Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of benzene-free odor-free scratch-resistant polyurethane matt gloss white topcoat for woodware

A benzene-free, clean-smelling, anti-scratch technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems that plague manufacturers and engineering technicians, fingerprints are not easy to disappear, and are not resistant to scratches, etc., to achieve excellent leveling Sex, improve gloss, accelerate the effect of convection

Active Publication Date: 2014-12-24
靖江市浩鑫电气机械配件有限公司
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Today's huge wood paint market has higher and higher requirements for paint products. Especially wood polyurethane (PU) paint has excellent comprehensive performance and is widely used by consumers. However, the product has many shortcomings, such as whitening, foaming, and peeling. layer, not resistant to scratches, ghosting, fingerprints are not easy to disappear, etc.
These problems bother manufacturers and engineers and technicians, and some problems have not been solved for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] According to the formula weight ratio, add 5 parts of mixed solvent into the dispersion tank, add 20 parts of 60% solid-free benzene-free alkyd resin, stir and dissolve evenly, then add 25 parts of titanium dioxide, 8 parts of heavy calcium powder, and matting powder 4 parts, 2.0 parts of dispersant, disperse at high speed for 30-40 minutes, grind to a fineness of ≤10μ in a horizontal sand mill, filter and pack for later use.

[0026] Add 28 parts of 60% solid-free benzene-free alkyd resin and 5 parts of mixed solvent into the paint bucket, stir and dissolve evenly, add the above-mentioned ground white pulp at medium speed, and add titanate modified organic 0.3 parts of silicon leveling agent, 0.3 parts of hand feeling leveling agent, 0.2 parts of antioxidant, 0.2 parts of defoaming agent, 2 parts of polyamide wax, stirred and passed the test, filtered and packaged to obtain a benzene-free clean-odor anti-scratch Two-component polyurethane wood matt white topcoat nail c...

Embodiment 2

[0028] Add 40 parts of TDI / TMP adduct, 25 parts of HDI trimer, and 35 parts of mixed solvent into the dispersion tank and stir evenly. After passing the test, filter and pack to produce benzene-free, clean-odor, anti-scratch, two-component polyurethane woodware Matt White Topcoat Part B.

[0029] According to the ratio of component A: component B = 1:0.5, the paint can be adjusted to the viscosity of spraying or brushing by adding diluent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a benzene-free odor-free scratch-resistant polyurethane matt gloss white topcoat for woodware. The benzene-free odor-free scratch-resistant polyurethane matt gloss white topcoat is composed of a component A and a component B which are in the weight ratio of 1:0.5, wherein the component A is composed of odor-free alkyd resin, titanium dioxide, matting powder, calcium carbonate powder, a dispersing agent, an anti-yellowing agent, a flatting agent, a hand feeling agent, a defoaming agent, an anti-settling agent and a solvent; and the component B is a benzene-free curing agent with TDI, an HDI tripolymer or an addition product as a main component. The matt gloss white topcoat prepared by using the preparation method does not contain arene, aldehyde ketone or heavy metals, and no residual odor is left on a paint film after 48 hours; the matt gloss white topcoat can not be settled when being stored, is good in flatting performance, capable of forming a thick film at one step without sagging, soft in hand feeling, full and exquisite, slippery, good in scratch resistance and capable of generating a mirror-surface-like full decorative effect and bringing elegance and comfort for people, and conforms to the modern aesthetic view so as to be popular to the market and consumers; and the matt gloss white topcoat is widely applied to the surfaces of woodware, metals, plastics and other products to take protective and decorative effects.

Description

technical field [0001] The invention relates to a preparation method of a two-component polyurethane matt white finish for woodware, in particular to an environment-friendly, benzene-free and odor-free anti-scratch two-component polyurethane matt white finish for woodware. Background technique [0002] With the improvement of people's material and cultural living standards, consumers have higher and higher requirements for the coating effect of furniture, which has led to the rapid growth of domestic wood coatings. The coating effect of the furniture surface will directly affect consumers' choice of furniture, and matt wood coatings occupy a large market share in the furniture coating market. Today's huge wood paint market has higher and higher requirements for paint products. Especially wood polyurethane (PU) paint has excellent comprehensive performance and is widely used by consumers. However, the product has many shortcomings, such as whitening, foaming, and peeling. la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/06C09D175/14C09D7/06C09D7/12C09D7/47
Inventor 许钧强李泽刚康伦国欧永杰姚东生
Owner 靖江市浩鑫电气机械配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com