Ceramic plate for cooktop and its preparation and use method

A ceramic plate and stove technology, applied in the field of building materials, can solve the problems of being easily affected by temperature changes and water vapor, affecting the home environment, accumulating large oil pollution, etc. Effect

Inactive Publication Date: 2016-01-27
福建格兰美学智能科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of my country's building materials industry, the production and consumption of ceramic tiles have achieved greater development, but most of the ceramic tiles currently on the market are low in strength and fragile, and it is difficult to meet the diverse needs of consumers.
[0003] At the same time, Chinese cooking methods are mainly frying, frying, and frying, and the oily smoke is heavy, which will cause a lot of oil stains to accumulate on the tiles and seams of the stove top, which is difficult to clean; It is called tile adhesive, which has high bonding strength, water resistance, aging resistance and other properties, but its price is high, it is easily affected by temperature changes and water vapor, and it contains more or less formaldehyde, which seriously affects the home environment and people. good health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic plate for cooktop and its preparation and use method
  • Ceramic plate for cooktop and its preparation and use method
  • Ceramic plate for cooktop and its preparation and use method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] A ceramic plate for a cooktop is composed of a green body and a glaze; slots for splicing are provided on both sides of the green body.

[0072] The preparation method of the ceramic plate for the cooktop comprises the following steps:

[0073] 1) Add water to 2kg of kaolin to make a slurry, slowly add 0.5kg of epoxy resin toughening emulsion containing modified bamboo fiber, stir thoroughly for 0.5h, dry, calcinate at 200°C for 0.5h, pulverize, and pass through a 200-mesh sieve to obtain Modified kaolin;

[0074] 2) Mix the modified kaolin in step 1) with 1kg of phosphogypsum, 0.8kg of quartz, 0.5kg of feldspar, and 0.3kg of lime, and ball mill to obtain a ceramic slurry;

[0075] 3) Dry or dry the ceramic slurry in step 2) and press it into a ceramic slab body;

[0076] 4) Dry the ceramic slab body in step 3) in a drying kiln until the water content is 3%, raise the temperature of the green body to 1000°C at 10°C / min, keep it warm for 2 hours, and then cool it down ...

Embodiment 2

[0092] A ceramic plate for a cooktop is composed of a green body and a glaze; slots for splicing are provided on both sides of the green body.

[0093] The preparation method of the ceramic plate for the cooktop comprises the following steps:

[0094] 1) Add water to 3kg of kaolin to make a slurry, slowly add 1kg of epoxy resin toughening emulsion containing modified bamboo fiber, stir thoroughly for 1 hour, dry, calcinate at 250°C for 0.5 hour, crush, pass through a 300-mesh sieve to obtain modified Kaolin;

[0095] 2) Mix the modified kaolin in step 1) with 1.5kg of phosphogypsum, 1.5kg of quartz, 0.8kg of feldspar, and 0.5kg of lime, and ball mill to obtain a ceramic slurry;

[0096] 3) Dry or dry the ceramic slurry in step 2) and press it into a ceramic slab body;

[0097] 4) Dry the ceramic slab body in step 3) in a drying kiln until the water content is 5%, raise the temperature of the green body to 1200 °C at 12 °C / min, keep it for 1 hour, and then cool it down to 700...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic plate for a cooktop and its preparation and use method. The ceramic plate is composed of a green body and a glaze surface; slots for splicing are provided on both sides of the green body; the raw material components of the green body include Kaolin, phosphogypsum, epoxy resin toughened emulsion containing modified bamboo fibres, quartz, feldspar and lime; used to insert inserts into slots in ceramic plates during cooktop laying or overall framing of the cooktop , or apply a layer of tile glue in the slot of the ceramic board and insert the cutting strip into the slot to realize the splicing of the ceramic board. The ceramic plate prepared by the invention has good toughness, waterproof, wear-resistant, and self-cleaning properties; and its use method is simple, which can effectively reduce or even avoid the use of tile glue, and can significantly speed up the construction progress, and is suitable for kitchen stove tops And the overall construction of the stove.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a ceramic plate for a stove top and a preparation method and application thereof. Background technique [0002] Ceramics are plate or block ceramic products produced by clay, quartz sand and other inorganic non-metallic raw materials through batching, ball milling, molding, sintering and other processes. They are used to decorate and protect the walls and floors of buildings. With the rapid development of my country's building materials industry, the production and consumption of ceramic tiles have achieved greater development. However, most of the ceramic panels currently on the market are low in strength and fragile, and it is difficult to meet the diverse needs of consumers. [0003] At the same time, Chinese cooking methods are mainly frying, frying, and frying, and the oily smoke is heavy, which will cause a lot of oil stains to accumulate on the tiles and seams...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B41/86
Inventor 张可池
Owner 福建格兰美学智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com