Copper product surface thermal coloring process method
A process method and technology of copper products, applied in the direction of metal material coating process, etc., can solve the problems of single color, not very strong artistic expression, not bright enough color, etc., to achieve the effect of improving adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0036] 1. Surface pretreatment of copper crafts
[0037] 1.1 Make copper incense burner according to product design requirements
[0038] 1.2 The surface pretreatment of the product, put the copper incense burner into the sandblasting machine and use 250 mesh glass fine sand to carry out sandblasting on the surface, clean and clean, then rinse with clean water.
[0039] 2. The surface color of the copper incense burner
[0040] 2.1 Using the method of thermal oxidation coloring, use a potassium sulfide aqueous solution with a concentration of 8 g / L to make a background color on the surface of the copper product from top to bottom on the entire surface of the copper product to obtain a copper product with a thickness of the background color layer of 10 μm;
[0041] 2.2 Use a plastic scouring pad to gently wipe off the floating dust and surface color layer on the above-mentioned copper products that have been finished with the background color, then rinse them with clean water,...
Embodiment 2
[0049] 1. Surface pretreatment of copper crafts
[0050] 1.1 Make copper handicraft horse ornaments according to product design requirements
[0051] 1.2 Product surface pretreatment, put the copper handicraft horse ornaments into the sandblasting machine with 320 mesh glass fine sand for surface sandblasting, clean and clean, then rinse with clean water.
[0052] 2. The surface of the copper handicraft horse ornament is black
[0053] 2.1 Preparation of colored black slurry: 3.5 grams of iron oxide red powder, 3.5 grams of iron oxide yellow powder, 1 gram of phthalocyanine blue, 0.5 grams of dispersant polyethylene glycol, 1 liter of water, grind and disperse, and filter through a 100-mesh filter to obtain colored black pulp;
[0054] 2.2 Using the method of thermal oxidation coloring, use a potassium sulfide aqueous solution with a concentration of 20 g / L to make a background color on the surface of the copper product from top to bottom on the entire surface of the copper ...
Embodiment 3
[0065] 1. Surface pretreatment of copper crafts
[0066] 1.1 Make copper handicraft cow ornaments according to product design requirements;
[0067] 1.2 Surface pretreatment of the product. Polish and clean the surface of the copper handicraft cow ornament with a plastic scouring pad and a copper brush. After cleaning, rinse it with clean water.
[0068] 2. The surface of the copper handicraft cow ornament is black
[0069] 2.1 Preparation of colored black slurry: 4 grams of iron oxide red powder, 4 grams of iron oxide yellow powder, 1.2 grams of phthalocyanine blue, 0.2 grams of polyethylene glycol as a dispersant, 1 liter of water, grind and disperse, and filter through a 200-mesh filter to obtain colored black pulp;
[0070] 2.2 Copper handicraft cow ornaments are blackened with copper blackening agent as the background color to obtain copper products with a thickness of the background color layer of about 15 μm;
[0071] 2.3 Use a plastic scouring pad to gently wipe off...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com