Method for producing insulating brick used for oxidation furnace by using glass fiber

A glass fiber and oxidation furnace technology, which is applied in the field of new building materials, can solve the problems that have not been put into industrial realization, and the comprehensive utilization of attapulgite waste is difficult, and achieves the effect of solving the problem of environmental pollution, light bulk density and large amount of use.

Inactive Publication Date: 2014-09-17
HEFEI RISINE HEATEK
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For a long time, the comprehensive utilization of attapulgite waste has been a worldwide problem. Although a lot of research has been done on the comprehensive utilization of attapulgite waste at home and abroad, due to various technical and economic reasons, most of them have not been put into industrial realization.
[0004] In summary, there have been reports of using attapulgite waste as auxiliary raw materials to produce cement, wall bricks, and road materials, but there have been no reports about using attapulgite waste as the main raw material for the production of aerated blocks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing insulating brick used for oxidation furnace by using glass fiber
  • Method for producing insulating brick used for oxidation furnace by using glass fiber
  • Method for producing insulating brick used for oxidation furnace by using glass fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] A method of utilizing glass fibers to prepare insulating bricks for oxidation furnaces is carried out according to the following steps:

[0020] (1), mix the raw materials according to the following dry basis mass parts:

[0021]

[0022]

[0023] (2) Mix and stir the above-mentioned raw materials to obtain a slurry, and the slurry is foamed at a temperature of 60-80° C. for 30-40 minutes;

[0024] (3), steam curing the foamed slurry of the above step (2) under normal pressure to obtain a green body, and cut into corresponding sizes;

[0025] (4), the green body of the above step (3) is maintained in 0.8-0.9Mpa steam for 18-22h, during which soap surfactant is sprayed to the green body every 0.6 hours to obtain the finished product of thermal insulation brick for oxidation furnace.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing an insulating brick used for an oxidation furnace by using a glass fiber. The method comprises the following steps: (1) mixing raw materials consisting of, on a dry basis, 55 to 60 parts by mass of a crushed glass fiber, 20 to 30 parts by mass of fly ash and 6 to 10 parts by mass of quicklime, wherein the fly ash has silica content of no less than 40% and iron mineral content of no greater than 15% and the quicklime has active calcium oxide content of no less than 80% and magnesium oxide content of no greater than 2%; (2) mixing the above-mentioned raw materials with stirring so as to obtain slurry and subjecting the slurry to foaming at 60 to 80 DEG C for 30 to 40 min; (3) subjecting foamed slurry prepared in the step (2) to steam curing at normal pressure so as to obtain a green body and cutting the green body to corresponding sizes; and (4) subjecting the green body prepared in the step (3) to steam curing at a pressure of 0.8 to 0.9 Mpa for 18 to 22 h and sprinkling a soap surfactant on the green body every 0.6 h during steam curing so as to obtain a finished insulating brick product used for the oxidation furnace. According to the invention, the usage amount of an attapulgite waste material is great, energy conservation and environmental protection are realized, the problem of environmental pollution caused by stockpiling treatment of attapulgite waste materials is alleviated, and a novel raw material is provided for a hollow brick.

Description

technical field [0001] The invention relates to the field of new building materials, in particular to a method for preparing insulating bricks for oxidation furnaces using glass fibers. Background technique [0002] With the rapid development of social economy and attapulgite industry, attapulgite industrial waste is increasing day by day, which not only puts great pressure on the urban environment, but also limits the development of urban economy and the sustainable development of attapulgite industry, so attapulgite industrial waste Processing and utilization are very important. [0003] For a long time, the comprehensive utilization of attapulgite waste has been a worldwide problem. Although a lot of research has been done on the comprehensive utilization of attapulgite waste at home and abroad, most of them have not been implemented in industry due to various technical and economic reasons. [0004] To sum up, it has been reported that using attapulgite waste as auxilia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B38/02C04B14/42
Inventor 张时利王建跃王皓静
Owner HEFEI RISINE HEATEK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products