RRP (polypropylene random) temperature-resistant water pipe

A temperature-resistant, carrier resin technology, applied in the field of plastic product processing, can solve the problems of resources not being optimally allocated, threatening people's safety, etc., achieving high temperature and low temperature resistance, wide application range, and improving creep.

Inactive Publication Date: 2014-09-24
BLUESTAR CHENGDU NEW MATERIALS
View PDF2 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cold water pipes and hot water pipes in the prior art are difficult to have both high temperature resistance and low temperature resistance. In actual use, some people confuse them because they cannot distinguish the use conditions of cold and hot water pipes. Hot water pipes can be used for cold water pipes. , but cold water pipes cannot be used for hot water pipes. Confusion in use will cause resources to not be allocated optimally, and even threaten people's safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A temperature-resistant PPR pipe, comprising the following raw materials in parts by weight: 80 parts of random copolymerized polypropylene resin, 30 parts of LLDPE, 6 parts of butyl rubber, and 8 parts of special coloring masterbatch for PPR pipes.

[0019] Among them, the special coloring masterbatch for PPR pipe is composed of the following raw materials in parts by weight: 40 parts of random copolymerized polypropylene resin, 21.9 parts of rutile titanium dioxide, 8.8 parts of carbon black, 4.4 parts of permanent yellow, 0.5 parts of polyethylene glycol 200, anti- 0.67 part of oxygen agent 1076, 0.33 part of antioxidant DLTP, 0.1 part of ultraviolet absorber UVP-327, 0.1 part of silver ion antibacterial agent.

[0020] Among them, the moisture content of the special coloring masterbatch for PPR pipe is controlled within 0.12%.

[0021] The preparation method is as follows: Weigh the raw materials according to the above weight parts: random copolymerized polypropylen...

Embodiment 2

[0023] A temperature-resistant PPR pipe, comprising the following raw materials in parts by weight: 60 parts of random copolymerized polypropylene resin, 10 parts of LLDPE, 1 part of butyl rubber, and 3 parts of special coloring masterbatch for PPR pipes.

[0024] Among them, the special coloring masterbatch for PPR pipe is composed of the following raw materials in parts by weight: 60 parts of random copolymerized polypropylene resin, 34 parts of rutile titanium dioxide, 14 parts of carbon black, 7 parts of permanent yellow, 3 parts of polyethylene glycol 200, anti- 2 parts of oxygen agent 1076, 1 part of antioxidant DLTP, 1 part of ultraviolet absorber UVP-327, 1.5 parts of silver ion antibacterial agent.

[0025] Among them, the moisture content of the special coloring masterbatch for PPR pipe is controlled within 0.12%.

[0026] The preparation method is the same as in Example 1.

Embodiment 3

[0028] A temperature-resistant PPR pipe, comprising the following raw materials in parts by weight: 70 parts of random copolymerized polypropylene resin, 15 parts of LLDPE, 2 parts of butyl rubber, and 5 parts of special coloring masterbatch for PPR pipes.

[0029] Among them, the special coloring masterbatch for PPR pipe is composed of the following raw materials in parts by weight: 50 parts of random copolymerized polypropylene resin, 25 parts of rutile titanium dioxide, 10 parts of carbon black, 5 parts of permanent yellow, 1 part of polyethylene glycol 200, anti- 0.77 part of oxygen agent 1076, 0.33 part of antioxidant DLTP, 0.6 part of ultraviolet absorber UVP-327, 0.4 part of silver ion antibacterial agent.

[0030] The preparation method is the same as in Example 1.

[0031] This example is used as a preferred implementation mode. The prepared pipe has the best weather resistance, high temperature resistance and low temperature resistance, strong impact resistance, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of plastic product processing, particularly a RRP (polypropylene random) temperature-resistant water pipe. The RRP temperature-resistant water pipe is prepared from the following raw materials in parts by weight: 60-80 parts of carrier resin, 10-30 parts of LLDPE (linear low-density polyethylene), 1-6 parts of butyl rubber and 3-8 parts of special coloring master batch for RRP pipes. The temperature-resistant pipe has the advantages of high toughness, favorable weather resistance, wide application range and high safety, and can be used as both a cold-water pipe and a hot-water pipe.

Description

technical field [0001] The invention relates to a PPR water pipe, in particular to a PPR temperature-resistant water pipe, which belongs to the technical field of plastic product processing. Background technique [0002] Compared with traditional cast iron pipes, galvanized steel pipes, cement pipes and other pipes, PPR pipes have the advantages of energy saving, environmental protection, light weight and high strength, corrosion resistance, smooth inner wall without scaling, easy construction and maintenance, and long service life. Widely used in building water supply and drainage, urban and rural water supply and drainage, city gas, electric power and optical cable sheathing, industrial fluid transportation, agricultural irrigation and other construction, municipal, industrial and agricultural fields. PPR pipe is officially called random copolymer polypropylene pipe, which is the most widely used water supply pipe in home improvement projects. PPR is a random copolymerize...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/08C08L23/22C08J3/22F16L9/12F16L11/04
CPCC08L23/14C08L2203/18C08L2205/025C08L2205/035C08L2310/00C08L23/0815C08L23/22C08K13/02C08K3/015C08L71/02Y02A20/20
Inventor 王凤德刘咏梅孙潜
Owner BLUESTAR CHENGDU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka