Bio-enzyme and rare earth type jute fiber oil and production method thereof

A bio-enzyme and hemp fiber technology, applied in plant fiber, biochemical fiber treatment, fiber treatment, etc., to achieve the effects of not easy to fluff and fall off, enhance spinnability, and reduce environmental pollution

Active Publication Date: 2010-07-07
南宁飞日润滑科技股份有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no public literature report on the preparation of hemp fiber oil by the above-mentioned process route in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031]First add amino acid (YIFN SLG-12) and 250KG surfactant solution, add 40KG Span-80 (Span-80), stir evenly and heat to 50±5°C, take the first sample to check whether it is dissolved well. Then add biological enzyme, i.e. LY-A128L acid cellulase (manufacturer: Hubei Liye Biological Products Co., Ltd.) 59KG, rare earth element lanthanum (manufacturer: Changsha Deli Rare Earth Chemical Co., Ltd.) 1KG, hydrorefined 150SN base oil 500KG, 150KG refined camellia oil, continue to heat to 70±5°C and stir for 2 hours, then you can take a sample for testing and test its physical and chemical indicators. get the product.

Embodiment 2

[0033] Add 45KG Tween-80 (Tween-80) to betaine (BS-12) and 280KG surfactant solution first, stir evenly and heat to 50±5°C, take the first sample to check whether it is dissolved well Then add the biological enzyme LY-A128L acid cellulase 65KG, rare earth element lanthanum 1KG, hydrorefined 150SN base oil 450KG, 160KG refined camellia oil, continue to heat to 70±5℃ and stir for 2 hours, then take samples for analysis and test its Physical and chemical indicators. get the product.

Embodiment 3

[0035] First mix amino acid (YIFN SLG-12), 150KG of surfactant solution, and 150KG of betaine type (BS-12) surfactant solution, then add 25KG of Span-80 (Span-80), 25KG of Tween 80 ( Tween-80), stir evenly and heat to 50±5°C, take the first sample to check whether it is dissolved well, add biological enzyme, namely LY-A128L acid cellulase 70KG, rare earth element lanthanum 1KG, hydrogenation refining 150SN base oil 400KG, 180KG refined camellia oil, continue to heat to 70±5°C and stir for 2 hours, then take a sample for testing and test its physical and chemical indicators. get the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
acid valueaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides bio-enzyme and rare earth type jute fiber oil and a production method thereof. In the method, hydrogenated refined 150SN base oil and tea oil are adopted as an oiliness additive and an assistant; proper bio-oil and bio-enzyme technology is introduced; and new compound technology is adopted, and superfine microemulsion decoloration and degradation are coordinated. The bio-enzyme and rare earth jute fiber oil comprises the following raw materials: hydrogenated refined 150SN base oil, refined tea oil, solution of ionic surfactant, a non-ionic surfactant, bio-enzyme, and rare earth elements. The bio-enzyme and rare earth type jute fiber oil can soften the fiber, so that long and hard fiber of the jute fiber is bulked and refined, desquamation and end breakage rate are reduced, and the fiber hardly fuzzes and falls off. The sisal fiber treated by the product has the yarn diameter of less than or equal to 0.2mm and has the brute force of spun yarn of 346.5. Therefore, the friction coefficient between the fiber and machinery can be reduced effectively, and the jute fiber has higher abrasion resistance and hygroscopic property and is hardly ruptured in the spinning process so as to achieve the effects of reducing the end breakage rate and improving the finished product rate.

Description

technical field [0001] The invention relates to a kind of fiber oil for sisal hemp, which can soften the sisal hemp fiber, make the long and hard hemp fiber soft, expand and refine, reduce the rate of shedding and broken ends, and make it difficult to fluff and fall off. Seed hemp fiber oil and its production method. Background technique [0002] At present, the fine petrochemical technology used in the sisal textile field in the world has a relatively high overall level, mainly because of the high level of softening, puffing and reforming treatment technology for sisal fibers. Therefore, high value-added sisal textiles can be produced, and these high-value-added products have high strength, corrosion resistance, fast moisture absorption and heat dissipation, hygiene, good usability, comfortable wearing, breathable, smooth, small elongation, and physical stability Good sex and other advantages, enjoy a high reputation in the international market. With the continuous expans...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/10D06M16/00D06M11/17C12S11/00D06M101/06
Inventor 熊维程
Owner 南宁飞日润滑科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap