Liquid crystal resin composition for camera module

A technology of resin composition and liquid crystallinity, which is applied in the field of liquid crystal resin composition, and can solve problems such as the reduction of optical characteristics of camera modules

Active Publication Date: 2016-04-13
POLYPLASTICS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For components used in optical equipment such as camera modules, when minute dirt, oil, and dust adhere to the lens, the optical characteristics of the camera module will be significantly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid crystal resin composition for camera module
  • Liquid crystal resin composition for camera module
  • Liquid crystal resin composition for camera module

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The (A) liquid crystalline resin used in the present invention can be prepared from the above-mentioned monomer compound (or a mixture of monomers) by a known method using a direct polymerization method or an ester exchange method, usually using a melt polymerization method or a slurry polymerization method. Wait. The above-mentioned compounds having ester-forming ability may be used in the polymerization as they are, or may be modified from a precursor to a derivative having the ester-forming ability in the early stage of polymerization. For their polymerization, various catalysts can be used, and typical examples include dialkyltin oxides, diaryltin oxides, titanium dioxide, alkoxytitanosilicates, titanium alkoxides, carboxylic acid Alkali metal salts and alkaline earth metal salts, like BF 3 Such Lewis acid salts etc. The amount of the catalyst used is usually about 0.001 to 1% by mass, particularly preferably about 0.01 to 0.2% by mass, based on the total weight o...

Embodiment

[0089] The following examples are given to illustrate the present invention in more detail, but the present invention is not limited to these examples.

[0090]

[0091] Liquid crystal resin (liquid crystal polyester amide resin): VECTRA (registered trademark) E950i (manufactured by Polyplastics Co., Ltd.)

[0092] Fibrous filler 1: TISMON-102 manufactured by Otsuka Chemical Co., Ltd. (potassium titanate fiber, average fiber diameter 0.3-0.6 μm, average fiber length 10-20 μm)

[0093] Fibrous filler 2: Nitto Bosho Co., Ltd. make PF70E-001 (ground glass fiber, fiber diameter 10 μm, weight average length 70 μm)

[0094] Non-fibrous filler 1: Crown TalcPP manufactured by Matsumura Sangyo Co., Ltd. (talc, average particle diameter 12.8 μm, average aspect ratio 6)

[0095] Non-fibrous filler 2: AB-25S manufactured by Yamaguchi Mica Industry (mica, average particle diameter 24 μm)

[0096] Non-fibrous filler 3: A-41S manufactured by Yamaguchi Mica Industry (Mica, average particl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The present invention provides a liquid crystalline resin composition for a camera module, which is used for producing a member for a camera module in which the surface of a molded body is less likely to fluff. The resin composition is compounded with (A) liquid crystal resin, at least one (B) inorganic filler selected from (B1) fibrous filler and (B2) non-fibrous filler, selected from (C1) At least one (C) copolymer of an olefin-based copolymer and a (C2) styrene-based copolymer such that the (A) component is 65 to 93% by mass, the (B) component is 5 to 20% by mass, and the (C) component 2 to 10% by mass, the average fiber diameter of the component (B1) is 1.0 μm or less, and the average fiber length is 5 to 50 μm, and the component (B2) is selected from sheet fillers and granular fillers with an average particle diameter of 50 μm or less. At least one of the fillers, (C1) component and (C2) component consists of a specific component.

Description

technical field [0001] The present invention relates to a liquid crystalline resin composition for a camera module. Background technique [0002] Liquid crystalline resins represented by liquid crystalline polyester resins have excellent mechanical strength, heat resistance, chemical resistance, electrical properties, etc. in a well-balanced manner, and also have excellent dimensional stability, so they are regarded as high-functional engineering plastics. widely used. Recently, these properties of liquid crystalline resins have been utilized for precision equipment parts. [0003] In the case of precision equipment, especially optical equipment with lenses, small amounts of dirt, dust, etc. can affect equipment performance. For components used in optical equipment such as camera modules, when minute dirt, oil, or dust adheres to the lenses, the optical characteristics of the camera modules are significantly degraded. In order to prevent such degradation of optical proper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03B17/02C08K3/00C08K7/00C08L63/00C08L101/12
CPCG03B17/02C09K19/3809C08L77/12C08K3/346C08K7/04C08L23/0884C08L25/08C08K3/013C08L101/12C08L63/00C08K3/04
Inventor 广濑悠人平等文雄深津博树田口吉昭
Owner POLYPLASTICS CO LTD