High-performance tin-phosphor bronze wire and production method thereof

A high-performance tin-phosphorus and production method technology, which is applied to the high-performance tin-phosphorus bronze wire and its production field, can solve the problems such as the inability to meet the use requirements of high-end electronic connectors, and achieve the effect of bright surface, uniform material performance and smooth surface

Active Publication Date: 2014-11-19
安徽鑫科铜业有限公司
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The performance and surface of the tin phosphor bronze wire produced by the existing ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance tin-phosphor bronze wire and production method thereof
  • High-performance tin-phosphor bronze wire and production method thereof
  • High-performance tin-phosphor bronze wire and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A high-performance tin-phosphorus bronze wire containing the following substances by weight:

[0034] Sn 4.3%, P 0.07%, Zn 0.03%, Fe 0.005%, Si 0.02%, Ni 0.04%, Cd 0.005%, total impurities 0.02%, and the balance is Cu.

[0035] A production method of high-performance tin-phosphorus bronze wire includes the following steps:

[0036] (1), casting

[0037] According to the above formula, add electrolytic copper and phosphor-copper intermediate alloy to the melting and casting furnace, cover the charcoal, add the tin block after heating up and melt, stir and remove the slag after melting, sample and analyze, after the composition meets the requirements, cover the retort charcoal, and pass the melting temperature 、Control of traction parameters and cooling water volume, and draw Φ12mm qualified rod blanks;

[0038] The casting temperature is controlled at 1200℃, and the drawing parameters are: drawing speed 0.92m / min, drawing length 13mm, drawing time 0.3s, drawing stop time 0.3s, re...

Embodiment 2

[0049] A high-performance tin-phosphorus bronze wire containing the following substances by weight:

[0050] Sn 4.5%, P 0.08%, Zn 0.02%, Fe 0.0045%, Si 0.02%, Ni 0.05%, Cd 0.005%, sum of impurities 0.01%, and the balance is Cu.

[0051] A production method of high-performance tin-phosphorus bronze wire includes the following steps:

[0052] (1), casting

[0053] According to the above formula, add electrolytic copper and phosphor-copper intermediate alloy to the melting and casting furnace, cover the charcoal, add the tin block after heating up and melt, stir and remove the slag after melting, sample and analyze, after the composition meets the requirements, cover the retort charcoal, and pass the melting temperature , Traction parameters, cooling water volume control, to pull out Φ12mm qualified rod billet; the melting temperature is controlled at 1210℃, the drawing parameters are: drawing speed 0.9m / min, drawing length 12mm, drawing time 0.2s, drawing stop Time 0.3s, reverse thrust...

Embodiment 3

[0064] A high-performance tin-phosphorus bronze wire containing the following substances by weight:

[0065] Sn 4.7%, P 0.09%, Zn 0.025%, Fe 0.004%, Si 0.03%, Ni 0.03%, Cd 0.005%, total impurities 0.02%, and the balance is Cu.

[0066] A production method of high-performance tin-phosphorus bronze wire includes the following steps:

[0067] (1), casting

[0068] According to the above formula, add electrolytic copper and phosphor-copper intermediate alloy to the melting and casting furnace, cover the charcoal, add the tin block after heating up and melt, stir and remove the slag after melting, sample and analyze, after the composition meets the requirements, cover the retort charcoal, and pass the melting temperature 、Control of traction parameters and cooling water volume, and draw Φ12mm qualified rod blanks;

[0069] The casting temperature is controlled at 1220℃, and the drawing parameters are: drawing speed 1m / min, drawing length 14mm, drawing time 0.4s, drawing stop time 0.2s, reve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Grain sizeaaaaaaaaaa
Grain sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-performance tin-phosphor bronze wire and a production method thereof. The high-performance tin-phosphor bronze wire comprises the following elements in percentage by weight: 4.3-5.0 percent of Sn, 0.06-0.12 percent of P, 0-0.03 percent of Zn, 0-0.005 percent of Fe, less than 0.0.3 percent of Si, 0-0.05 percent of Ni, 0-0.005 percent of Cd, 0-0.02 percent of total impurities, and Cu in balancing amount. The materials are smelted and drawn to cast a rod blank with the diameter of 12 mm, and then the rod blank is subjected to five-pass processing. The required optimal grain size is achieved by controlling the contents of minor elements like Fe in the tin-phosphor bronze wire and adjusting the annealing temperature, heat preservation time and processing rate in the processing process, therefore, that the material performance is uniform is ensured, and the produced tin-phosphor bronze wire has uniform performance and a smooth surface, and can meet the use requirements of customers in the high-end electronic connector assembly industry.

Description

Technical field [0001] The invention relates to a high-performance tin-phosphorus bronze wire and a production method thereof. Background technique [0002] Tin phosphor bronze has high strength, hardness, wear resistance and corrosion resistance, and is used for electronic equipment components, high-performance plug-ins, terminal blocks, etc. [0003] C51000 tin-phosphorus bronze wire products are mainly used in the high-end electronic connector industry. Due to the high performance uniformity and surface requirements of customers, it is mainly imported from abroad. Only a few domestic manufacturers have mastered the production technology of this product, but the quality of the products produced rarely can fully reach the level of imported products. [0004] The performance and surface of the tin-phosphorus bronze wire produced by the prior art cannot meet the requirements of customers in the high-end electronic connector industry. Summary of the invention [0005] In order to solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C9/02C22C1/03C22F1/08B21C37/04
Inventor 罗继华罗鑫宇王禹发杨贤保梁国庆蒋平
Owner 安徽鑫科铜业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap