology of environmentally friendly latex and acrylic emulsion, applied in the direction of latex paint, coating, etc., can solve the problems of unsatisfactory application effects, achieve excellent adhesion, improve the quality of life, and cause little harm to the human body and the environment

Inactive Publication Date: 2014-09-10
NANTONG XIONGYING PAINT
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although a variety of functional latex paint products have appeared on the market today, the actual application effect of such products has been unsatisfactory for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] An environmentally friendly latex paint, which is prepared from the following components by weight: 150 parts of nanoacrylic acid emulsion, 100 parts of deionized water, 50 parts of ultrafine silicon dioxide, 40 parts of titanium dioxide, 10 parts of camphor extract, 7 parts of propylene glycol, 4 parts of manganese naphthenate, 3 parts of sodium hexametaphosphate, 2 parts of dispersant, 1 part of preservative, 2 parts of thickener, 1 part of defoamer, and 0.5 part of coalescent.

[0011] The method for preparing the above-mentioned environmentally friendly latex paint is as follows: add nano-acrylic emulsion and camphor extract to the disperser in a stirring state according to the formula, disperse at a low speed for 4-6 minutes, then add the remaining materials except titanium dioxide, and disperse at a medium speed for 10-6 minutes. After 15 minutes, finally add titanium dioxide and stir to mix evenly, then filter and discharge.

Embodiment 2

[0013] An environment-friendly latex paint, which is prepared from the following components by weight: 180 parts of nanoacrylic acid emulsion, 120 parts of deionized water, 65 parts of ultrafine silicon dioxide, 55 parts of titanium dioxide, 15 parts of camphor extract, 12 parts of propylene glycol, 6 parts of manganese naphthenate, 4 parts of sodium hexametaphosphate, 3 parts of dispersant, 2 parts of preservative, 3 parts of thickener, 2 parts of defoamer, and 1 part of coalescent.

[0014] The method for preparing the above-mentioned environmentally friendly latex paint is as follows: add nano-acrylic emulsion and camphor extract to the disperser in a stirring state according to the formula, disperse at a low speed for 4-6 minutes, then add the remaining materials except titanium dioxide, and disperse at a medium speed for 10-6 minutes. After 15 minutes, finally add titanium dioxide and stir to mix evenly, then filter and discharge.

Embodiment 3

[0016] An environment-friendly latex paint, which is prepared from the following components by weight: 200 parts of nanoacrylic acid emulsion, 150 parts of deionized water, 80 parts of ultrafine silicon dioxide, 65 parts of titanium dioxide, 20 parts of camphor extract, 15 parts of propylene glycol, 7 parts of manganese naphthenate, 5 parts of sodium hexametaphosphate, 4 parts of dispersant, 3 parts of preservative, 4 parts of thickener, 3 parts of defoamer, and 1.5 parts of coalescent.

[0017] The method for preparing the above-mentioned environmentally friendly latex paint is as follows: add nano-acrylic emulsion and camphor extract to the disperser in a stirring state according to the formula, disperse at a low speed for 4-6 minutes, then add the remaining materials except titanium dioxide, and disperse at a medium speed for 10-6 minutes. After 15 minutes, finally add titanium dioxide and stir to mix evenly, then filter and discharge.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed environment-friendly latex paint is prepared from the following compositions in parts by weight: 150-200 parts of nanometer acrylic emulsion, 100-150 parts of deionized water, 50-80 parts of superfine silicon dioxide, 40-65 parts of titanium dioxide, 10-20 parts of cinnamomum camphora extraction liquid, 7-15 parts of propylene glycol, 4-7 parts of manganese naphthenate, 3-5 parts of sodium hexametaphosphate, 2-4 parts of a dispersant, 1-3 parts of an aseptic, 2-4 parts of a thickening agent, 1-3 parts of an anti-foaming agent and 0.5-1.5 parts of a film-forming auxiliary agent. The beneficial effects comprise that the latex paint is low in preparation cost, extremely excellent in adhesive force and small in damage to human body and environment, and has certain antifouling capability; and also, the added cinnamomum camphora extraction liquid helps to effectively dispel mosquitoes and improve life quality.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to an environment-friendly latex paint. Background technique [0002] Under the circumstances of increasingly stringent environmental protection requirements, global warming, and shortage of energy resources, it is imminent to vigorously develop environmentally friendly coatings. Although the development of latex paint is late, it is quickly favored by people and develops rapidly due to its unique advantages of safety and environmental protection. With the continuous improvement of people's requirements for quality of life, latex paint will also move towards the direction of high performance, low energy consumption and functionality develop. Although a variety of functional latex paint products have appeared on the market today, the actual application effect of this type of product has been unsatisfactory for a long time. Contents of the invention [0003] The techn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/02C09D7/12
Inventor 蒋建军虞天笔
Owner NANTONG XIONGYING PAINT