Carboxymethyl-chitosan-starch-polyving-alcohol blending thin film

A carboxymethyl chitosan and polyvinyl alcohol technology, applied in the field of carboxymethyl chitosan-starch-polyvinyl alcohol blend film, can solve the problems of poor film mechanical properties, high brittleness, and unsuitability for acidic environments , to achieve the effects of low production cost, improved quality, and good biodegradability

Active Publication Date: 2014-10-15
ANHUI CHAOHU SOUTH MEMBRANE IND
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in actual production and application, it is found that the films prepared only from chitos...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carboxymethyl-chitosan-starch-polyving-alcohol blending thin film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 50 parts of carboxymethyl chitosan, 15 parts of starch, 15 parts of polyvinyl alcohol, 5 parts of artemisia gum, 2 parts of hydroxypropyl cellulose, 3 parts of nano silicon dioxide, 5 parts of zinc stearate, oxidized polyethylene 4 parts of wax, 2 parts of ethyl silicone oil, 4 parts of glutaraldehyde, 150 parts of distilled water.

Embodiment 2

[0020] 52 parts of carboxymethyl chitosan, 19 parts of starch, 19 parts of polyvinyl alcohol, 6 parts of artemisia gum, 4 parts of hydroxypropyl cellulose, 4 parts of nano silicon dioxide, 6 parts of zinc stearate, oxidized polyethylene 5 parts of wax, 3 parts of ethyl silicone oil, 6 parts of glutaraldehyde, 160 parts of distilled water.

Embodiment 3

[0022] 55 parts of carboxymethyl chitosan, 23 parts of starch, 23 parts of polyvinyl alcohol, 7 parts of artemisia gum, 5 parts of hydroxypropyl cellulose, 4 parts of nano silicon dioxide, 8 parts of zinc stearate, oxidized polyethylene 6 parts of wax, 5 parts of ethyl silicone oil, 7 parts of glutaraldehyde, 170 parts of distilled water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a carboxymethyl-chitosan-starch-polyving-akohol blending thin film, and relates to the technical field of thin film production. The blending thin film is prepared by the following raw materials in parts by mass: 50 to 60 parts of carboxymethyl chitosan, 15 to 30 parts of starch, 15 to 30 parts of polyving alcohol, 5 to 10 parts of artemisia arenaria seed gum, 2 to 8 parts of hydroxy propyl cellulose, 3 to 6 parts of nano-silica, 5 to 10 parts of zinc stearate, 4 to 8 parts of oxidized polyethlene wax, 2 to 7 parts of ethyl silicon oil, 4 to 10 parts of glutaraldehyde and 150 to 200 parts of distilled water. The blending thin film is mainly made of the carboxymethyl chitosan, the starch and the zinc stearate with auxiliary agents, such as a plasticizing agent, a fluxing agent, a cross-linking agent and a degrading agent; not only can the excellent biodegradability of the chitosan and the starch be maintained, but also the quality of the plastic thin film can be effectively improved; moreover, the preparation method is simple and the production cost is low. Therefore, the preparation method is beneficial for industrial production.

Description

Technical field: [0001] The invention relates to the technical field of film production, in particular to a carboxymethyl chitosan-starch-polyvinyl alcohol blend film. Background technique: [0002] Chitosan is obtained by deacetylation of chitin, which exists widely in nature, and its source is second only to cellulose. It is known as "the second type of natural polymer". Chitosan has good film-forming properties, good biocompatibility with organisms, and can be biodegraded. It is widely used in food preservation, environmental treatment and medical fields. Due to the good film-forming properties, antibacterial properties and water vapor permeability of chitosan, as well as the suitable gas barrier properties after film formation, the application in the field of fresh-keeping is particularly prominent. [0003] However, in actual production and application, it is found that the films prepared only from chitosan have problems such as poor mechanical properties, high brittle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L5/08C08L3/02C08L29/04C08L1/26C08L83/04C08K3/36C08K5/098C08K5/07C08J5/18
Inventor 武道贵
Owner ANHUI CHAOHU SOUTH MEMBRANE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap