Transparent scratch-resistant PC/PMMA (Poly Carbonate/Polymethyl Methacrylate) alloy material and preparation method thereof
An alloy material and scratch-resistant technology, which is applied in the field of transparent scratch-resistant PC/PMMA alloy material and its preparation, can solve the problems such as the scratch resistance of alloy materials that are not mentioned, and achieve the effect of high transparency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1 Preparation of the transparent scratch-resistant PC / PMMA alloy material of the present invention (1)
[0028] (A) Weigh each component in parts by weight: 40 parts L1250Y, 60 parts PMMA205, 0.1 part antioxidant 1010, 0.1 part antioxidant 168, 1 part pentaerythritol ester.
[0029] (B) Add L1250Y, antioxidant 1010, antioxidant 168 and pentaerythritol ester into a mixing mixer for mixing, and feed the resulting mixture through the main feed port of the twin-screw extruder.
[0030] (C) After the PMMA205 is melted, high-pressure inert gas is introduced, and the high-pressure injection pump is used to inject from the side feeding port of the extruder, blending and granulating, the extrusion temperature is 250~300℃, and the screw extruder speed is 600~900rpm , After melt extrusion, granulation to obtain transparent scratch-resistant PC / PMMA alloy material. Wherein, the inert gas is carbon dioxide; the temperature of the inert gas exceeds 31°C, and the pressure is between...
Example Embodiment
[0031] Example 2 Preparation of the transparent scratch-resistant PC / PMMA alloy material of the present invention (2)
[0032] (A) Weigh each component by weight: 95 parts of L1250Y, 5 parts of PMMA205, 0.5 parts of antioxidant 1010, 0.5 parts of antioxidant 168, and 0.1 parts of ethylene bis-stearamide.
[0033] (B) Add L1250Y, antioxidant 1010, antioxidant 168 and ethylene bis-stearamide into the mixing mixer for mixing, and feed the resulting mixture through the main feed port of the twin-screw extruder.
[0034] (C) After the PMMA205 is melted, high-pressure inert gas is introduced, and the high-pressure injection pump is used to inject from the side feeding port of the extruder, blending and granulating, the extrusion temperature is 250~300℃, and the screw extruder speed is 600~900rpm , After melt extrusion, granulation to obtain transparent scratch-resistant PC / PMMA alloy material. Wherein, the inert gas is nitrogen; the temperature of the inert gas exceeds 31°C, is between 3...
Example Embodiment
[0035] Example 3 Preparation of the transparent scratch-resistant PC / PMMA alloy material of the present invention (3)
[0036] (A) Weigh each component by weight: 80 parts of PC-1220, 20 parts of PMMA205, 0.1 part of antioxidant 245, 0.1 part of antioxidant 168, and 0.3 part of ethylene bis-stearamide.
[0037] (B) Add L1250Y, antioxidant 245, antioxidant 168 and ethylene bisstearamide into a mixing mixer for mixing, and feed the resulting mixture through the main feed port of the twin-screw extruder.
[0038] (C) After the PMMA205 is melted, high-pressure inert gas is introduced, and the high-pressure injection pump is used to inject from the side feeding port of the extruder, blending and granulating, the extrusion temperature is 250~300℃, and the screw extruder speed is 600~900rpm , After melt extrusion, granulation to obtain transparent scratch-resistant PC / PMMA alloy material. Wherein, the inert gas is carbon dioxide and argon; the temperature of the inert gas exceeds 31°C, is...
PUM
Property | Measurement | Unit |
---|---|---|
Screw diameter | aaaaa | aaaaa |
Melt index | aaaaa | aaaaa |
Melt finger | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap