A kind of epoxy resin antirust paint and preparation method thereof

A technology of epoxy resin and anti-rust paint, which is applied in the direction of epoxy resin coating, anti-corrosion coating, coating, etc., to achieve the effect of strong adhesion, fast curing speed and good anti-rust performance

Inactive Publication Date: 2016-07-06
BLUESTAR CHENGDU NEW MATERIALS
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to solve the problems of the epoxy resin antirust paint in the prior art, and provides an epoxy resin antirust paint, which can be cured quickly at room temperature, has strong adhesion, and is suitable for hot and humid conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] An epoxy resin antirust paint, comprising the following raw materials in parts by weight:

[0048] E-51 epoxy resin 40 parts

[0049] 10 parts polybutadiene

[0050] Cyclohexanone 100 parts

[0051] 3 parts of silane coupling agent

[0052] Aluminum stearate 5 parts

[0053] 2 parts calcium chromate

[0054] 5 parts diatomaceous earth

[0055] Zinc phosphochromate 12 parts

[0056] Potassium polymethacrylate 3 parts

[0057] 30 parts of titanium dioxide

[0058] 10 parts of pigment

[0059] 30 parts of curing agent.

[0060] Preferred:

[0061] The silane coupling agent is KH-550 silane coupling agent.

[0062] The potassium polymethacrylate is an aqueous solution, and the weight ratio of the potassium polymethacrylate to water is 1:5.

[0063] Described curing agent is No. 504 curing agent.

Embodiment 2

[0065] An epoxy resin antirust paint, comprising the following raw materials in parts by weight:

[0066] E-51 epoxy resin 60 parts

[0067] 20 parts polybutadiene

[0068] Cyclohexanone 200 parts

[0069] 5 parts of silane coupling agent

[0070] Aluminum stearate 12 parts

[0071] Calcium chromate 9 parts

[0072] Diatomaceous earth 19 parts

[0073] 21 parts zinc phosphochromate

[0074] Potassium polymethacrylate 10 parts

[0075] 50 parts of titanium dioxide

[0076] 20 parts of pigment

[0077] 50 parts of curing agent.

[0078] Preferred:

[0079] The silane coupling agent is KH-550 silane coupling agent.

[0080] The potassium polymethacrylate is an aqueous solution, and the weight ratio of the potassium polymethacrylate to water is 1:9.

[0081] Described curing agent is No. 504 curing agent.

Embodiment 3

[0083] An epoxy resin antirust paint, comprising the following raw materials in parts by weight:

[0084] E-51 epoxy resin 50 parts

[0085] 15 parts polybutadiene

[0086] Cyclohexanone 150 parts

[0087] 4 parts of silane coupling agent

[0088] Aluminum stearate 9.5 parts

[0089] Calcium chromate 5.5 parts

[0090] 12 parts diatomaceous earth

[0091] Zinc phosphochromate 16.5 parts

[0092] Potassium polymethacrylate 6.5 parts

[0093] 40 parts of titanium dioxide

[0094] 15 parts of pigment

[0095] 40 parts of curing agent.

[0096] Preferred:

[0097] The silane coupling agent is KH-550 silane coupling agent.

[0098] The potassium polymethacrylate is an aqueous solution, and the weight ratio of the potassium polymethacrylate to water is 1:7.

[0099] Described curing agent is No. 504 curing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an epoxy resin antirust paint and a preparation method thereof, belonging to the technical field of polymer materials. The epoxy resin antirust paint of the present invention comprises the following raw materials in parts by weight: 40-60 parts of E-51 epoxy resin, 10-20 parts of polybutadiene, 100-200 parts of cyclohexanone, silane coupling 3-5 parts of aluminum stearate, 5-12 parts of aluminum stearate, 2-9 parts of calcium chromate, 5-19 parts of diatomaceous earth, 12-21 parts of zinc phosphochromate, 3-10 parts of potassium polymethacrylate , 30-50 parts of titanium dioxide, 10-20 parts of pigment, 30-50 parts of curing agent. The epoxy resin antirust paint of the present invention adopts E-51 epoxy resin, cooperates with other components, can solidify well at room temperature, and curing speed is faster, and according to the characteristic of functional coating, climate characteristic, anticorrosion coating construction The characteristics of the performance requirements meet the requirements of the validity period of the anti-corrosion protection.

Description

technical field [0001] The invention relates to an antirust paint and a preparation method thereof. More specifically, the invention relates to an epoxy resin antirust paint and a preparation method thereof, belonging to the technical field of polymer materials. Background technique [0002] In the natural environment, metals such as steel are in an unstable state and are susceptible to corrosion. How to protect metals such as iron and steel so that they can function, prevent corrosion, and prolong service life is an important content of anti-corrosion research. Research and development, functional heavy-duty anti-corrosion coatings are more and more popular. [0003] The State Intellectual Property Office published an invention patent with the publication number CN103360909A on 2013.10.23 and titled "A Waterborne Epoxy Antirust Paint and Its Preparation Method". The patent relates to a waterborne epoxy antirust paint and its The preparation method, the antirust paint is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D147/00C09D133/02C09D5/08C09D7/12
Inventor 曹先军王凤德梁克俭赵奕李智高川孙潜余海燕阎昉邡
Owner BLUESTAR CHENGDU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com