Preparation method of carbon fiber precursor oil agent

A technology of carbon fiber and silk oil agent, which is applied in the fields of carbon fiber, fiber treatment, textiles and papermaking, etc., which can solve the problem of few manufacturers of carbon fiber raw silk oil agent, reduce the phenomenon of monofilament adhesion and parallel silk, and have strong permeability , Good process stability

Inactive Publication Date: 2014-12-03
ZHONGFU SHENYING CARBON FIBER
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Carbon fiber raw silk oil should have excellent high temperature resistance, antistatic performance, wetting and lubricating performance, clustering and anti-sticking performance, but carbon fiber raw silk oil with excellent performance is very rare in the domestic market, and even domestic carbon fiber raw silk There are very few manufacturers of silk finishing agents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbon fiber precursor oil agent
  • Preparation method of carbon fiber precursor oil agent
  • Preparation method of carbon fiber precursor oil agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, a kind of preparation method of carbon fiber precursor oil agent, its steps are as follows:

[0030] Use the compound of alkylphenol polyoxyethylene ether type nonionic surfactant and fatty alcohol polyoxyethylene ether type nonionic surfactant as the compound emulsifier, put the compound emulsifier in the container, raise the temperature to 60°C, and stir Cool to room temperature after uniformity to obtain a milky white or light yellow composite emulsifier, take the composite emulsifier and 60 parts of amino-modified polydimethylsiloxane (25 ° C viscosity is 100mm 2 / s, the ammonia value is 0.6, the chemical formula of the modified group (I)) and 40 parts of polyether modified polydimethylsiloxane (viscosity at 25°C is 1500mm 2 / s, modification amount 0.5) The composite modified silicone oil is put into the high shear emulsifier according to the weight ratio of 3:10 and stirred evenly. Oxyethylene ether 1:1 compound additive, then drop deionized wate...

Embodiment 2

[0031] Embodiment 2, a kind of preparation method of carbon fiber precursor oil agent, its steps are as follows:

[0032] Use C13 linear alcohol ether type nonionic surfactant and fatty alcohol polyoxyethylene ether type nonionic surfactant compound as compound emulsifier, put the compound emulsifier in the container, raise the temperature to 60°C, and stir well Cool to room temperature to obtain a milky white or light yellow composite emulsifier, take the composite emulsifier and 60 parts of amino-modified polydimethylsiloxane (the viscosity at 25°C is 100mm 2 / s, the ammonia value is 0.6, the chemical formula of the modified group (I)) and 40 parts of polyether modified polydimethylsiloxane (viscosity at 25°C is 1500mm 2 / s, modification amount 0.5) The composite modified silicone oil is put into the high shear emulsifier according to the weight ratio of 3:10 and stirred evenly, and the isotridecyl ether phosphate methyl ester salt and the fatty alcohol polyoxygen The compo...

Embodiment 3

[0033] Embodiment 3, a kind of preparation method of carbon fiber precursor oil agent, its steps are as follows:

[0034] Use C13 linear alcohol ether type nonionic surfactant and fatty alcohol polyoxyethylene ether type nonionic surfactant compound as compound emulsifier, put the compound emulsifier in the container, raise the temperature to 60°C, and stir well Cool to room temperature to obtain a milky white or light yellow composite emulsifier, take the composite emulsifier and 50 parts of amino-modified polydimethylsiloxane (the viscosity at 25°C is 100mm 2 / s, the ammonia value is 0.6, the chemical formula of the modified group (I)), 30 parts of polyether modified polydimethylsiloxane (viscosity of 1500mm at 25°C 2 / s, modification amount 0.5), 20 parts of epoxy-modified polydimethylsiloxane (viscosity at 25°C is 3000mm2 / s, the epoxy equivalent value is 0.15, the chemical formula of the modified group (I)) the compound modified silicone oil is put into the high shear emu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a carbon fiber precursor oil agent. The method comprises the following steps: putting a composite emulsifier and a characteristic composite modified silicone oil in a weight ratio of (1-4) to (3-10) into a high-shear emulsifying machine; evenly stirring; adding a composite assistant; dropwise adding an appropriate amount of deionized water; stirring for 20-120 minutes; and adjusting the pH value to 3-10, thereby obtaining a light blue, light yellow or white emulsion, namely the carbon fiber precursor oil agent. According to the method, the technology operation is simple and can be directly applied to an industrial production line. When in use, the oil agent prepared by the method has good permeability, high temperature resistance and good process stability, and can well enhance the bunching performance of fibers and well protect the fibers in the whole process of pre-oxidation as well as in the initial stage of low-temperature carbonization, thereby greatly reducing the phenomena of monofilament adhesion and doubling, reducing the surface detects of the fibers, and enhancing the performance of the fibers.

Description

technical field [0001] The invention relates to a preparation method of an oil agent, in particular to a preparation method of a carbon fiber raw silk oil agent. Background technique [0002] Carbon fiber has many advantages such as high strength, high modulus, high temperature resistance, acid and alkali corrosion resistance, etc., and is widely used in aerospace, civil engineering, new energy and other fields. At the same time, carbon fiber composite materials are being widely used in various industries. With the rapid development of economy and technology, the demand for carbon fiber will further increase. [0003] High-quality carbon fiber precursors are the key to preparing high-quality carbon fibers, and the properties of the precursors directly determine the properties of the final carbon fibers. In the raw silk manufacturing process, the oiling process is an extremely important production process. High-quality oiling agents can solve the adhesion of the filaments du...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/643D06M15/647D06M15/65D06M101/40
Inventor 刘芳欧阳新峰陈秋飞崔丽敏
Owner ZHONGFU SHENYING CARBON FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com