Modified wood dyeing method

A dyeing method and modified technology, which is applied in wood treatment, wood processing equipment, wood treatment details, etc., can solve problems such as uneven structure, achieve the effect of wide chromatographic range, uniform color, and improved dyeing levelness

Inactive Publication Date: 2014-12-17
CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, there are crystalline regions in the internal structure of the modified wood, which has structural inhomogeneity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1: Staining of acetylated pear wood boards

[0025] 558 Dehong soaked 10.15g of acetylated pear wood board in water for 30min (weight gain was about 7.5%), and hung it in supercritical CO 2Add 0.100g of Disperse Red 73 to the dyeing jar (1000mL) of the fluid dyeing equipment, and seal the dyeing jar. Inject CO at 130°C 2 , to a pressure of 35MPa, and keep it warm at 130°C for 240min. After the staining was completed, the CO was recovered under reduced pressure. 2 and dyes, and lower the temperature to below 40°C. Take out the dyeing vat, and take out the dyed acetylated pear wood board to obtain a evenly colored maroon acetylated pear wood board with grade 4 color fastness to washing.

Embodiment 2

[0029] Embodiment 2: the dyeing of acetylated Chinese fir powder

[0030] After mixing 5.00g acetylated fir powder and 0.050g Disperse Red 152, add to supercritical CO 2 In the dyeing jar (1000mL) of the fluid dyeing equipment, then evenly drop 2.0mL of water onto the acetylated fir powder, and seal the dyeing jar. Inject CO at 130°C 2 Gas to a pressure of 30MPa, and maintain for 90min. After the staining was completed, the CO was recovered under reduced pressure. 2 and dyes, and lower the temperature to below 40°C. Take out the dyeing vat and pour out the dyed wood powder in the vat to obtain evenly colored red acetylated fir powder with a color fastness to washing of grade 4.

[0031] The above-mentioned red acetylated Chinese fir powder was hot-pressed at 120°C and 2.0 MPa for 10 minutes to obtain red acetylated wood boards.

Embodiment 3

[0035] Example 3: Staining of benzylated Chinese fir powder

[0036] After mixing 20.00g benzylated fir powder and 0.400g disperse blue 148, add to supercritical CO 2 In the dyeing jar (1000mL) of the fluid dyeing equipment, 2.0mL of water was evenly added dropwise to the benzylated fir powder. Airtight dyeing tank, through 120 ℃ CO 2 Gas to a pressure of 25MPa, and keep for 45min. After the staining was completed, the CO was recovered under reduced pressure. 2 Gas and dye, and cool down to 40°C. Take out the dyeing vat, and pour out the dyed wood powder in the vat to obtain dark blue benzylated fir powder with uniform color, and its color fastness to washing is grade 4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a modified wood dyeing method. A modified wood board or modified wood powder is put in a dyeing container of supercritical CO2 fluid dyeing equipment for dyeing with CO2-H2O serving as a dyeing medium, disperse dye serving as a dyeing agent, the temperature of 100-140 DEG C, the pressure of 10-40 MPa and the time of 10-600 minutes. After the dyeing is finished, the CO2 and the disperse dye are recovered by reducing the pressure and the temperature so as to obtain the dyed modified wood board or the dyed modified wood powder; and the hot press molding can be further performed for the dyed modified wood powder to obtain the dyed modified wood board. The dyed wood board has such effects as rich colors, bright colors and uniform colors; and the dyeing process has such advantages as cleanness and environmental protection. The color board can be applied to the indoor or outdoor decoration engineering, can particularly serve as a beautiful decoration material in a humid environment, and has wide application prospect.

Description

technical field [0001] The invention relates to the technical field of modified wood and its dyeing, in particular to a dyeing method of modified wood. Background technique [0002] Chemical modification of wood is one of the important means to realize the durability of wood. Certain characteristics of wood after chemical modification are often significantly improved or improved, such as corrosion resistance, insect resistance and service life. The dyeing of wood can improve the physical and chemical properties of the original surface of the wood, so that the wood can obtain a firmer color, improve the visual effect of the wood, and enhance the decorative effect of the appearance color of the wood products. [0003] Wood is mainly composed of cellulose, hemicellulose and lignin, which has a good affinity for water. Therefore, wood is often dyed with hydrophilic direct dyes, acid dyes, basic dyes and reactive reactive dyes, but the dyed wood often has disadvantages such as p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K5/02
Inventor 赵莹汤静芳杨瑶曹福祥王贵武谭晓燕
Owner CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com