A kind of ceramic ink with separation glaze effect and its preparation and use method and ceramic tile

A technology for ceramic ink and glaze separation, applied in ink, application, household appliances and other directions, to achieve the effect of improving clarity and layering, production safety, and improving stability

Active Publication Date: 2017-01-11
FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of concave-convex decorative effect of ceramic tile products in the prior art. A kind of ceramic ink with separation glaze effect and its preparation and use method and ceramic tile are proposed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic ink with separation glaze effect and its preparation and use method and ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] refer to figure 1 , a method for preparing and using ceramic ink with separation glaze effect, comprising the following steps:

[0038] a. Mix the raw materials according to the following proportions: 25 parts of polyurethane acrylate, 30 parts of propylene carbonate, 20 parts of hydroquinone, 20 parts of industrial solvent oil, organically modified polysiloxane acrylic type leveling agent 3 parts, 1 part of high molecular weight polyurethane type dispersant, 1 part of polyamide wax;

[0039] b. Stir the above-mentioned raw material mixture at a high speed to obtain a preliminary mixed material;

[0040] c. Preliminarily grind and disperse the preliminary mixed material with a ball mill, and then transfer to a sand mill for further grinding, with a fineness of less than 1 micron, to obtain ceramic ink;

[0041] d. Spray printing the ceramic ink prepared in step c onto the surface of the ceramic biscuit, and then glaze it; the thickness of the glazed surface is about 0...

Embodiment 2

[0059] A method for preparing and using ceramic ink with separation glaze effect, comprising the following steps:

[0060] a. Mix the raw materials according to the following proportions: 26 parts of polyurethane acrylate, 50 parts of propyl propenyl carbonate, 10 parts of p-methoxyphenol, 11 parts of industrial solvent oil, organically modified polysiloxane acrylic type leveling 1 part of dispersant, 1 part of high molecular weight polyacrylate type dispersant, 1 part of oxidized polyethylene;

[0061] b. Stir the above-mentioned raw material mixture at a high speed to obtain a preliminary mixed material;

[0062] c. Preliminarily grind and disperse the preliminary mixed materials with a ball mill, and then transfer to a sand mill for further grinding to obtain a ceramic ink with a fineness of less than 1 micron.

[0063] d. Spray printing the ceramic ink prepared in step c onto the surface of the ceramic biscuit, and then glaze it; the thickness of the glazed surface is abo...

Embodiment 3

[0070] A method for preparing and using ceramic ink with separation glaze effect, comprising the following steps:

[0071] a. Mix the raw materials according to the following ratio: 27 parts of polyurethane acrylate, 35 parts of dodecyl vinyl ether, 16 parts of hydroquinone, 18 parts of alkane oil, organically modified polysiloxane acrylic leveling agent 1 part, 2 parts of high molecular weight polyacrylate type dispersant, 1 part of polyamide wax;

[0072] b. Stir the above-mentioned raw material mixture at a high speed to obtain a preliminary mixed material;

[0073] c. Preliminarily grind and disperse the preliminary mixed materials with a ball mill, and then transfer to a sand mill for further grinding to obtain a ceramic ink with a fineness of less than 1 micron.

[0074] d. Spray printing the ceramic ink prepared in step c onto the surface of the ceramic biscuit, and then glaze it; the thickness of the glazed surface is about 0.7mm;

[0075] e. Finally, put it into the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
Login to View More

Abstract

The invention provides ceramic ink with an effect of separating glaze, as well as preparation and using methods and a ceramic tile of the ceramic ink. The preparation method of the ceramic ink comprises the following steps: a, mixing the following raw materials in parts by weight: 25-30 parts of urethane acrylate, 30-50 parts of propyl allyl ether carbonate or dodecyl vinyl ether, 10-20 parts of hydroquinone or p-methoxyphenol, 0-20 parts of paraffin oil or industrial solvent oil and 3-5 parts of an auxiliary; b, uniformly stirring the mixture of the raw materials at high speed to obtain a primary mixed material; c, initially grinding and dispersing the primary mixed material by using a ball mill, and transferring into a sand mill for further grinding to obtain the ceramic ink with fineness less than 1 micron. A ceramic tile product prepared by adopting the ceramic ink which is dissoluble with ceramic glaze has an uneven decorating effect without a punch-cum-blanking die, the process is simple, the production is safe, the stability of the ink can be improved, and the clarity and layer sense of patterns can be improved.

Description

technical field [0001] The invention relates to the field of ceramic pigments, in particular to a ceramic ink with separation glaze effect, its preparation and use method and tiles. Background technique [0002] With the development and popularization of digital technology, inkjet printing technology has gradually been applied in the field of ceramic industry. Ceramic inkjet technology is to spray an ink composed of ceramic powder (pigment, colorant), solvent, dispersant and other auxiliary materials from a nozzle with a diameter of tens of microns, and deposit it on the surface at a speed of thousands of drops per second. Decorative technology on body and glaze. Because it is a non-contact decoration, it can be decorated on any concave-convex surface, so the product is more personalized, realistic, delicate, and richer in texture changes. At the same time, because the inkjet printing technology does not need to make a stencil, it saves time and improves efficiency. Theref...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/30C04B41/89
Inventor 周克芳刘咏平
Owner FOSHAN SHI WAN YING BRAND CERAMICS CO LTD