Derivatives of trimesic acid and method for producing the same

A technology of trimenetricarboxylic acid and trimenetricarboxylate, which is applied in coating, organic chemistry, powder coating, etc., can solve the problems of limited application range, inability to completely replace TGIC, inferiority, etc.

Inactive Publication Date: 2016-05-25
SHANGHAI YAO HE BIOCHEM TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because it is not as good as TGIC in some applications, its use is limited. Except for Europe, which is known for its environmental protection, it cannot completely replace TGIC in other regions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Derivatives of trimesic acid and method for producing the same
  • Derivatives of trimesic acid and method for producing the same
  • Derivatives of trimesic acid and method for producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A preferred embodiment of the present invention is to first prepare trimethylenetricarboxylate (trimethyl1,3,5-benzenetricarboxylate), and then use trimellitic acid methyl ester to manufacture 1,3,5-tri(2-oxazoline base) ) Benzene (1,3,5-tris(2-oxazolidinyl-2-y1)benzene, hereinafter referred to as TOX-1). The detailed implementation steps and reaction formula are as follows:

[0018] Preparation of trimethyl trimesate

[0019] Take a four-neck bottle, install a mechanical stirrer, a condenser tube and a thermometer, weigh trimesic acid (1.0 equiv), add solvent methanol (7.0 equiv), and heat up to 35-40°C. Add thionyl chloride (3.4 equiv) slowly, control the temperature to 40°C, and stir for 3 hours. Sampling is detected, and the reaction is completed if the content of the starting material is less than 1%. Then the temperature was lowered to 20°C, and a white solid was obtained by suction filtration. Wash the white solid with solvent methanol, and dry it to obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fatigue bending timesaaaaaaaaaa
Login to View More

Abstract

The invention provides a 1,3,5-benzenetricarboxylic acid derivative and a making method thereof. The 1,3,5-benzenetricarboxylic acid derivative can be used as a curing agent for a polyester powder coating, and has a structural formula as shown in the specification, wherein n is 0, 1 or 2, R1 is H, CH3 or C2H5, and R2 is H, CH3 or C2H5. The making method of the 1,3,5-benzenetricarboxylic acid derivative comprises the following steps: (1) 1,3,5-benzenetricarboxylic acid ester is mixed with ethanolamine with the structural formula as shown in the following structural formula for reaction in a first solvent, R1 and R2 are as defined, the equivalence ratio of ethanolamine to 1,3,5-benzenetricarboxylic acid ester is about 2-5, the reaction temperature is 120 to 200 DEG C, and a white solid product B is obtained; (2) the white solid product B is mixed with thionyl chloride for reaction in a second solvent, the equivalence ratio of thionyl chloride to white solid product B is about 2-4, the reaction temperature is 10 to 50 DEG C, and a product C is obtained; and (3) the product C is mixed with sodium hydroxide for reaction in a third solvent, the equivalent ratio of sodium hydroxide to product C is about 2.5-3.5, the reaction temperature is 30-50 DEG C, and the 1,3,5-benzenetricarboxylic acid derivative is obtained.

Description

technical field [0001] The invention relates to a derivative of trimenetricarboxylic acid and a manufacturing method thereof, in particular to a derivative of trimenetricarboxylic acid used as a curing agent for polyester powder coatings and a manufacturing method thereof. Background technique [0002] Powder coatings are environmentally friendly coatings that have developed rapidly in recent years. Among them, the curing agent for polyester powder coatings is triglycidyl isocyanurate (1,3,5-Triglycidylisocyanurate, referred to as TGIC) and hydroxyalkylamide (N, N, N', N'-Tetrakis (2- Hydroxyethyl) adipamide (HAA for short) is the most used. [0003] TGIC was developed earlier and has strong functions, but it is irritating to the skin and eyes. In 1991, it was found that it may have carcinogenic and even mutagenic properties. It has long been banned in Europe, but its use still accounts for a large share in other regions. [0004] Due to the toxicity and environmental poll...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D263/12C09D7/12C09D167/00C09D5/03
CPCC07D263/12C09D7/63
Inventor 洪顺明
Owner SHANGHAI YAO HE BIOCHEM TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com